Method of producing carbon fiber and product thereof
Assignee: Fiber Materials Inc
•
Filing: 1982-06-04
•
Granted: 1985-07-02
•
Expires: 2002-06-04
Abstract
Abstract A novel process is provided for the formation of improved carbonized fibrous materials with increased modulus of elasticity and strength as well as decreased diameter. Preferably, the precursor material is acrylonitrile, typically copolymerized with a minor amount of an acrylic monomer such as methyl acrylate. Drawing of the polymer fiber during oxidation is effected at an elevated temperature in the presence of a carboxylic acid (other than formic acid), or its anhydride, within the fiber. It is believed that the acid and/or its anhydride which is formed at the oxidizing temperature serves as a plasticizer and reduces the fiber yield stress and increases fiber plasticity so that the fibers may be drawn by as much as 300% or more in the presence of the acid and/or its anhydride during oxidation, thereby providing the desired improvement in increased modulus of elasticity and tensile strength of carbon fibers formed subsequently by carbonization of the oxidized fibers.
Inventors
- 👤 Roger T. Pepper
- 👤 Daniel C. Nelson
- 👤 Douglas S. Lewing
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 19:28
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/20; D01F9/21; D01F9/22
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
134 words
In a method of oxidizing fibers of an acrylic polymer comprising recurring acrylonitrile units, wherein said fibers are oxidized in an oxidizing atmosphere heated to a temperature range between about 180° C. to about 300° C. preparatory to carbonization of said fibers, and during oxidation said fibers are drawn under tension, the improvement comprising the steps of permeating said polymer with a carboxylic acid capable of forming its anhydride when heated to within said temperature range, and drawing said permeated fibers under tension during oxidation of said fibers in said atmosphere within said temperature range, said carboxylic acid being present initially in said polymer in an amount sufficient to permit improved drawing of the fiber to at least double the original fiber length, and to an average fiber diameter of less than 10 microns.
Claim 2
Dependent Claim
134 words
In a method of oxidizing fibers of an acrylic polymer comprising recurring acrylonitrile units, wherein said fibers are oxidized in an oxidizing atmosphere heated to a temperature range between about 180° C. to about 300° C. preparatory to carbonization of said fibers, and during oxidation said fibers are drawn under tension, the improvement comprising the steps of permeating said polymer with a carboxylic acid capable of forming its anhydride when heated to within said temperature range, and drawing said permeated fibers under tension during oxidation of said fibers in said atmosphere within said temperature range, said carboxylic acid being present initially in said polymer in an amount sufficient to permit improved drawing of the fiber to at least double the original fiber length, and to an average fiber diameter of less than 10 microns.
Claim 3
Dependent Claim
12 words
A process according to claim 1 wherein said polymer is acrylonitrile homopolymer.
Claim 4
Dependent Claim
29 words
A process according to claim 3 wherein said polymer is an acrylonitrile polymer containing at least about 85 mole percent of acrylonitrile units copolymerized with at least another material.
Claim 5
Dependent Claim
13 words
A process according to claim 1 wherein said acid is a monocarboxylic acid.
Claim 6
Dependent Claim
13 words
A process according to claim 1 wherein said acid is a dicarboxylic acid.
Claim 7
Dependent Claim
20 words
A process according to claim 1 wherein said acid is selected from the group consisting of acetic and itaconic acids.
Claim 8
Dependent Claim
24 words
A process according to claim 1 wherein said fiber is maintained in said atmosphere for a period of between about 1/2 to 120 minutes.
Claim 9
Dependent Claim
28 words
A process according to claim 1 including the step of establishing a temperature gradient along said fibers from about 220° C. to about 260° C. during said oxidation.
Claim 10
Dependent Claim
23 words
A process according to claim 1 wherein said drawing of the fibers is in excess of double the original length of said fibers.
Claim 11
Dependent Claim
28 words
A process according to claim 1 including the step of treating the fiber with said acid in a soaking bath before disposing said fibers within said oxygen-containing atmosphere.
Claim 12
Dependent Claim
24 words
A process according to claim 1 wherein said acid is incorporated in said fibers during or prior to the original formation of the latter.
Claim 13
Dependent Claim
208 words
A process of producing a carbonized fiber which, during oxidation, is drawn beyond the prior limit of elongation of about 95%, said process comprising the steps of: a. supplying an oxygen-containing atmosphere to a multizone gradient furnace; b. heating said furnace so as to maintain a temperature gradient in said atmosphere from about 220° C. at the inlet of said furnace to about 260° C. at the outlet thereof; c. permeating a multifilament tow of fibers formed of a polyacrylonitrile copolymer which contains about 85 mole percent acrylonitrile units and about 15 mole percent methyl acrylate, with sufficient carboxylic acid to permit subsequent drawing of said fibers during oxidation to at least double its original length; d. passing the multifilament permeated tow of fibers through said atmosphere along said temperature gradient in said furnace, with a residence time of between about 1/2 and 120 minutes; e. tensioning said multifilament permeated tow of fibers during passage through said atmosphere along said temperature gradient so as to draw the fibers to at least double its original length; and f. thereafter passing the multifilament tow through a second multizone gradient furnace with a temperature gradient of about 300° C. at the inlet thereof to about 800° C. at the outlet thereof.
Claim 14
Dependent Claim
208 words
A process of producing a carbonized fiber which, during oxidation, is drawn beyond the prior limit of elongation of about 95%, said process comprising the steps of: a. supplying an oxygen-containing atmosphere to a multizone gradient furnace; b. heating said furnace so as to maintain a temperature gradient in said atmosphere from about 220° C. at the inlet of said furnace to about 260° C. at the outlet thereof; c. permeating a multifilament tow of fibers formed of a polyacrylonitrile copolymer which contains about 85 mole percent acrylonitrile units and about 15 mole percent methyl acrylate, with sufficient carboxylic acid to permit subsequent drawing of said fibers during oxidation to at least double its original length; d. passing the multifilament permeated tow of fibers through said atmosphere along said temperature gradient in said furnace, with a residence time of between about 1/2 and 120 minutes; e. tensioning said multifilament permeated tow of fibers during passage through said atmosphere along said temperature gradient so as to draw the fibers to at least double its original length; and f. thereafter passing the multifilament tow through a second multizone gradient furnace with a temperature gradient of about 300° C. at the inlet thereof to about 800° C. at the outlet thereof.
Claim 15
Dependent Claim
37 words
A graphitized fiber produced from an oxidized polyacrylonitrile precursor fiber and having a tensile strength of approximately 51×10 4 psi, and a modulus of approximately 64×10 6 psi and a diameter of about 4.5 microns or less.
Claim 16
Dependent Claim
37 words
A graphitized fiber produced from an oxidized polyacrylonitrile precursor fiber and having a tensile strength of approximately 51×10 4 psi, and a modulus of approximately 64×10 6 psi and a diameter of about 4.5 microns or less.
Claim 17
Dependent Claim
78 words
A graphitized fiber produced from an oxidized polyacrylonitrile precursor fiber permeated with a carboxylic acid prior to oxidation, said fiber having been drawn under tension during oxidation to an elongation of more than double the original length of the fiber and to an average diameter of less than 10 microns, said graphitized fiber having a tensile strength of approximately 64×10 4 psi, a modulus of approximately 35×10 6 psi and a diameter of about 4.5 microns or less.
Claim 18
Dependent Claim
78 words
A graphitized fiber produced from an oxidized polyacrylonitrile precursor fiber permeated with a carboxylic acid prior to oxidation, said fiber having been drawn under tension during oxidation to an elongation of more than double the original length of the fiber and to an average diameter of less than 10 microns, said graphitized fiber having a tensile strength of approximately 64×10 4 psi, a modulus of approximately 35×10 6 psi and a diameter of about 4.5 microns or less.
References Cited (Backward Citations)
US3656904A
Cited
US4002426A
Cited
JPS49527A
Cited
DE2338357A1
Cited
US4073870A
Cited
US4113847A
Cited
US4100004A
Cited
US4347279A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |