US4422907A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Pretreatment of plastic materials for metal plating
Assignee: Honeywell International Inc
•
Filing: 1981-12-30
•
Granted: 1983-12-27
•
Expires: 2001-12-30
Abstract
Abstract This invention relates to a process for conditioning the surfaces of natural and synthetic plastic materials for electroless plating of a metal coating thereon by exposing such materials to an atmosphere comprising an effective amount of ozone and thereafter contacting said exposed materials with an effective amount of a conditioning solvent, such as an aqueous solution of sodium, potassium or lithium hydroxide.
Inventors
- 👤 Albert A. Birkmaier
- 👤 Gary A. Harpell
- 👤 Bruce E. Kurtz
- 👤 Gordhanbhai N. Patel
- 👤 Rustom P. Poncha
- 👤 Adam L. Skovrinski
- 👤 James M. Lesco
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 10:32
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381; Y; Y10; Y10S; Y10S205/00; Y10S205/924; Y10S205/928
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
74 words
In an improved process for metal plating a natural or synthetic plastic material by conditioning said material to improve metal adhesion and depositing a metal coating upon said conditioned surface from an electroless plating bath, wherein said improvement comprises a conditioning step in which said material is exposed to an atmosphere comprising an effective amount of ozone and is then contacted with an effective amount of one or more strong organic or inorganic bases.
Claim 2
Dependent Claim
74 words
In an improved process for metal plating a natural or synthetic plastic material by conditioning said material to improve metal adhesion and depositing a metal coating upon said conditioned surface from an electroless plating bath, wherein said improvement comprises a conditioning step in which said material is exposed to an atmosphere comprising an effective amount of ozone and is then contacted with an effective amount of one or more strong organic or inorganic bases.
Claim 3
Dependent Claim
25 words
An improved process according to claim 1 wherein said material is selected from the group consisting of polymers containing carbon-carbon unsaturation within the polymer chain.
Claim 4
Dependent Claim
40 words
An improved process according to claim 2 wherein said material is a plastic selected from the group consisting of block and graft copolymers in which at least one type of the recurring monomeric units of said plastic includes carbon/carbon unsaturation.
Claim 5
Dependent Claim
25 words
An improved process according to claim 2 wherein said plastic comprises three types of recurring monomeric units, one of which includes a carbon/carbon double bond.
Claim 6
Dependent Claim
13 words
An improved process according to claim 2 wherein said plastic is acrylonitrile-butadiene-styrene copolymer.
Claim 7
Dependent Claim
26 words
A composition according to claim 1 wherein said material comprises a mixture of polymers at least one of which contains carbon-carbon unsaturation in the polymer chain.
Claim 8
Dependent Claim
19 words
An improved process according to claim 2 or 3 or 4 wherein said carbon/carbon unsaturation is a double bond.
Claim 9
Dependent Claim
27 words
An improved process according to claim 7 wherein said material is selected from the group consisting of polybutadiene, butadiene/styrene copolymer, butadiene/acrylonitrile copolymer, polychloroprene, polyisoprene and acrylonitrile-butadiene-styrene copolymer.
Claim 10
Dependent Claim
32 words
An improved process according to claim 1 or 4 wherein the quantity of ozone in said atmosphere is at least about 0.1 weight percent based on the total weight of the atmosphere.
Claim 11
Dependent Claim
17 words
An improved process according to claim 9 wherein said quantity is at least about 0.5 weight percent.
Claim 12
Dependent Claim
17 words
An improved process according to claim 10 wherein said quantity is at least about 0.8 weight percent.
Claim 13
Dependent Claim
17 words
An improved process according to claim 11 wherein said quantity is at least about 1.5 weight percent.
Claim 14
Dependent Claim
20 words
An improved process according to claim 1 wherein said bases are selected from the group consisting of strong inorganic bases.
Claim 15
Dependent Claim
26 words
An improved process according to claim 13 wherein said exposed material is contacted with an aqueous solution containing an effective amount of said strong inorganic base.
Claim 16
Dependent Claim
26 words
An improved process according to claim 14 wherein said base is selected from the group consisting of sodium hydroxide, lithium hydroxide, potassium hydroxide and ammonium hydroxide.
Claim 17
Dependent Claim
30 words
An improved process according to claim 1 wherein the concentration of base in said solution is at least about 0.5 weight percent based on the total weight of the solution.
Claim 18
Dependent Claim
19 words
An improved process according to claim 16 wherein said concentration is from about 0.5 to about 30 weight percent.
Claim 19
Dependent Claim
19 words
An improved process according to claim 17 wherein said concentration is from about 2 to about 30 weight percent.
Claim 20
Dependent Claim
19 words
An improved process according to claim 18 wherein said concentration is from about 5 to about 10 weight percent.
Claim 21
Dependent Claim
76 words
An improved process for plating one or more metals onto the surfaces of a plastic material which comprises: (a) exposing said material to an atmosphere containing an effective amount of ozone; (b) contacting said exposed material with an effective amount of one or more strong organic or inorganic bases; (c) coating said contacted material with a catalyst for electroless plating of metal thereon; and (d) depositing a metal coating on said catalyzed material by electroless plating.
Claim 22
Dependent Claim
76 words
An improved process for plating one or more metals onto the surfaces of a plastic material which comprises: (a) exposing said material to an atmosphere containing an effective amount of ozone; (b) contacting said exposed material with an effective amount of one or more strong organic or inorganic bases; (c) coating said contacted material with a catalyst for electroless plating of metal thereon; and (d) depositing a metal coating on said catalyzed material by electroless plating.
Claim 23
Dependent Claim
21 words
An improved process according to claim 20 wherein said metal is selected from the group consisting of copper, nickel and cobalt.
Claim 24
Dependent Claim
27 words
An improved process according to claim 20 which further comprises depositing one or more additional metal coatings onto said metal coated material of step d, by electroplating.
Claim 25
Dependent Claim
25 words
An improved process according to claim 22 wherein said one or more additional metals are selected from the group consisting of copper, nickel and chromium.
References Cited (Backward Citations)
US2715076A
Cited
US2715075A
Cited
US2805960A
Cited
US3227605A
Cited
US3313642A
Cited
US3437507A
Cited
US3370974A
Cited
US3686018A
Cited
US4039714A
Cited
US4165394A
Cited
US4337279A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-26 | 1987-06-27 | 1987-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-26 | 1991-06-27 | 1991-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-26 | 1995-06-27 | 1995-12-27 | $7700.00 | Window Closed / Lapsed |