US4528082A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for sputtering a PIN amorphous silicon semi-conductor device having partially crystallized P and N-layers
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1983-09-26
•
Granted: 1985-07-09
•
Expires: 2003-09-26
Abstract
Abstract A high efficiency amorphous silicon PIN semiconductor device having partially crystallized (microcrystalline) P and N layers is constructed by the sequential sputtering of N, I and P layers and at least one semi-transparent ohmic electrode. The method of construction produces a PIN device, exhibiting enhanced electrical and optical properties, improved physical integrity, and facilitates the preparation in a singular vacuum system and vacuum pump down procedure.
Inventors
- 👤 Theodore D. Moustakas
- 👤 H. Paul Maruska
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:56
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/10; H10F71/103; H10D; H10D62/00; H10D62/40; H10D8/00; H10D8/50; H10F10/00; H10F10/10; H10F10/17; H10F77/00; H10F77/10; H10F77/16; H10F77/169; H10F77/1692; H10P; H10P14/00; H10P14/20; H10P14/22; H10P14/24; H10P14/29; H10P14/2901; H10P14/2922; H10P14/2923; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3438; H10P14/3441; H10P14/3442; H10P14/3444; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/548; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
190 words
A method for producing an amorphous silicon PIN semi-conductor device having partially crystallized microcrystalline P and N-layers comprising: providing a substrate having at least a surface region comprising an electroconductive material which forms an ohmic contact to doped microcrystalline silicon; reactively RF diode sputtering a layer of microcrystalline silicon doped with one type of charge carrier in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon ranging from about 3 mTorr to about 10 mTorr onto at least said surface region of the substrate; reactively RF diode sputtering a layer of amorphous intrinsic, I, silicon onto said layer of silicon doped with said one type of charge carrier; reactively RF diode sputtering a layer of microcrystalline silicon doped with the opposite type of charge carrier in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon ranging from about 3 mTorr to about 10 mTorr onto said I layer; sputtering an electroconductive material onto at least a region of said layer of microcrystalline silicon doped with said opposite type of charge carrier which material forms an ohmic contact thereto.
Claim 2
Independent Claim
190 words
A method for producing an amorphous silicon PIN semi-conductor device having partially crystallized microcrystalline P and N-layers comprising: providing a substrate having at least a surface region comprising an electroconductive material which forms an ohmic contact to doped microcrystalline silicon; reactively RF diode sputtering a layer of microcrystalline silicon doped with one type of charge carrier in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon ranging from about 3 mTorr to about 10 mTorr onto at least said surface region of the substrate; reactively RF diode sputtering a layer of amorphous intrinsic, I, silicon onto said layer of silicon doped with said one type of charge carrier; reactively RF diode sputtering a layer of microcrystalline silicon doped with the opposite type of charge carrier in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon ranging from about 3 mTorr to about 10 mTorr onto said I layer; sputtering an electroconductive material onto at least a region of said layer of microcrystalline silicon doped with said opposite type of charge carrier which material forms an ohmic contact thereto.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said one type of charge carrier is N type and said opposite type of charge carrier is P type.
Claim 4
Dependent Claim
57 words
The method of claim 2 wherein said reactive sputtering of N doped microcrystalline silicon comprises sputtering microcrystalline silicon in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon ranging from about 3 mTorr to about 10 mTorr, said argon including about 0.2 to 1 atomic % of phosphine (PH 3 ).
Claim 5
Dependent Claim
18 words
The method of claim 3 wherein said N-doped microcrystalline silicon is sputtered from an undoped polycrystalline silicon target.
Claim 6
Dependent Claim
25 words
The method of claim 4 wherein said target is about five inches in diameter and located a distance of about 4.5 cm from said substrate.
Claim 7
Dependent Claim
36 words
The method of claim 5 wherein an RF sputtering power of about 100 watts to 200 watts is coupled to the plasma, resulting in a target dc voltage of about -800 volts to about -2000 volts.
Claim 8
Dependent Claim
22 words
The method of claim 6 wherein said substrate is maintained at a temperature ranging from about 200° C. to about 400° C.
Claim 9
Dependent Claim
20 words
The method of claim 2 wherein said N layer ranges in thickness from about 100 up to about 1,000 Angstroms.
Claim 10
Dependent Claim
23 words
The method of claim 2 wherein said N layer comprises a doping level gradient of phosphorus through the thickness of the N layer.
Claim 11
Dependent Claim
61 words
The method of claim 2 wherein said reactive sputtering of the P layer of microcrystalline silicon comprises sputtering microcrystalline silicon in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon, ranging from about 3 mTorr to about 10 mTorr, said argon containing about 0.2 to 1 atomic % of diborane, B 2 H 6 .
Claim 12
Dependent Claim
20 words
The method of claim 10 wherein said P layer ranges in thickness from about 80 Å to about 150 Angstroms.
Claim 13
Dependent Claim
15 words
The method of claim 11 wherein said P layer is about 100 Å in thickness.
Claim 14
Dependent Claim
35 words
The method of claim 2 wherein said electroconductive material, sputtered onto said P-doped microcrystalline silicon is a thin film of material selected from the group consisting of indium tin oxide, tin oxide, and cadmium stannate.
Claim 15
Dependent Claim
17 words
The method of claim 13 wherein said electroconductive material is a thin film of indium tin oxide.
Claim 16
Dependent Claim
25 words
The method of claim 1 wherein said one type of charge carrier is P type and said opposite type of charge carrier is N type.
Claim 17
Dependent Claim
57 words
The method of claim 15 wherein said reactive sputtering of N doped microcrystalline silicon comprises sputtering microcrystalline silicon in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon ranging from about 3 mTorr to about 10 mTorr, said argon including about 0.2 to 1 atomic % of phosphine (PH 3 ).
Claim 18
Dependent Claim
18 words
The method of claim 16 wherein said N-doped microcrystalline silicon is sputtered from an undoped polycrystalline silicon target.
Claim 19
Dependent Claim
36 words
The method of claim 17 wherein an RF sputtering power of about 100 watts to 200 watts is coupled to the plasma, resulting in a target dc voltage of about -800 volts to about -2000 volts.
Claim 20
Dependent Claim
23 words
The method of claim 15 wherein said N layer comprises a doping level gradient of phosphorus through the thickness of the N layer.
Claim 21
Dependent Claim
61 words
The method of claim 15 wherein said reactive sputtering of the P layer of microcrystalline silicon comprises sputtering microcrystalline silicon in partial pressures of hydrogen, ranging from about 20 mTorr to about 80 mTorr, and argon, ranging from about 3 mTorr to about 10 mTorr, said argon containing about 0.2 to 1 atomic % of diborane, B 2 H 6 .
Claim 22
Dependent Claim
20 words
The method of claim 1 wherein said substrate is selected from the group consisting of Mo, stainless steel, and Cr.
Claim 23
Dependent Claim
23 words
The method of claim 1 wherein said substrate comprises glass having an electroconductive coating of indium tin oxide, Tin oxide, or cadmium stanate.
Claim 24
Dependent Claim
44 words
The method of claim 1 wherein said reactive sputtering of the intrinsic, I, layer of silicon comprises sputtering silicon in partial pressures of hydrogen, ranging from about 0.3 mTorr to about 1.5 mTorr, and argon, ranging from about 3 mTorr to about 15 mTorr.
Claim 25
Dependent Claim
20 words
The method of claim 23 wherein said intrinsic layer ranges in thickness from about 0.2 μm to about 1.5 μm.
Claim 26
Dependent Claim
47 words
The method of claim 24 wherein an RF sputtering power of about 100 watts to 200 watts is used to sputter said intrinsic silicon layer from an undoped target which is about five inches in diameter and located a distance of about 4.5 cm from said substrates.
Claim 27
Dependent Claim
25 words
The method of claim 23 wherein said substrates are maintained at a temperature ranging from about 200° C. to about 400° C. during said sputtering.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |