Process for the controlled cooling of ferrous metal
Assignee: EF Houghton and Co
•
Filing: 1975-07-03
•
Granted: 1978-05-02
•
Expires: 1995-07-03
Abstract
Abstract Austenitized ferrous metal, such as carbon steel, is quenched by means of an aqueous solution of a salt of polyacrylic acid which develops an extremely stable and uniform water vapor envelope surrounding the steel. Rate of cooling is controlled by (1) the molecular weight of the salt, (2) concentration of the salt in the solution, (3) solution temperature, and (4) the degree of agitation of the quenchant solution. In the case of carbon steel, by proper selection of the above variables, the austenitic structure of the hot steel may be directly transformed into non-martensitic structures of improved ductility, machinability and cold working properties, such as fine striped pearlite, without the necessity of further heat treatments, such as tempering, following quenching. The quenching solution may also be used to quench parts formed of alloy steel to obtain a martensitic structure without unwanted cracking and distortion. Non-ferrous metals may also be quenched using the polyacrylate quenching solution.
Inventors
- 👤 Karl-Heinz Kopietz
- 👤 Francis S. Munjat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:38
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/56; C21D1/60
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
125 words
In a process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium an aqueous solution containing from about 0.1% to about 6% by weight of a water-soluble salt of polyacrylic acid selected from the group consisting of sodium, potassium, ammonium, lower alkylamine and lower alkanolamine polyacrylates, and mixtures thereof, said salt having a molecular weight such that an aqueous solution thereof containing 20% by weight of said salt has a viscosity of from about 5,000 to about 100,000 centipoises at 25° C.
Claim 2
Dependent Claim
125 words
In a process of quenching which is useful in the heat treatment of metals wherein a metal is heated to an elevated temperature and said heated metal is then quenched in a bath comprising a liquid quenching medium to effect desirable metallurgical changes in the metal, the improvement which comprises using as said quenching medium an aqueous solution containing from about 0.1% to about 6% by weight of a water-soluble salt of polyacrylic acid selected from the group consisting of sodium, potassium, ammonium, lower alkylamine and lower alkanolamine polyacrylates, and mixtures thereof, said salt having a molecular weight such that an aqueous solution thereof containing 20% by weight of said salt has a viscosity of from about 5,000 to about 100,000 centipoises at 25° C.
Claim 3
Dependent Claim
136 words
In a process of quenching which is useful in the heat treatment of steel wherein said steel to be heat treated is heated to an austenitizing temperature and said heated steel is then quenched in a bath comprising a liquid quenching medium to provide said steel with a non-martensitic microstructure of improved ductility and cold working properties, the improvement which comprises using as said quenching medium an aqueous solution containing from about 0.1% to about 6% by weight of a water-soluble salt of polyacrylic acid selected from the group consisting of sodium, potassium, ammonium, lower alkylamine and lower alkanolamine polyacrylates, and mixtures thereof, said salt having a molecular weight such that an aqueous solution thereof containing 20% by weight of said salt has a viscosity of from about 5,000 to about 100,000 centipoises at 25° C.
Claim 4
Dependent Claim
136 words
In a process of quenching which is useful in the heat treatment of steel wherein said steel to be heat treated is heated to an austenitizing temperature and said heated steel is then quenched in a bath comprising a liquid quenching medium to provide said steel with a non-martensitic microstructure of improved ductility and cold working properties, the improvement which comprises using as said quenching medium an aqueous solution containing from about 0.1% to about 6% by weight of a water-soluble salt of polyacrylic acid selected from the group consisting of sodium, potassium, ammonium, lower alkylamine and lower alkanolamine polyacrylates, and mixtures thereof, said salt having a molecular weight such that an aqueous solution thereof containing 20% by weight of said salt has a viscosity of from about 5,000 to about 100,000 centipoises at 25° C.
Claim 5
Dependent Claim
40 words
A process according to claim 1 in which said salt has a molecular weight such that an aqueous solution containing 20% by weight of said salt has a viscosity of from about 25,000 to about 75,000 centipoises at 25° C.
Claim 6
Dependent Claim
40 words
A process according to claim 2 in which said salt has a molecular weight such that an aqueous solution containing 20% by weight of said salt has a viscosity of from about 25,000 to about 75,000 centipoises at 25° C.
References Cited (Backward Citations)
US2600290A
Cited
US2770564A
Cited
US3220893A
Cited
US3563895A
Cited
US3669762A
Cited
US3939016A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-01 | 1981-10-31 | 1982-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-01 | 1985-10-31 | 1986-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-01 | 1989-10-31 | 1990-05-02 | $7700.00 | Window Closed / Lapsed |