US4528063A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for refinishing rigid data storage discs
Assignee: WINCHESTER DISC Inc 710 SYCAMORE DRIVE MILPITAS CA 95035 A CORP OF
•
Filing: 1984-06-15
•
Granted: 1985-07-09
•
Expires: 2004-06-15
Abstract
Abstract A method for refinishing rigid data storage discs for recoating including the steps of removing a magnetically alterable coating and its sub-interfacing material from rigid data storage discs to expose disc substrates, inspecting the substrate for surface discontinuities, measuring the thickness and flatness of the substrates, resurfacing the surfaces of the substrates to remove surface unevenness and surface discontinuities, polishing the surfaces of the substrates to produce a visually mar-free flat substrates, and rinsing and drying the substrate before recoating.
Inventors
- 👤 John E. Lawrence
- 👤 Lloyd L. Barnes, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 01:06
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/44; C23G; C23G1/00; C23G1/02; C23G1/12; C23G1/125; G; G11; G11B; G11B5/00; G11B5/84
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
236 words
A method for refinishing data storage discs, comprising the steps of: removing from a data storage disc a coating adhered to a planar surface of a rigid substrate to expose the substrate surface; measuring the actual thickness and flatness of said substrate; inspecting said planar surface for surface discontinuities exceeding a predetermined depth; inspecting the texture of said planar surface for roughness exceeding a predetermined roughness value; comparing the actual thickness value of said substrate with a predetermined thickness value; comparing the actual flatness of said substrate with a predetermined flatness value; resurfacing said planar surface of those said substrate having actual flatness values greater than or equal to said predetermined flatness values to create resurfaced substrate having a planar surface of a flatness value less than said predetermined flatness value; polishing said resurfaced substrate and non-discarded substrate to create a visually discontinuity-free substrate without tapering the edges of said substrate beyond a predetermined level, whereby said predetermined level maintains and ensures that said substrate edges are sufficient to prevent transducer head contact with said substrate edges when said substrate is recoated and used in a data storage media device; rinsing said substrate with a rinsing fluid to remove residue foreign material from the substrate; and drying said substrate to remove residue rinsing fluid from said substrate whereby a chemically clean coating free substrate acceptable for future use in said data storage media device is created.
Claim 2
Independent Claim
236 words
A method for refinishing data storage discs, comprising the steps of: removing from a data storage disc a coating adhered to a planar surface of a rigid substrate to expose the substrate surface; measuring the actual thickness and flatness of said substrate; inspecting said planar surface for surface discontinuities exceeding a predetermined depth; inspecting the texture of said planar surface for roughness exceeding a predetermined roughness value; comparing the actual thickness value of said substrate with a predetermined thickness value; comparing the actual flatness of said substrate with a predetermined flatness value; resurfacing said planar surface of those said substrate having actual flatness values greater than or equal to said predetermined flatness values to create resurfaced substrate having a planar surface of a flatness value less than said predetermined flatness value; polishing said resurfaced substrate and non-discarded substrate to create a visually discontinuity-free substrate without tapering the edges of said substrate beyond a predetermined level, whereby said predetermined level maintains and ensures that said substrate edges are sufficient to prevent transducer head contact with said substrate edges when said substrate is recoated and used in a data storage media device; rinsing said substrate with a rinsing fluid to remove residue foreign material from the substrate; and drying said substrate to remove residue rinsing fluid from said substrate whereby a chemically clean coating free substrate acceptable for future use in said data storage media device is created.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein the removal of the coating includes exposing said coating to a heated acid solution for a predetermined time period until said substrate is coating free.
Claim 4
Dependent Claim
41 words
The method of claim 2 wherein the coating includes ferric oxide, said acid solution includes sulfuric acid and is heated to at least 20° C. (68° F.), and said coating is exposed to the acid solution for at least fifteen seconds.
Claim 5
Dependent Claim
20 words
The method of claim 3 wherein said disc is inspected to determine if said substrate is free of the coating.
Claim 6
Dependent Claim
48 words
The method of claim 4 wherein said disc is heated for a predetermined time to cause a molecular change in the coating when the coating has not been removed by said acid solution after its first exposure, and then again exposing said disc to said heated acid solution.
Claim 7
Dependent Claim
35 words
The method of claim 5 wherein said coating free substrate is rinsed with a rinsing liquid to remove residue acid solution from said substrate and then dried to remove residue rinsing liquid from said substrate.
Claim 8
Dependent Claim
36 words
The method of claim 1 wherein the coating includes nickel, said substrate includes aluminum, and said acid solution includes nitric acid whereby said nickel coating is removed from said aluminum substrate without damaging said substrate surface.
Claim 9
Dependent Claim
46 words
The method of claim 7 wherein said solution is at least a forty-five percent solution of buffered nitric acid heated to at least 20° C. (68° F.); and said media is exposed to said solution for at least fifteen seconds to create a coating free substrate.
Claim 10
Dependent Claim
37 words
The method of claim 8 wherein the coating free substrate is rinsed in a rinsing liquid to remove residue acid from the surfaces of said substrate; and said rinsed substrate is dried to remove residue rinsing liquid.
Claim 11
Dependent Claim
104 words
The method of claim 1 wherein said chemically clean coating free substrate are remeasured to determine actual thickness and flatness values, the actual thickness and flatness values are compared to predetermined thickness and flatness values, and discarding those substrates having an actual thickness value less than the predetermined value, and discarding substrates having an actual flatness values in excess of the predetermined flatness value if resurfacing of the substrate would reduce the thickness of the substrate below the predetermined value; and resurfacing those substrates for which resurfacing would not cause the substrate to have an actual thickness value less than the predetermined thickness value.
Claim 12
Dependent Claim
72 words
The method of claim 10 including inspecting the surfaces of said chemically clean coating-free substrate for surface discontinuities and roughness; discarding substrates having surface discontinuities greater than a predetermined depth; and resurfacing substrates having surface roughness in excess of a predetermined roughness value to create a substrate having surfaces free of visual discontinuities provided that resurfacing does not create a substrate with an actual thickness value less than the predetermined thickness value.
Claim 13
Dependent Claim
22 words
The method of claim 1 wherein said polished substrate is rinsed in a cascade rinse having at least fourteen megohm deionized water.
Claim 14
Dependent Claim
30 words
The method of claim 12 wherein said polished substrate is rinsed in at least a class 100 clean room environment to prevent airborne contamination of the surfaces of said substrate.
Claim 15
Dependent Claim
22 words
The method of claim 13 wherein said rinsed substrate is dried in a rinse/dry apparatus having at least fourteen megohm deionized water.
Claim 16
Dependent Claim
21 words
The method of claim 14 wherein said substrate is placed in a clean gas environment when said substrate is spun dry.
Claim 17
Dependent Claim
51 words
The method of claim 15 wherein said chemically clean coating-free substrate are remeasured to determine actual thickness and flatness values of the substrate, the actual thickness and flatness values are compared to predetermined thickness and flatness values, and discarding those substrates having an actual thickness values less than the predetermined value.
Claim 18
Dependent Claim
53 words
The method of claim 6 including inspecting the surfaces of said chemically clean coating-free substrate for surface discontinuities and roughness; discarding substrates having surface discontinuities greater than a predetermined depth; and resurfacing substrates having surface roughness in excess of a predetermined roughness value to create a substrate having surfaces free of visual discontinuities.
Claim 19
Dependent Claim
18 words
The method of claim 17 wherein the data storage discs are rigid; and said substrate is disc shaped.
Claim 20
Dependent Claim
15 words
The method of claim 10 wherein said substrates are resurfaced in a lathe resurfacing process.
Claim 21
Dependent Claim
15 words
The method of claim 11 wherein said substrates are resurfaced in a lathe resurfacing process.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-08 | 1989-01-07 | 1989-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-08 | 1993-01-07 | 1993-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-08 | 1997-01-07 | 1997-07-09 | $7700.00 | Window Closed / Lapsed |