Process for producing fine-crystalline α-quartz
Assignee: MOSKOVSKY GOSUDARSTVENNY UNIVERSITET IMENI MV LOMONOSOVA USSR MOSCOW
•
Filing: 1983-06-10
•
Granted: 1985-07-16
•
Expires: 2003-06-10
Abstract
Abstract The present invention relates to a process for producing a fine-crystalline α-quartz with a crystal size of from 0.08 to 0.8 mm. The process comprises crystallization of amorphous silica in the atmosphere of water vapors in the presence of a crystallization promotor--a surface-active nitrogen-containing substance possessing basic properties in an amount of from 1×10 -3 to 1% by weight of amorphous silica at a temperature within the range of from 300° to 500° C. under a pressure of from 20 to 400 atm for 6 to 100 hours. The process of the present invention is simple as regards its technology and equipment. The resulting product is noted for a low content of impurities and is fit for the manufacture of high-quality quartz glass and quartz ceramics.
Inventors
- 👤 Vladislav B. Lazarev
- 👤 Georgy P. Panasjuk
- 👤 Marina N. Danchevskaya
- 👤 Vladimir M. Gavrilko
- 👤 Valery A. Kreisberg
- 👤 Galina P. Budova
- 👤 Sergei N. Torbin
- 👤 Igor L. Voroshilov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 08:13
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/14; C01; C01B; C01B33/00; C01B33/113; C01B33/12; C03; C03C; C03C1/00; C30; C30B; C30B29/00; C30B29/10; C30B29/16; C30B29/18; C30B7/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
82 words
A process for producing fine-crystalline α-quartz with a crystal size of from 0.08 to 0.8 mm, residing in that amorphous silica is crystallized in the atmosphere of water vapours in the presence of a crystallization promotor, viz. a surface-active nitrogen-containing substance with basic properties in an amount of from 1×10 -3 to 1% by weight of amorphous silica at a temperature within the range of 300° to 500° C. under a pressure of 20 to 400 atm for 6 to 100 hours.
Claim 2
Dependent Claim
82 words
A process for producing fine-crystalline α-quartz with a crystal size of from 0.08 to 0.8 mm, residing in that amorphous silica is crystallized in the atmosphere of water vapours in the presence of a crystallization promotor, viz. a surface-active nitrogen-containing substance with basic properties in an amount of from 1×10 -3 to 1% by weight of amorphous silica at a temperature within the range of 300° to 500° C. under a pressure of 20 to 400 atm for 6 to 100 hours.
Claim 3
Dependent Claim
43 words
A process according to claim 1, wherein as the crystallization promotor use is made of ammonium bases selected from the group consisting of ammonium hydroxide or quaternary ammonium bases in an amount of from 2×10 -2 to 1% by weight of amorphous silica.
Claim 4
Dependent Claim
41 words
A process according to claim 1, wherein as the crystallization promotor use is made of polyelectrolytes-polyethylenimines with a molecular weight of from 190 to 50,000 in an amount of from 1×10 -3 to 1×10 -1 % by weight of amorphous silica.
Claim 5
Dependent Claim
33 words
A process according to claim 1, wherein as the crystallization promotor use is made of hydrazine or alkylderivatives thereof in an amount of from 2×10 -2 to 1% by weight of amorphous silica.
Claim 6
Dependent Claim
93 words
A process for producing fine-crystalline α-quartz with a crystal size of from 0.08 to 0.8 mm, residing in that amorphous silica is crystallized in the atmosphere of water vapours in the presence of a crystallization promotor, at a temperature within the range of 300° to 500° C. under a pressure of 20 to 400 atm for 6 to 100 hours, and wherein said crystallization promotor comprises polyelectrolytes-polyethylenimines with a molecular weight of from 190 to 50,000 in an amount of from 1×10 -3 to to 1×10 -1 % by weight of amorphous silica.
Claim 7
Dependent Claim
93 words
A process for producing fine-crystalline α-quartz with a crystal size of from 0.08 to 0.8 mm, residing in that amorphous silica is crystallized in the atmosphere of water vapours in the presence of a crystallization promotor, at a temperature within the range of 300° to 500° C. under a pressure of 20 to 400 atm for 6 to 100 hours, and wherein said crystallization promotor comprises polyelectrolytes-polyethylenimines with a molecular weight of from 190 to 50,000 in an amount of from 1×10 -3 to to 1×10 -1 % by weight of amorphous silica.
Claim 8
Dependent Claim
82 words
A process for producing fine-crystalline α-quartz with a crystal size of from 0.08 mm, residing in that amorphous silica is crystallized in the atmosphere of water vapours in the presence of a crystallization promotor, at a temperature within the range of 300° to 500° C. under a pressure of 20 to 400 atm for 6 to 100 hours, and wherein said crystallization promotor comprises hydrazine or alkylderivatives thereof in an amount of from 2×10 -2 to 1% by weight of amorphous silica.
Claim 9
Dependent Claim
82 words
A process for producing fine-crystalline α-quartz with a crystal size of from 0.08 mm, residing in that amorphous silica is crystallized in the atmosphere of water vapours in the presence of a crystallization promotor, at a temperature within the range of 300° to 500° C. under a pressure of 20 to 400 atm for 6 to 100 hours, and wherein said crystallization promotor comprises hydrazine or alkylderivatives thereof in an amount of from 2×10 -2 to 1% by weight of amorphous silica.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-15 | 1989-01-14 | 1989-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-15 | 1993-01-14 | 1993-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-15 | 1997-01-14 | 1997-07-16 | $7700.00 | Window Closed / Lapsed |