Aqueous quenchants containing polyoxazolines and n-vinyl heterocyclic polymers and their use in quenching steel

Claim 2

In the process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium an aqueous composition comprising an effective cooling rate reducing amount of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR4## where R is an organic radical which does not significantly alter the nonionic and water-soluble and water-dispersible characteristics of said oxazoline polymer when said polymer is present in said concentrations, and n is an integer such as to provide said oxazoline polymer with a molecular weight of from about 5000 to 1,000,000 and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer in which the heterocyclic group is composed of carbon, nitrogen and oxygen, said N-vinyl polymer or copolymer having a molecular weight of from about 5000 to about 400,000.

Claim 3

A process according to claim 1 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, said oxazoline polymer has a molecular weight of from about 50,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 50,000 to 360,000.

Claim 4

A process according to claim 2 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to about 1.5%, said oxazoline polymer has a molecular weight in the range of from about 200,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 100,000 to 200,000.

Claim 5

The process according to claim 3 in which the weight ratio component (a) to component (b) in said bath is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 6

The process according to claim 4 in which the weight ratio of component (a) to component (b) in said bath is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 7

The process according to claim 5 in which the weight ratio of component (a) to component (b) in said quenching bath is about 75% component (a) and 25% component (b).

Claim 8

In the process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium a composition comprising an effective cooling rate reducing amount of a mixture of (a), a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the formula ##STR5## where R is a substituent selected from the group consisting of a phenyl group or an alkyl group containing from 1 to 7 carbon atoms which may be halogen substituted, and n is an integer such as to provide said polymer with a molecular weight of from about 5000 to about 1,000,000, the substituent R in at least about 50 percent of said units in said polymer being alkyl containing from 1 to 3 carbon atoms, and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer selected from the group consisting of polyvinylpyrrolidone, and copolymers of N-vinyl pyrrolidone with styrene, vinyl acetate, maleic anhydride, or a methacylate, said N-vinyl heterocyclic compound having a molecular weight of from about 5000 to 400,000.

Claim 9

In the process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium a composition comprising an effective cooling rate reducing amount of a mixture of (a), a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the formula ##STR5## where R is a substituent selected from the group consisting of a phenyl group or an alkyl group containing from 1 to 7 carbon atoms which may be halogen substituted, and n is an integer such as to provide said polymer with a molecular weight of from about 5000 to about 1,000,000, the substituent R in at least about 50 percent of said units in said polymer being alkyl containing from 1 to 3 carbon atoms, and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer selected from the group consisting of polyvinylpyrrolidone, and copolymers of N-vinyl pyrrolidone with styrene, vinyl acetate, maleic anhydride, or a methacylate, said N-vinyl heterocyclic compound having a molecular weight of from about 5000 to 400,000.

Claim 10

A process according to claim 7 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, said oxazoline polymer has a molecular weight of from about 50,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 50,000 to 360,000.

Claim 11

A process according to claim 8 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to about 1.5%, said oxazoline polymer has a molecular weight in the range of from about 200,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 100,000 to 200,000.

Claim 12

The process according to claim 9 in which the weight ratio component (a) to component (b) in said bath is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 13

The process according to claim 10 in which the weight ratio of component (a) to component (b) in said bath is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 14

The process according to claim 11 in which the weight ratio of component (a) to component (b) in said quenching bath is about 75% component (a) and 25% component (b).

Claim 15

In a process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium an aqueous solution containing from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR6## where n is an integer such as to provide said polymer with a molecular weight of from about 50,000 to 500,000, and (b) a water-soluble or water-dispersible polyvinylpyrrolidone having a molecular weight of from about 50,000 to 360,000.

Claim 16

In a process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium an aqueous solution containing from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR6## where n is an integer such as to provide said polymer with a molecular weight of from about 50,000 to 500,000, and (b) a water-soluble or water-dispersible polyvinylpyrrolidone having a molecular weight of from about 50,000 to 360,000.

Claim 17

The process according to claim 13 in which the total concentration of the polymer mixture in said quenching medium is from about 0.5% to about 1.5%, said polyoxazoline has a molecular weight of from about 200,000 to 500,000, and said polyvinylpyrrolidone has a molecular weight of from about 100,000 to 200,000.

Claim 18

The process according to claim 14 in which the weight ratio component (a) to component (b) in said bath is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 19

The process according to claim 15 in which the weight ratio of component (a) to component (b) in said bath is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 20

The process according to claim 16 in which the weight ratio of component (a) to component (b) in said quenching bath is about 75% component (a) and 25% component (b).

Claim 21

A quenching medium which is useful in the heat treatment of metals comprising aqueous composition containing an effective cooling rate reducing amount of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR7## where R is an organic radical which does not significantly alter the nonionic and water-soluble and water-dispersible characteristics of said oxazoline polymer when said polymer is present in said concentrations, and n is an integer such as to provide said oxazoline polymer with a molecular weight of from about 5000 to 1,000,000 and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer in which the heterocyclic group is composed of carbon, nitrogen and oxygen, said N-vinyl polymer or copolymer having a molecular weight of from about 5000 to about 400,000.

Claim 22

A quenching medium which is useful in the heat treatment of metals comprising aqueous composition containing an effective cooling rate reducing amount of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR7## where R is an organic radical which does not significantly alter the nonionic and water-soluble and water-dispersible characteristics of said oxazoline polymer when said polymer is present in said concentrations, and n is an integer such as to provide said oxazoline polymer with a molecular weight of from about 5000 to 1,000,000 and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer in which the heterocyclic group is composed of carbon, nitrogen and oxygen, said N-vinyl polymer or copolymer having a molecular weight of from about 5000 to about 400,000.

Claim 23

A quenching medium according to claim 18 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, said oxazoline polymer has a molecular weight of from about 50,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 50,000 to 360,000.

Claim 24

A quenching medium according to claim 19 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to about 1.5%, said oxazoline polymer has a molecular weight in the range of from about 200,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 100,000 to 200,000.

Claim 25

The quenching medium according to claim 20 in which the weight ratio component (a) to component (b) in said bath is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 26

A quenching medium according to claim 21 in which the weight ratio of component (a) to component (b) in said medium is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 27

A quenching medium according to claim 22 in which the weight ratio of component (a) to component (b) in said quenching medium is about 75% component (a) and 25% component (b).

Claim 28

A quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing an effective cooling rate reducing amount of a mixture of (a), a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the formula ##STR8## where R is a substituent selected from the group consisting of a phenyl group or an alkyl group containing from 1 to 7 carbon atoms which may be halogen substituted, and n is an integer such as to provide said polymer with a molecular weight of from about 5000 to about 1,000,000, the substituent R in at least about 50 percent of said units in said polymer being alkyl containing from 1 to 3 carbon atoms, and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer selected from the group consisting of polyvinylpyrrolidone, and copolymers of N-vinyl pyrrolidone with styrene, vinyl acetate, meleic anhydride, or a methacylate, said N-vinyl heterocyclic compound having a molecular weight of from about 5000 to 400,000.

Claim 29

A quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing an effective cooling rate reducing amount of a mixture of (a), a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the formula ##STR8## where R is a substituent selected from the group consisting of a phenyl group or an alkyl group containing from 1 to 7 carbon atoms which may be halogen substituted, and n is an integer such as to provide said polymer with a molecular weight of from about 5000 to about 1,000,000, the substituent R in at least about 50 percent of said units in said polymer being alkyl containing from 1 to 3 carbon atoms, and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer selected from the group consisting of polyvinylpyrrolidone, and copolymers of N-vinyl pyrrolidone with styrene, vinyl acetate, meleic anhydride, or a methacylate, said N-vinyl heterocyclic compound having a molecular weight of from about 5000 to 400,000.

Claim 30

A quenching medium according to claim 24 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, said oxazoline polymer has a molecular weight of from about 50,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 50,000 to 360,000.

Claim 31

A quenching medium according to claim 25 in which the total concentration of said mixture of polymers in said quenching medium is from about 0.5% to about 1.5%, said oxazoline polymer has a molecular weight in the range of from about 200,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 100,000 to 200,000.

Claim 32

The quenching medium according to claim 26 in which the weight ratio of component (a) to component (b) in said medium is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 33

A quenching medium according to claim 27 in which the weight ratio of component (a) to component (b) in said medium is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 34

A quenching medium according to claim 28 in which the weight ratio of component (a) to component (b) in said quenching medium is about 75% component (a) and 25% component (b).

Claim 35

A quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR9## where n is an integer such as to provide said polymer with a molecular weight of from about 50,000 to 500,000, and (b) a water-soluble or water-dispersible polyvinylpyrrolidone having a molecular weight of from about 50,000 to 360,000.

Claim 36

A quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing from about 0.5% to 3%, by weight, based on the total weight of the quenching medium, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR9## where n is an integer such as to provide said polymer with a molecular weight of from about 50,000 to 500,000, and (b) a water-soluble or water-dispersible polyvinylpyrrolidone having a molecular weight of from about 50,000 to 360,000.

Claim 37

A quenching medium according to claim 30 in which the total concentration of the polymer mixture in said quenching medium is from about 0.5% to about 1.5%, said polyoxazoline has a molecular weight of from about 200,000 to 500,000, and said polyvinylpyrrolidone has a molecular weight of from about 100,000 to 200,000.

Claim 38

The quenching medium according to claim 31 in which the weight ratio component (a) to component (b) in said bath is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 39

A quenching medium according to claim 31 in which the weight ratio of component (a) to component (b) in said medium is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 40

A quenching medium according to claim 33 in which the weight ratio of component (a) to component (b) in said quenching medium is about 75% component (a) and 25% component (b).

Claim 41

A concentrate for forming a quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing at least about 5%, by weight, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR10## where R is an organic radical which does not significantly alter the nonionic and water-soluble and water-dispersible characteristics of said oxazoline polymer when said polymer is present in said concentrations, and n is an integer such as to provide said oxazoline polymer with a molecular weight of from about 5000 to 1,000,000 and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer in which the heterocyclic group is composed of carbon, nitrogen and oxygen, said N-vinyl polymer or copolymer having a molecular weight of from about 5000 to about 400,000.

Claim 42

A concentrate for forming a quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing at least about 5%, by weight, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR10## where R is an organic radical which does not significantly alter the nonionic and water-soluble and water-dispersible characteristics of said oxazoline polymer when said polymer is present in said concentrations, and n is an integer such as to provide said oxazoline polymer with a molecular weight of from about 5000 to 1,000,000 and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer in which the heterocyclic group is composed of carbon, nitrogen and oxygen, said N-vinyl polymer or copolymer having a molecular weight of from about 5000 to about 400,000.

Claim 43

A concentrate according to claim 35 in which the total concentration of said mixture of polymers in said concentrate is from about 5% to 70%, by weight, based on the total weight of the concentrate, said oxazoline polymer has a molecular weight of from about 50,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 50,000 to 360,000.

Claim 44

A concentrate according to claim 36 in which the total concentration of said mixture of polymers in said concentrate is from about 5% to about 10%, said oxazoline polymer has a molecular weight in the range of from about 200,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 100,000 to 200,000.

Claim 45

The concentrate to claim 37 in which the weight ratio of component (a) to component (b) in said concentrate is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 46

A concentrate according to claim 38 in which the weight ratio of component (a) to component (b) in said concentrate is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 47

A concentrate according to claim 39 in which the weight ratio of component (a) to component (b) in said concentrate is about 75% component (a) and 25% component (b).

Claim 48

A concentrate for forming a quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing at least about 5%, by weight, of a mixture of (a), a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having requiring units of the formula ##STR11##

Claim 49

A concentrate for forming a quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing at least about 5%, by weight, of a mixture of (a), a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having requiring units of the formula ##STR11##

Claim 50

where R is a substituent selected from the group consisting of a phenyl group or an alkyl group containing from 1 to 7 carbon atoms which may be halogen substituted, and n is an integer such as to provide said polymer with a molecular weight of from about 5000 to about 1,000,000, the substituent R in at least about 50 percent of said units in said polymer being alkyl containing from 1 to 3 carbon atoms, and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer selected from the group consisting of polyvinylpyrrolidone, and copolymers of N-vinyl pyrrolidone with styrene, vinyl acetate, maleic anhydride, or a methacylate, said N-vinyl heterocyclic compound having a molecular weight of from about 5000 to 400,000.

Claim 51

where R is a substituent selected from the group consisting of a phenyl group or an alkyl group containing from 1 to 7 carbon atoms which may be halogen substituted, and n is an integer such as to provide said polymer with a molecular weight of from about 5000 to about 1,000,000, the substituent R in at least about 50 percent of said units in said polymer being alkyl containing from 1 to 3 carbon atoms, and (b) a water-soluble or water-dispersible N-vinyl heterocyclic polymer or copolymer selected from the group consisting of polyvinylpyrrolidone, and copolymers of N-vinyl pyrrolidone with styrene, vinyl acetate, maleic anhydride, or a methacylate, said N-vinyl heterocyclic compound having a molecular weight of from about 5000 to 400,000.

Claim 52

A concentrate according to claim 41 in which the total concentration of said mixture of polymers in said concentrate is from about 5% to about 70%, by weight, based on the total weight of the concentrate, said oxazoline polymer has a molecular weight of from about 50,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 50,000 to 360,000.

Claim 53

A concentrate according to claim 42 in which the total concentration of said mixture of polymers in said concentrate is from about 5% to about 10%, said oxazoline polymer has a molecular weight in the range of from about 200,000 to about 500,000, and said N-vinyl polymer or copolymer has a molecular weight of from about 100,000 to 200,000.

Claim 54

The concentrate according to claim 43 in which the weight ratio of component (a) to component (b) in said concentrate is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 55

A concentrate according to claim 44 in which the weight ratio of component (a) to component (b) in said concentrate is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 56

A concentrate according to claim 45 in which the weight ratio of component (a) to component (b) in said concentrate is about 75% component (a) and 25% component (b).

Claim 57

A concentrate for forming a quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing at least about 5%, by weight, based on the total weight of the concentrate, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR12## where n is an integer such as to provide said polymer with a molecular weight of from about 50,000 to 500,000, and (b) a water-soluble or water-dispersible polyvinylpyrrolidone having a molecular weight of from about 50,000 to 360,000.

Claim 58

A concentrate for forming a quenching medium which is useful in the heat treatment of metals comprising an aqueous composition containing at least about 5%, by weight, based on the total weight of the concentrate, of a mixture of (a) a nonionic, water-soluble or water-dispersible substituted oxazoline polymer having recurring units of the general formula ##STR12## where n is an integer such as to provide said polymer with a molecular weight of from about 50,000 to 500,000, and (b) a water-soluble or water-dispersible polyvinylpyrrolidone having a molecular weight of from about 50,000 to 360,000.

Claim 59

A concentrate according to claim 47 in which the total concentration of the polymer mixture in said concentrate is from about 5% to about 10%, said polyoxazoline has a molecular weight of from about 200,000 to 500,000, and said polyvinylpyrrolidone has a molecular weight of from about 100,000 to 200,000.

Claim 60

The concentrate according to claim 48 in which the weight ratio of component (a) to component (b) in said concentrate is in the range of from about 90% of component (a) to about 10% of component (b) to about 10% of component (a) to about 90% of component (b).

Claim 61

A concentrate according to claim 49 in which the weight ratio of component (a) to component (b) in said concentrate is in the range of from about 75% of component (a) to 25% of component (b) to 25% of component (a) to 75% of component (b).

Claim 62

A concentrate according to claim 50 in which the weight ratio of component (a) to component (b) in said concentrate is about 75% component (a) and 25% component (b).