Pretreatment of plastic materials for metal plating
Assignee: Honeywell International Inc
•
Filing: 1984-02-27
•
Granted: 1985-07-09
•
Expires: 2004-02-27
Abstract
Abstract This invention relates to a process for conditioning the surfaces of natural and synthetic plastic materials for electroless plating of a metal coating thereon by exposing such materials to an atmosphere comprising ozone, contacting said exposed materials with a conditioning solvent, such as an aqueous solution of sodium, potassium or lithium hydroxide, and thereafter rinsing said contacted materials with an aqueous solution of one or more surfactants.
Inventors
- 👤 Jill M. Jobbins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:14
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; C08; C08J; C08J7/00; C08J7/12; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31696
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
86 words
In an improved process for metal plating a natural or synthetic plastic material by conditioning said material to improve metal adhesion by exposing said material to an atmosphere comprising ozone, contacting said exposed material with a conditioning solvent, and depositing a metal coating upon said conditioned surface from an electroless plating bath, wherein said improvement comprises rinsing said contacted material with an aqueous solution comprising an effective amount of one or more surfactants after contacting said material with said solvent and before depositing said metal coating.
Claim 2
Dependent Claim
86 words
In an improved process for metal plating a natural or synthetic plastic material by conditioning said material to improve metal adhesion by exposing said material to an atmosphere comprising ozone, contacting said exposed material with a conditioning solvent, and depositing a metal coating upon said conditioned surface from an electroless plating bath, wherein said improvement comprises rinsing said contacted material with an aqueous solution comprising an effective amount of one or more surfactants after contacting said material with said solvent and before depositing said metal coating.
Claim 3
Dependent Claim
24 words
A process according to claim 1 wherein said material is selected from the group consisting of polydiphenylene sulfones, polyacetals, polyphenylene sulfides and polyphenylene oxides.
Claim 4
Dependent Claim
13 words
A process according to claim 2 wherein said material is a polydiphenylene sulfone.
Claim 5
Dependent Claim
12 words
A process according to claim 2 wherein said material is polyphenylene sulfide.
Claim 6
Dependent Claim
12 words
A process according to claim 2 wherein said material is polyphenylene oxide.
Claim 7
Dependent Claim
12 words
A process according to claim 2 wherein said material is a polyacetal.
Claim 8
Dependent Claim
25 words
An improved process according to claim 1 wherein said material is selected from the group consisting of polymers containing carbon-carbon unsaturation within the polymer chain.
Claim 9
Dependent Claim
40 words
An improved process according to claim 7 wherein said material is a material selected from the group consisting of block and graft copolymers in which at least one type of the recurring monomeric units of said plastic includes carbon/carbon unsaturation.
Claim 10
Dependent Claim
15 words
An improved process according to claim 8 wherein said carbon/carbon unsaturation is a double bond.
Claim 11
Dependent Claim
13 words
An improved process according to claim 2 wherein said material is acrylonitrile-butadiene-styrene copolymer.
Claim 12
Dependent Claim
30 words
An improved process according to claim 1 wherein the quantity of ozone in said atmosphere is at least about 0.1 weight percent based on the total weight of the atmosphere.
Claim 13
Dependent Claim
24 words
An improved process according to claim 1 wherein said conditioning solvent comprises a aqueous solution of one or more strong organic or inorganic bases.
Claim 14
Dependent Claim
26 words
An improved process according to claim 12 wherein said base is selected from the group consisting of sodium hydroxide, lithium hydroxide, potassium hydroxide and ammonium hydroxide.
Claim 15
Dependent Claim
29 words
An improved process according to claim 1 wherein said one or more surfactants are selected from the group consisting of nonionic surfactants, and mixtures of nonionic and anionic surfactants.
Claim 16
Dependent Claim
22 words
An improved process according to claim 14 wherein said one or more surfactants are selected from the group consisting of nonionic surfactants.
Claim 17
Dependent Claim
29 words
An improved process according to claim 14 wherein said nonionic surfactants are selected from the group consisting of alkylarylpolyethers, fatty acid alkanol amides, polyalkoxylated alcohols, and fatty alcohol polyethers.
Claim 18
Dependent Claim
44 words
An improved process according to claim 16 wherein said nonionic surfactants are selected from the group consisting of the condensation products of alkylphenols and ethylene oxide, the adduct of isotridecyl alcohol and ethylene oxide, polyethoxylated 3-tridecanol, fatty alcohol polyethers and fatty acid alkanol amides.
Claim 19
Dependent Claim
18 words
An improved process according to claim 17 wherein said solution comprises a mixture of more than one surfactant.
Claim 20
Dependent Claim
33 words
An improved process according to claim 1 wherein the concentration of one or more surfactants in said solution is at least about 0.0001 weight percent based on the total weight of the solution.
Claim 21
Dependent Claim
19 words
An improved process according to claim 19 wherein said concentration is from about 0.0001 to about 20 weight percent.
Claim 22
Dependent Claim
19 words
An improved process according to claim 20 wherein said concentration is from about 0.001 to about 10 weight percent.
Claim 23
Dependent Claim
19 words
An improved process according to claim 21 wherein said concentration is from about 0.01 to about 1 weight percent.
Claim 24
Dependent Claim
19 words
An improved process according to claim 22 wherein said concentration is from about 0.025 to about 0.5 weight percent.
Claim 25
Dependent Claim
81 words
An improved process for plating one or more metals onto the surfaces of a plastic material which comprises: (a) exposing said material to an atmosphere containing ozone; (b) contacting said exposed material with a conditioning solvent; (c) rinsing said contacted material with an aqueous solution containing an effective amount of one or more surfactants; and (d) coating said contacted material with a catalyst for electroless plating of metal thereon; (e) depositing a metal coating on said catalyzed material by electroless plating.
Claim 26
Dependent Claim
81 words
An improved process for plating one or more metals onto the surfaces of a plastic material which comprises: (a) exposing said material to an atmosphere containing ozone; (b) contacting said exposed material with a conditioning solvent; (c) rinsing said contacted material with an aqueous solution containing an effective amount of one or more surfactants; and (d) coating said contacted material with a catalyst for electroless plating of metal thereon; (e) depositing a metal coating on said catalyzed material by electroless plating.
Claim 27
Dependent Claim
22 words
An improved process according to claim 24 wherein said metal is selected from the group consisting of copper, silver, nickel and cobalt.
Claim 28
Dependent Claim
30 words
An improved process according to claim 25 which further comprises depositing one or more additional metal coatings onto said metal coated material of step e by electroplating or electroless plating.
Claim 29
Dependent Claim
26 words
An improved process according to claim 26 wherein said one or more additional metals are selected from the group consisting of copper, nickel, silver and chromium.
Claim 30
Dependent Claim
20 words
A natural or synthetic material which has been conditioned and metal plated in accordance with the process of claim 1.
Claim 31
Dependent Claim
26 words
A metal plated natural or synthetic plastic material one or more surfaces of which have been metal plated in accordance with the process of claim 24.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |