US4528243A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for surface treatment of polyorganosiloxane gel-filled containers to prevent bubble migration into said gel
Assignee: Dow Silicones Corp
•
Filing: 1984-10-16
•
Granted: 1985-07-09
•
Expires: 2004-10-16
Abstract
Abstract Bubble migration from a surface of a container or other substrate into a polyorganosiloxane gel that is in contact with the surface can be substantially eliminated by coating the surface with a liquid composition comprising an organohydrogensiloxane containing at least three silicon-bonded hydrogen atoms per molecule. The liquid composition is covered with a layer of uncured silicone rubber that is curable by hydrosilation reaction in addition to being compatible with and adherent to the polyorganosiloxane gel. The gel is then placed over the uncured silicone rubber, after which the rubber and gel are concurrently cured. The cured silicone rubber exhibits a durometer hardness value of at least 10 on the Shore A scale, and the layer of silicone rubber is at least 3 mm. thick.
Inventors
- 👤 Gust J. Kookootsedes
- 👤 Herschel H. Reese
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:07
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31598
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
165 words
A method for treating a substrate to prevent the migration of gas bubbles from the surface of said substrate into a polyorganosiloxane gel that is in contact with said surface, said method consisting essentially of the following sequence of steps: (I) coating at least a portion of said surface with a liquid composition comprising an amount of an organohydrogensiloxane sufficient to react with all hydrogen-reactive materials in contact with said organohydrogensiloxane, where said organohydrogensiloxane contains at least three silicon-bonded hydrogen atoms per molecule; (II) applying over said liquid composition a layer of uncured silicone rubber composition curable by a platinum-catalyzed hydrosilation reaction, where said layer is at least 3 mm thick and where said silicone rubber in the cured form exhibits a durometer of at least 10 on the Shore A scale; (III) placing said polyorganosiloxane gel in uncured form over said layer, said gel being curable by a platinum catalyzed hydrosilation reaction; and (IV) concurrently curing said gel and said uncured silicone rubber composition.
Claim 2
Independent Claim
165 words
A method for treating a substrate to prevent the migration of gas bubbles from the surface of said substrate into a polyorganosiloxane gel that is in contact with said surface, said method consisting essentially of the following sequence of steps: (I) coating at least a portion of said surface with a liquid composition comprising an amount of an organohydrogensiloxane sufficient to react with all hydrogen-reactive materials in contact with said organohydrogensiloxane, where said organohydrogensiloxane contains at least three silicon-bonded hydrogen atoms per molecule; (II) applying over said liquid composition a layer of uncured silicone rubber composition curable by a platinum-catalyzed hydrosilation reaction, where said layer is at least 3 mm thick and where said silicone rubber in the cured form exhibits a durometer of at least 10 on the Shore A scale; (III) placing said polyorganosiloxane gel in uncured form over said layer, said gel being curable by a platinum catalyzed hydrosilation reaction; and (IV) concurrently curing said gel and said uncured silicone rubber composition.
Claim 3
Dependent Claim
83 words
A method according to claim 1 where said polyorganosiloxane gel in an uncured form comprises the product obtained by mixing (A) at least one diorganovinylsiloxy endblocked polydiorganosiloxane exhibiting a viscosity of from 0.1 to 50 Pa.s at 25° C., (B) at least one polyorganohydrogensiloxane containing an average of at least three silicon-bonded hydrogen atoms per molecule in an amount sufficient to cure said polyorganosiloxane gel, and (C) platinum or a platinum compouhd in an amount sufficient to catalyze curing of said polyorganosiloxane gel.
Claim 4
Dependent Claim
69 words
A method according to claim 2 where said polyorganosiloxane gel in the uncured form includes at least one polydiorganosiloxane containing a silicon-bonded hydrogen atom at each of the two terminal positions, the molar ratio of silicon-bonded hydrogen atoms to vinyl groups present in said gel is from 1.8 to 2.9 and said polydiorganosiloxane provides from 80 to 95 mol percent of the silicon-bonded hydrogen atoms present in said gel.
Claim 5
Dependent Claim
25 words
A method according to claim 1 where silicon-bonded hydrocarbon radicals present in said uncured silicone rubber composition and said polyorganosiloxane gel are vinyl and methyl.
Claim 6
Dependent Claim
136 words
A method according to claim 2 where said polyorganosiloxane gel in the uncured form includes up to 25%, based on the weight of (A), of a resinous, benzene soluble copolymer consisting essentially of repeating units of the formulae (a) (CH 3 ) 2 CH 2 ═CHSiO 0 .5, (b) (CH 3 ) 3 SiO 0 .5 and (c) SiO 4/2 where the molar ratio of combined (a) and (b) units to (c) units is from 0.6:1 to 1.1:1, units represented by formula (a) constitute from 2 to 8% by weight of the copolymer, the copolymer contains at least two vinyl groups per molecule and the molar ratio of (a) to (b) to (c) units is 5-10:40-45:45-50, with the proviso that the concentration of (a) units does not exceed 8% of the total weight of said copolymer.
Claim 7
Dependent Claim
58 words
A method according to claim 1 where said silicone rubber composition is extrudable and comprises a diorganovinylsiloxy endblocked polydiorganosiloxane, an organohydrogensiloxane containing at least three silicon-bonded hydrogen atoms per molecule in an amount sufficient to cure said composition and a platinum-containing hydrosilation catalyst in an amount sufficient to promote curing of said composition at temperatures above 50° C.
Claim 8
Dependent Claim
115 words
A method according to claim 6 where said polydiorganosiloxane is a mixture of polydimethylsiloxanes that collectively provides a molecular weight distribution such that there is present at least one polymeric species (1) at a concentration greater than the concentrations of polymeric species of lower and higher molecular weight, said species (1) having a molecular weight, determined by gel permeation chromatography, within the range from 68,000 to 135,000, where the lowest molecular weight species is within the range from 854 to 3146, the highest molecular weight species is within the range from 174,000 to 370,000 and the various polymeric species exhibit a molecular weight distribution such that the mixture exhibits a dispersity index greater than 3.8.
Claim 9
Dependent Claim
23 words
A method according to claim 1 where said extrudable silicone rubber composition and said uncured polyorganosiloxane gel composition include a platinum catalyst inhibitor.
Claim 10
Dependent Claim
12 words
A method according to claim 1 where said organohydrogensiloxane is a methylhydrogensiloxane.
Claim 11
Dependent Claim
15 words
A method according to claim 1 where said first layer included a platinum-containing hydrosilation catalyst.
Claim 12
Dependent Claim
19 words
A method according to claim 1 where said first layer is applied as a solution in an organic solvent.
Claim 13
Dependent Claim
12 words
A method according to claim 11 where said solvent is methylene chloride.
Claim 14
Dependent Claim
13 words
A method according to claim 1 where said substrate comprises an organic elastomer.
Claim 15
Dependent Claim
13 words
A method according to claim 13 where said organic elastomer is a polyurethane.
Claim 16
Dependent Claim
97 words
A composite consisting essentially of (I) a substrate wherein at least one surface thereof is coated with (II) a layer of cured silicone rubber that is cohesively bonded to said substrate by means of an organohydrogensiloxane and (III) a cured polyorganosiloxane gel overlaying said silicone rubber and cohesively bonded thereto, where said layer of silicone rubber is at least three millimeters thick, said silicone rubber exhibits a durometer of at least 10 on the Shore A scale, and where said organohydrogensiloxane, silicone rubber and polyorganosiloxane gel are cured concurrently by means of a platinum catalyzed hydrosilation reaction.
Claim 17
Dependent Claim
97 words
A composite consisting essentially of (I) a substrate wherein at least one surface thereof is coated with (II) a layer of cured silicone rubber that is cohesively bonded to said substrate by means of an organohydrogensiloxane and (III) a cured polyorganosiloxane gel overlaying said silicone rubber and cohesively bonded thereto, where said layer of silicone rubber is at least three millimeters thick, said silicone rubber exhibits a durometer of at least 10 on the Shore A scale, and where said organohydrogensiloxane, silicone rubber and polyorganosiloxane gel are cured concurrently by means of a platinum catalyzed hydrosilation reaction.
Claim 18
Dependent Claim
84 words
A composite according to claim 15 where said polyorganosiloxane gel in the uncured form comprises the product obtained by mixing (A) at least one diorganovinylsiloxy endblocked polyorganosiloxane exhibiting a viscosity of from 0.1 to 50 Pa.s at 25° C., (B) at least one polyorganohydrogensiloxane containing an average of at least three silicon-bonded hydrogen atoms per molecule in an amount sufficient to cure said polyorganosiloxane gel, and (C) platinum or a platinum compound in an amount sufficient to catalyze curing of said polyorganosiloxane gel composition.
Claim 19
Dependent Claim
70 words
A composite according to claim 16 where said polyorganosiloxane gel composition in the uncured form includes at least one polydiorganosiloxane containing a silicon-bonded hydrogen atom at each of the two terminal positions, the molar ratio of silicon-bonded hydrogen atoms to vinyl groups present in said gel is from 1.8 to 2.9 and said polydiorganosiloxane provides from 80 to 95 mol percent of the silicon-bonded hydrogen atoms present in said gel.
Claim 20
Dependent Claim
23 words
A composite according to claim 15 where silicon-bonded hydrocarbon radicals present in said silicone rubber and said polyorganosiloxane gel are vinyl and methyl.
Claim 21
Dependent Claim
131 words
A composite according to claim 16 where said product includes up to 25%, based on the weight of (A), of a resinous, benzene soluble copolymer consisting essentially of repeating units of the formulae (a) (CH 3 ) 2 CH 2 ═CHSiO 0 .5, (b) (CH 3 ) 3 SiO 0 .5 and (c) SiO 4/2 where the molar ratio of combined (a) and (b) units to (c) units is from 0.6:1 to 1.1:1, units represented by formula (a) constitute from 2 to 8% by weight of the copolymer, the copolymer contains at least two vinyl groups per molecule and the molar ratio of (a) to (b) to (c) units is 5-10:40-45:45-50, with the proviso that the concentration of (a) units does not exceed 8% of the total weight of said copolymer.
Claim 22
Dependent Claim
63 words
A composite according to claim 15 where said silicone rubber in the uncured form comprises the product obtained by mixing a diorganovinylsiloxy endblocked polydiorganosiloxane, an organohydrogensiloxane containing at least three silicon-bonded hydrogen atoms per molecule in an amount sufficient to cure said composition and a platinum-containing hydrosilation catalyst in an amount sufficient to promote curing of said composition at temperatures above 50° C.
Claim 23
Dependent Claim
115 words
A composite according to claim 20 where said polydiorganosiloxane is a mixture of polydimethylsiloxanes that collectively provides a molecular weight distribution such that there is present at least one polymeric species (1) at a concentration greater than the concentrations of polymeric species of lower and higher molecular weight, said species (1) having a molecular weight, determined by gel permeation chromatography, within the range from 68,000 to 135,000, where the lowest molecular weight species is within the range from 854 to 3146, the highest molecular weight species is within the range from 174,000 to 370,000 and the various polymeric species exhibit a molecular weight distribution such that the mixture exhibits a dispersity index greater than 3.8.
Claim 24
Dependent Claim
22 words
A composite according to claim 15 where the uncured forms of said silicone rubber and said gel include a platinum catalyst inhibitor.
Claim 25
Dependent Claim
12 words
A composite according to claim 15 where said organohydrogensiloxane is a methylhydrogensiloxane.
Claim 26
Dependent Claim
14 words
A composite according to claim 15 where said organohydrogensiloxane includes a platinum-containing hydrosilation catalyst.
Claim 27
Dependent Claim
21 words
A composite according to claim 15 where said organohydrogensiloxane is applied to said surface as a solution in an organic solvent.
Claim 28
Dependent Claim
13 words
A composite according to claim 25 where said organic solvent is methylene chloride.
Claim 29
Dependent Claim
13 words
A composite according to claim 15 where said substrate comprises an organic polymer.
Claim 30
Dependent Claim
13 words
A composite according to claim 27 where said organic polymer is a polyurethane.
References Cited (Backward Citations)
US4070224A
Cited
US4122127A
Cited
US4163082A
Cited
US4332844A
Cited
US4490496A
Cited
US4278707A
Cited
US4478895A
Cited
US4477499A
Cited
US4477517A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |