Process for producing hydrophilic polymers
Assignee: Ube Corp
•
Filing: 1984-08-29
•
Granted: 1985-07-09
•
Expires: 2004-08-29
Abstract
Abstract A hydrophilic modified diene polymer material is produced by the steps of epoxidizing a diene polymer material consisting of at least one member selected from rubber polymers which have a molecular weight of 10,000 or more and contain an 85 molar % of more 1,4-addition structure based on the entire molar amount of double bonds contained therein, and crystalline 1,2-polybutadiene polymers which have a melting point of from 60 DEG C. to 170 DEG C., and a reduced viscosity (nsp/c) of 0.2 or more determined in a tetrahydronaphthalene solution in a concentration of 200 mg/100 ml at a temperature of 100 DEG C., and contain a 75 molar % or more 1,2-addition structure based on the entire molar amount of double bonds contained therein, for example, with a combination of a carboxylic acid and a peroxide compound, or a carboxylic peracid, to an extent such that the degree of epoxidization of the rubber polymers is in the range of from 5% to 60% and the degree of epoxidization of the crystalline 1,2-polybutadiene is in the range of from 5% to 45%; and ring-opening at least a portion of the epoxy rings in the resultant epoxidized polymeric material by heating it in the presence of a tertiary amine and a carboxylic acid.
Inventors
- 👤 Osamu Hayashi
- 👤 Hideo Kurihara
- 👤 Yukio Matsumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:18
CPC Classifications
C; C08; C08C; C08C19/00; C08C19/04; C08C19/06; C08G; C08G59/00; C08G59/14; C08G59/1433; C08G59/1438; C08G59/1455
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
200 words
A process for producing a hydrophilic polymer, comprising the step of: epoxidizing a diene polymer material consisting of at least one member selected from the group consisting of rubber polymers which have a molecular weight of 10,000 or more and contain a 1,4-addition structure in a molar content of 85% or more based on the entire molar amount of double bonds contained therein, and crystalline 1,2-polybutadiene polymers which have a melting point of from 60° C. to 170° C., and a reduced Viscosity (ηsp/c) of 0.2 or more determined in a tetrahydronaphthalene solution in a concentration of 200 mg/100 ml at a temperature of 100° C., and contain a 1,2-addition structure in a molar content of 75% or more based on the entire molar amount of double bonds contained therein, to an extent such that the degree of epoxidization of said rubber polymers is in the range of from 5% to 60% and the degree of epoxidization of said crystalline 1,2-polybutadiene is in the range of from 5% to 45%; and ring-opening at least a portion of the epoxy rings in the resultant epoxidized polymeric material by heating it in the presence of a tertiary amine and a carboxylic acid.
Claim 2
Dependent Claim
200 words
A process for producing a hydrophilic polymer, comprising the step of: epoxidizing a diene polymer material consisting of at least one member selected from the group consisting of rubber polymers which have a molecular weight of 10,000 or more and contain a 1,4-addition structure in a molar content of 85% or more based on the entire molar amount of double bonds contained therein, and crystalline 1,2-polybutadiene polymers which have a melting point of from 60° C. to 170° C., and a reduced Viscosity (ηsp/c) of 0.2 or more determined in a tetrahydronaphthalene solution in a concentration of 200 mg/100 ml at a temperature of 100° C., and contain a 1,2-addition structure in a molar content of 75% or more based on the entire molar amount of double bonds contained therein, to an extent such that the degree of epoxidization of said rubber polymers is in the range of from 5% to 60% and the degree of epoxidization of said crystalline 1,2-polybutadiene is in the range of from 5% to 45%; and ring-opening at least a portion of the epoxy rings in the resultant epoxidized polymeric material by heating it in the presence of a tertiary amine and a carboxylic acid.
Claim 3
Dependent Claim
24 words
The process as claimed in claim 1, wherein said rubber polymers are selected from the group consisting of natural rubber and synthetic rubber polymers.
Claim 4
Dependent Claim
28 words
The process as claimed in claim 2, wherein said synthetic rubber polymers are selected from the group consisting of 1,4-polybutadiene polymers, polyisoprene polymers, styrene-butadiene copolymers and acrylonitrile-butadiene copolymers.
Claim 5
Dependent Claim
40 words
The process as claimed in claim 1, wherein said diene polymer material is epoxidized with an epoxidizing agent consisting of at least one member selected from the group consisting of combinations of carboxylic acids with peroxide compounds and carboxylic peracids.
Claim 6
Dependent Claim
27 words
The process as claimed in claim 4, wherein in said epoxidizing step, said carboxylic acid is selected from saturated carboxylic acids having 1 to 10 carbon atoms.
Claim 7
Dependent Claim
14 words
The process as claimed in claim 4, wherein said peroxide compound is hydrogen peroxide.
Claim 8
Dependent Claim
19 words
The process as claimed in claim 1, wherein said epoxidizing step is carried out in an inert organic medium.
Claim 9
Dependent Claim
28 words
The process as claimed in claim 7, wherein said organic medium comprises at least one liquid organic compound selected from the group consisting of hydrocarbons and halogenated hydrocarbons.
Claim 10
Dependent Claim
40 words
The process as claimed in claim 4, wherein in said epoxidizing step, said carboxylic acid and peroxide compound are used in amounts of 0.01 to 5 moles and 0.1 to 5 moles, respectively, per 100 g of said polymeric material.
Claim 11
Dependent Claim
24 words
The process as claimed in claim 4, wherein said epoxidizing step is carried out at a temperature of from 5° C. to 90° C.
Claim 12
Dependent Claim
27 words
The process as claimed in claim 4, wherein the resultant reaction mixture of said epoxidizing step is washed with water to remove the residual peroxide compound therefrom.
Claim 13
Dependent Claim
29 words
The process as claimed in claim 4, wherein said carboxylic acid used in the epoxy ring-opening step is selected from saturated carboxylic acids having 1 to 10 carbon atoms.
Claim 14
Dependent Claim
30 words
The process as claimed in claim 1, wherein said tertiary amine used in the epoxy ring-opening step is selected from heterocyclic tertiary amines, aliphatic tertiary amines, and aromatic tertiary amines.
Claim 15
Dependent Claim
20 words
The process as claimed in claim 1, wherein the epoxy ring-opening step is carried out in an inert organic medium.
Claim 16
Dependent Claim
29 words
The process as claimed in claim 13, wherein said inert organic medium comprises at least one liquid organic compound selected from the group consisting of hydrocarbons and halogenated hydrocarbons.
Claim 17
Dependent Claim
25 words
The process as claimed in claim 1, wherein the epoxy ring-opening step is carried out at a temperature of from 40° C. to 160° C.
Claim 18
Dependent Claim
67 words
The process as claimed in claim 1, wherein the epoxy ring-opening step is carried out to an extent such that said epoxy rings in a molar amount corresponding to 5% to 60% of the entire molar amount of the double bonds contained in said rubber polymers and to 5% to 45% of the entire molar amount of the double bonds contained in said 1,2-polybutadiene polymers are ring-opened.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |