Synthetic polyester pulp and process for preparing same
Assignee: Teijin Ltd
•
Filing: 1983-08-29
•
Granted: 1985-07-16
•
Expires: 2003-08-29
Abstract
Abstract Synthetic polyester pulps are provided which are comprised of substantially fibrous fibrils made of a linear aromatic polyester, said fibrils (i) having branches at least in part thereof, (ii) being of an oriented crystalline structure, (iii) having cross-sectional shapes that have irregular and unusual contours, and (iv) exhibiting a freeness of from 50 to 700 cc. The fibrils preferably possess an average fiber diameter of smaller than about 10 microns and a fiber diameter variance of not larger than about 0.7. The pulps are prepared by a process, which comprises the steps of: forming a shaped article from a mixture of a linear aromatic polyester and an organic compound which is incompatible with said polyester and soluble in an alkaline solution; treating the shaped article with an alkaline solution so that the polyester ingredient in the shaped article be at least partially hydrolyzed and the organic compound be at least partially dissolved in the alkaline solution; and then, beating the alkaline solution-treated shaped article.
Inventors
- 👤 Makoto Yoshida
- 👤 Tadashi Hirakawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:45
CPC Classifications
B; B01; B01D; B01D39/00; B01D39/14; B01D39/16; B01D39/1607; B01D39/1623; C; C08; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/16; C08G63/18; C08G63/68; C08G63/688; C08G63/6884; C08G63/6886; C08G63/78; D; D01; D01D; D01D5/00; D01D5/42; D01F; D01F6/00; D01F6/88; D01F6/92; D21; D21H; D21H13/00; D21H13/10; D21H13/20; D21H13/24; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2973; Y10T428/2978; Y10T428/298
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
202 words
A process for preparing a synthetic linear polyester pulp, which comprises the steps of: forming a hollow fiber from a mixture consisting essentially of a linear aromatic polyester and 0.1 to 20% by weight, based on the weight of the linear aromatic polyester, of a metal salt of an organic sulfonic acid which is incompatible with said polyester and soluble in an alkaline solution, wherein the difference SP, between the solubility parameter SPc of said metal salt of an organic sulfonic acid and the solubility parameter SPe of said polyester satisfies the formula: ΔSP=|SPc-SPe|≧2; said metal salt of the organic sulfonic acid is represented by the formula: ##STR4## wherein R is an alkyl group which can be branched having from 3 to 30 carbon atoms an aryl or aralkyl group having 7 to 40 carbon atoms, and M is alkali metal or alkaline earth metal; drawing the hollow fiber; treating the drawn hollow fiber with an alkaline solution, to at least partially hydrolyze the polyester and to at least partially dissolve the metal salt of an organic sulfonic acid, until the hollow fiber loses from about 20 to 80% of its weight; and beating the alkaline solution-treated hollow fiber to fibrillate it.
Claim 2
Dependent Claim
202 words
A process for preparing a synthetic linear polyester pulp, which comprises the steps of: forming a hollow fiber from a mixture consisting essentially of a linear aromatic polyester and 0.1 to 20% by weight, based on the weight of the linear aromatic polyester, of a metal salt of an organic sulfonic acid which is incompatible with said polyester and soluble in an alkaline solution, wherein the difference SP, between the solubility parameter SPc of said metal salt of an organic sulfonic acid and the solubility parameter SPe of said polyester satisfies the formula: ΔSP=|SPc-SPe|≧2; said metal salt of the organic sulfonic acid is represented by the formula: ##STR4## wherein R is an alkyl group which can be branched having from 3 to 30 carbon atoms an aryl or aralkyl group having 7 to 40 carbon atoms, and M is alkali metal or alkaline earth metal; drawing the hollow fiber; treating the drawn hollow fiber with an alkaline solution, to at least partially hydrolyze the polyester and to at least partially dissolve the metal salt of an organic sulfonic acid, until the hollow fiber loses from about 20 to 80% of its weight; and beating the alkaline solution-treated hollow fiber to fibrillate it.
Claim 3
Dependent Claim
36 words
A process according to claim 1, wherein said linear aromatic polyester comprises at least 80% by mole of a recurring unit represented by the formula: ##STR5## where n is an integer of from 2 to 6.
Claim 4
Dependent Claim
12 words
A process according to claim 2, wherein the integer "n" is 2.
Claim 5
Dependent Claim
29 words
A process of claim 1, 2 or 3 wherein the linear aromatic polyester has an intrinsic viscosity of from 0.3 to 1.15 as measured in orthochlorophenol at 35° C.
Claim 6
Dependent Claim
14 words
A process according to claim 1, wherein said difference ΔSP satisfies the formula: ΔSP=|SPc-SPe|≧3.0.
Claim 7
Dependent Claim
40 words
A process of claim 1, 2 or 3, wherein the amount of said metal salt of an organic sulfonic acid is in the range of from 1% to 10% by weight based on the weight of the linear aromatic polyester.
Claim 8
Dependent Claim
19 words
A process according to claim 1, wherein the hollow fiber has a hollow percentage of from 5% to 50%.
Claim 9
Dependent Claim
20 words
A process according to claim 1, wherein the hollow fiber has a wall thickness not greater than about 6 microns.
Claim 10
Dependent Claim
20 words
A process according to claim 1, wherein the hollow fiber has a wall thickness not greater than about 4 microns.
Claim 11
Dependent Claim
69 words
A process according to claim 1, 2, or 3, wherein the hollow fiber is, prior to the treatment with the alkali solution, heat-treated at a temperature not lower than the temperature which is 20° C. higher than the softening point of the metal salt of an organic sulfonic acid, but not higher than the temperature which is 10° C. lower than the softening point of the linear aromatic polyester.
Claim 12
Dependent Claim
54 words
A process according to claim 10, wherein the heat-treating temperature is not lower than the temperature which is 30° C. higher than the softening point of the metal salt of an organic sulfonic acid but not higher than the temperature which is 20° C. lower than the softening point of the linear aromatic polyester.
Claim 13
Dependent Claim
33 words
A prociess according to claim 1, 2 or 3 wherein said alkaline solution is an aqueous solution of at least one alkali selected from the group consisting of sodium hydroxide and potassium hydroxide.
Claim 14
Dependent Claim
25 words
A process according to claim 1, 2 or 3, wherein said alkaline solution is an aqueous solution containing an inorganic alkali and an organic base.
Claim 15
Dependent Claim
31 words
A process according to claim 1, 2 or 3, wherein said treatment with the alkaline solution is effected by using an aqueous inorganic alkali solution and an aqueous organic base solution.
Claim 16
Dependent Claim
58 words
A process according to claim 1, 2 or 3, wherein said treatment with the alkali solution is effected by immersing the hollow fiber in an aqueous solution containing 0.5 to 50 moles, per a recurring unit of the linear aromatic polyester, of an inorganic alkali or an organic base, at a bath ratio of from 1:30 to 1:300.
Claim 17
Dependent Claim
40 words
A process according to claim 1, 2 or 3, wherein the alkaline solution-treated hollow fiber is beaten to an extent such that the beaten product has a freeness of 50 to 700 as expressed in the Canadian standard freeness number.
Claim 18
Dependent Claim
14 words
A synthetic polyester pulp prepared by the process of claim 1, 2 or 3.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-15 | 1989-01-14 | 1989-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-15 | 1993-01-14 | 1993-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-15 | 1997-01-14 | 1997-07-16 | $7700.00 | Window Closed / Lapsed |