Method and article of manufacture for controlling slag carry-over during tapping of a heat in steelmaking
Assignee: Individual
•
Filing: 1983-12-13
•
Granted: 1985-07-02
•
Expires: 2003-12-13
Abstract
Abstract A steelmaking process and an article of manufacture for use therein, comprising the addition to the steelmaking vessel or caster tundish prior to the tapping of the finished steel of a heat-stable material having a density such that said material floats substantially at the interface between the slag and steel, said material being in the physical form of at least one annular disc. The heat-stable material may also be added to the vessel in the physical form of at least one discrete piece in addition to the annular disc.
Inventors
- 👤 John W. Schwer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:48
CPC Classifications
B; B22; B22D; B22D43/00; B22D43/001; B22D43/002
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
106 words
In a steelmaking process in which a layer of liquid slag is formed on the liquid steel in the steelmaking vessel during said process, whereafter at the completion of the heat said liquid steel is removed from said vessel through a side taphole, the improvement comprising the addition to said vessel prior to tapping of a spatially unconstrained, heat-stable material having a density such that said material floats substantially at the interface between said slag and said steel and effects unrestricted spatial movement with respect to said interface and said taphole during tapping, said material being in the physical form of at least one annular disc.
Claim 2
Dependent Claim
106 words
In a steelmaking process in which a layer of liquid slag is formed on the liquid steel in the steelmaking vessel during said process, whereafter at the completion of the heat said liquid steel is removed from said vessel through a side taphole, the improvement comprising the addition to said vessel prior to tapping of a spatially unconstrained, heat-stable material having a density such that said material floats substantially at the interface between said slag and said steel and effects unrestricted spatial movement with respect to said interface and said taphole during tapping, said material being in the physical form of at least one annular disc.
Claim 3
Dependent Claim
16 words
The process of claim 1 wherein the surface of said annular disc is toroidal in shape.
Claim 4
Dependent Claim
26 words
The process of claim 1 wherein said steelmaking process comprises a basic oxygen steelmaking process, an electric furnace process, or a process utilizing a caster tundish.
Claim 5
Dependent Claim
28 words
The process of claims 1, 2 or 3 wherein there is further added to said vessel at least one additional discrete piece of heat-stable material prior to tapping.
Claim 6
Dependent Claim
15 words
The process of claim 4 wherein said additional discrete piece is substantially spherical in shape.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-07-01 | 1988-12-31 | 1989-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-07-01 | 1992-12-31 | 1993-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-07-01 | 1996-12-31 | 1997-07-02 | $7700.00 | Window Closed / Lapsed |