Patterning method for reducing hillock density in thin metal films and a structure produced thereby
Assignee: Eastman Kodak Co
•
Filing: 1982-03-03
•
Granted: 1985-06-25
•
Expires: 2002-03-03
Abstract
Abstract Hillock formation in a thin film of metal having a high coefficient of thermal expansion on a substrate having a low coefficient of thermal expansion is reduced by patterning the substrate in an area normally free from such pattern, specifically for the purpose of reducing hillocks, prior to formation of the thin metal film, with a bas-relief pattern of lands and valleys, having a depth dimension on the same order of magnitude as the thickness of the film.
Inventors
- 👤 David L. Losee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:43
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/40; H10W20/41; H10W20/435; Y; Y10; Y10S; Y10S438/00; Y10S438/937
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
115 words
A method of reducing hillock density in a thin film of metal having a high coefficient of thermal expansion on a substrate having a low coefficient of thermal expansion, comprising the steps of: forming for the purpose of reducing hillocks, a bas-relief pattern of lands and valleys, in an area of the substrate normally free from such pattern; forming on said pattern a thin film of metal having a high coefficient of thermal expansion, the height and depth dimensions of said lands and valleys being of the same order of magnitude as the thickness of said metal film, whereby stress relief is provided by said bas-relief pattern thereby reducing hillock formation in said metal film.
Claim 2
Independent Claim
115 words
A method of reducing hillock density in a thin film of metal having a high coefficient of thermal expansion on a substrate having a low coefficient of thermal expansion, comprising the steps of: forming for the purpose of reducing hillocks, a bas-relief pattern of lands and valleys, in an area of the substrate normally free from such pattern; forming on said pattern a thin film of metal having a high coefficient of thermal expansion, the height and depth dimensions of said lands and valleys being of the same order of magnitude as the thickness of said metal film, whereby stress relief is provided by said bas-relief pattern thereby reducing hillock formation in said metal film.
Claim 3
Dependent Claim
20 words
The invention claimed in claim 1, wherein said substrate is silicon and silicon dioxide, and wherein said metal is aluminum.
Claim 4
Dependent Claim
38 words
The invention claimed in claim 2, wherein said aluminum is approximately 1 μm thick, wherein said lands and valleys form a checkerboard pattern, said valleys being approximately 1 μm deep and said pattern being approximately 5 μm×5 μm.
Claim 5
Dependent Claim
118 words
A thin film structure comprising: a substrate having a low coefficient of thermal expansion, a portion of said substrate defining a bas-relief pattern of lands and valleys, in an area normally free from such pattern, for the purpose of reducing hillock density in a film of metal overlying said portion of said substrate; and a thin film of metal over said pattern on said portion of said substrate, having a high coefficient of thermal expansion, the height and depth dimensions of said pattern of lands and valleys being of the same order of magnitude as the thickness of said metal film, whereby stress relief is provided by said bas-relief pattern, thereby reducing hillock formation in said metal film.
Claim 6
Dependent Claim
118 words
A thin film structure comprising: a substrate having a low coefficient of thermal expansion, a portion of said substrate defining a bas-relief pattern of lands and valleys, in an area normally free from such pattern, for the purpose of reducing hillock density in a film of metal overlying said portion of said substrate; and a thin film of metal over said pattern on said portion of said substrate, having a high coefficient of thermal expansion, the height and depth dimensions of said pattern of lands and valleys being of the same order of magnitude as the thickness of said metal film, whereby stress relief is provided by said bas-relief pattern, thereby reducing hillock formation in said metal film.
Claim 7
Dependent Claim
20 words
The invention claimed in claim 4, wherein said substrate is silicon and silicon dioxide, and wherein said metal is aluminum.
Claim 8
Dependent Claim
40 words
The invention claimed in claim 5, wherein said aluminium is approximately 1 μm thick, wherein said bas-relief pattern is a checkerboard pattern, said valleys being approximately 1 μm deep and the squares of said checkerboard being approximately 5 μm square.
Claim 9
Independent Claim
85 words
A method of reducing hillock density in a thin film of metal having a high coefficient of thermal expansion on a substrate having a low coefficient of thermal expansion, comprising the steps of: forming a bas-relief pattern of lands and valleys on said substrate, in an area normally free from such pattern, for the purpose of reducing hillock density, the dimensions of said bas-relief pattern being of size and depth sufficient to reduce hillock density in an overlying film of metal to an acceptable level;
Claim 10
Independent Claim
85 words
A method of reducing hillock density in a thin film of metal having a high coefficient of thermal expansion on a substrate having a low coefficient of thermal expansion, comprising the steps of: forming a bas-relief pattern of lands and valleys on said substrate, in an area normally free from such pattern, for the purpose of reducing hillock density, the dimensions of said bas-relief pattern being of size and depth sufficient to reduce hillock density in an overlying film of metal to an acceptable level;
Claim 11
Dependent Claim
10 words
forming a thin film of metal over said bas-relief pattern.
Claim 12
Dependent Claim
10 words
forming a thin film of metal over said bas-relief pattern.
Claim 13
Dependent Claim
47 words
The invention claimed in claim 1, wherein said substrate is silicon dioxide, and said bas-relief pattern is formed by: depositing a layer of polysilicon on said substrate; patterning said layer of polysilicon; and oxidizing said patterned layer of polysilicon to form a patterned layer of silicon dioxide.
References Cited (Backward Citations)
GB1234544A
Cited
US4012756A
Cited
US3986897A
Cited
US4307131A
Cited
US4178396A
Cited
US4291068A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |