Assignee: Forschungszentrum Jülich
•
Filing: 1984-03-29
•
Granted: 1985-07-02
•
Expires: 2004-03-29
Abstract
Abstract For joining molded parts having silicon carbide surfaces, the surfaces are first roughened to a depth of about 100-500 μm by removal of the free silicon either by vaporization or by etching when treating silicon containing silicon carbide layers containing at least 15% weight of excessive silicon. In the alternative, when no excessive silicon is present, the roughening can be done by laser shots pitting the surface. The pores provided by such a step are then loaded with carbon by (repeated) application of a cokable resin followed by coking, said resin can be soaked into the pores or attached as silicon containing resin wafer of cokable material. The surfaces to be joined are united and are heated, preferably at from 1600° to 1800° C. in the presence of silicon that is either made available at the edges of the joint as a liquid or else has been provided in the joint by a synthetic resin foil in which silicon powder is dispersed.
Inventors
- 👤 Ashok K. Gupta
- 👤 Erno Gyarmati
- 👤 Rudolf Munzer
- 👤 Aristides Naoumidis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:00
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/003; C04B37/005; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/573; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/08; C04B2237/083; C04B2237/086; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/365; C04B2237/50; C04B2237/60
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
74 words
Method of bonding together molded parts, composed of silicon carbide at least on and near their surfaces, at respective silicon carbide joining surfaces thereof, comprising roughening the surfaces to be joined up to a depth of at least 100 μm; loading the pores of the roughened zone by carbon coked in the pores and infiltrating liquid silicon into the joint converting the carbon to silicon carbide at a temperature between 1500° and 2000° C.
Claim 2
Dependent Claim
74 words
Method of bonding together molded parts, composed of silicon carbide at least on and near their surfaces, at respective silicon carbide joining surfaces thereof, comprising roughening the surfaces to be joined up to a depth of at least 100 μm; loading the pores of the roughened zone by carbon coked in the pores and infiltrating liquid silicon into the joint converting the carbon to silicon carbide at a temperature between 1500° and 2000° C.
Claim 3
Dependent Claim
33 words
A method according to claim 1 in which the step of roughening is performed by removing free silicon from a surface zone of reaction bonded silicon carbide containing at least 15% free silicon.
Claim 4
Dependent Claim
23 words
Method according to claim 2 in which the step of removing free silicon is performed by vaporizing off the silicon by prolonged heat.
Claim 5
Dependent Claim
25 words
Method according to claim 2 in which the step of removing free silicon is performed by leaching the surface layer with a silicon dissolving liquid.
Claim 6
Dependent Claim
29 words
Method according to claim 4, in which the leaching is performed with a hydrofluoric acid solution containing an oxidizer, followed by expelling liquid residues by washing, drying and heating.
Claim 7
Dependent Claim
22 words
Method according to claim 4 in which the leaching is performed by the etching with a solution of sodium or potassium hydroxide.
Claim 8
Dependent Claim
21 words
Method according to claim 1 in which the roughening is performed up to a depth of between 200 to 600 μm.
Claim 9
Dependent Claim
27 words
Method according to claim 1 in which molded parts of silicon carbide are bonded containing about 20% free silicon in and near the surfaces to be joined.
Claim 10
Dependent Claim
27 words
Method according to claim 1 in which the step of roughening is performed by means of laser shots producing pits distributed over the surface to be joined.
Claim 11
Dependent Claim
34 words
Method according to claim 9 in which said pits have a depth of about 500 μm and a diameter of about 200 μm and a spacing between the pits of 200 to 500 μm.
Claim 12
Dependent Claim
32 words
Method according to claim 1 in which the step of pore loading is done by impregnating the pores with a cokable material of low viscosity and coking said material in the pores.
Claim 13
Dependent Claim
14 words
Method according to claim 11 in which said impregnating and coking is repeatedly performed.
Claim 14
Dependent Claim
18 words
Method according to claim 12 in which said impregnating and coking is between two and four fold performed.
Claim 15
Dependent Claim
19 words
Method according to claim 11 in which a low viscosity solution of phenolformaldehyde resin is used for said impregnating.
Claim 16
Dependent Claim
32 words
Method according to claim 11 in which a catalytically polymerisable resin on the base of at least one member of the group comprising furfural and furfuryl alcohol is used for said impregnating.
Claim 17
Dependent Claim
64 words
Method according to claim 1 in which said steps of loading the pores by coked carbon and infiltrating liquid silicon are performed by inserting a synthetic resin wafer containing silicon dispersed therein between said joining surfaces putting said respective joining surfaces together to form a joint having said wafer held therein and heating the thus prepared joint carefully up to 1500° to 2000° C.
Claim 18
Dependent Claim
35 words
Method according to claim 16 in which said synthetic resin wafer has a thickness of 10 to 100 μm and contains 30 to 70 wt. % silicon powder of at most 1 μm grain size.
Claim 19
Dependent Claim
26 words
Method according to claim 17 in which said wafer has a thickness of 20 to 50 μm and contains about 50 percent by weight silicon powder.
Claim 20
Dependent Claim
14 words
Method according to claim 17 in which said wafer is formed with phenolformaldehyde resin.
Claim 21
Dependent Claim
41 words
Method according to claim 1 in which said infiltration of silicon and conversion to silicon carbide is performed by attaching a packing of silicon releasing powder to the edges of the joint and heating said assembly to 1500° to 2000° C.
Claim 22
Dependent Claim
23 words
Method according to claim 20 in which said silicon releasing powder is formed by a 1:1 powder mixture of silicon and silicon carbide.
Claim 23
Dependent Claim
21 words
Method according to claim 21 in which said powder has a grain size in the range of 200 to 400 μm.
Claim 24
Dependent Claim
19 words
Method according to claim 1 in which said converting to silicon carbide is performed at 1600° to 1800° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |