Ferroelectric photomechanical actuators
Assignee: United States Department of the Army
•
Filing: 1984-05-07
•
Granted: 1985-06-18
•
Expires: 2004-05-07
Abstract
Abstract A method for deforming materials which are ferroelectric, have remanent polarization, and which exhibit a length-dependent photoelectric effect. One type of material is photovoltaic, piezoelectric, ferroelectric ceramics. Illuminating such materials causes them to deform, either in length or in thickness, depending on the direction of the remanent polarization. A single plate of such material may be used, or a pair of plates bonded together may be used.
Inventors
- 👤 Philip S. Brody
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:52
CPC Classifications
H; H10; H10F; H10F10/00; H10N; H10N30/00; H10N30/80; H10N30/85; H10N30/853; G; G02; G02B; G02B6/00; G02B6/24; G02B6/26; G02B6/35; G02B6/351; G02B6/3512; G02B6/3564; G02B6/3568; G02B6/3578; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
35 words
A method for deforming materials which are ferroelectric, have remanent polarization, and which exhibit a length-dependent photoelectric effect, comprising the step of illuminating a plate of said material to cause the deformation of said plate.
Claim 2
Independent Claim
35 words
A method for deforming materials which are ferroelectric, have remanent polarization, and which exhibit a length-dependent photoelectric effect, comprising the step of illuminating a plate of said material to cause the deformation of said plate.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein said plate has an axis and first and second opposite planar faces extending between opposite top and bottom tips to form a rectangular polyhedron.
Claim 4
Dependent Claim
42 words
The method of claim 2 wherein the direction of the remanent polarization of said plate is from said bottom tip to said top tip, such that said plate expands along said axis and said tips bend away from the source of illumination.
Claim 5
Dependent Claim
32 words
The method of claim 2 wherein the direction of the direction of the remanent polarization of said plate is normal to said axis, such that said plate expands normal to said axis.
Claim 6
Dependent Claim
24 words
The method of claim 4 wherein the wavelength of the illumination is such that it will be transmitted through the thickness of said plate.
Claim 7
Dependent Claim
13 words
The method of claim 1 wherein said materials comprise photovoltaic, piezoelectric, ferroelectric ceramics.
Claim 8
Dependent Claim
76 words
The method of claim 6 wherein said ceramic is a solid solution of lead titanate and lead zirconate having the compositional formula Pb(Zr 0 .53 Ti 0 .47)O 3 to which is added 1% by weight of niobium oxide, or said ceramic is a solid solution of lead titanate with 5% by weight of magnesium oxide and 5% by weight of tungsten oxide having the compositional formula 0.9PbTiO 3 -0.1Pb(Mg 1/2 W 1/2 )O 3 .
Claim 9
Independent Claim
53 words
A method for deforming materials which are ferroelectric, have remanent polarization, and which exhibit a length-dependent photoelectric effect, comprising the steps of: a. bonding a first plate of said material to a second plate of said material; and b. illuminating at least one of said plates to cause the deformation of the plates.
Claim 10
Independent Claim
53 words
A method for deforming materials which are ferroelectric, have remanent polarization, and which exhibit a length-dependent photoelectric effect, comprising the steps of: a. bonding a first plate of said material to a second plate of said material; and b. illuminating at least one of said plates to cause the deformation of the plates.
Claim 11
Dependent Claim
30 words
The method of claim 8 wherein said plates each have an axis and first and second opposite planar faces extending between the opposite top and bottom tips forming rectangular polyhedrons.
Claim 12
Dependent Claim
76 words
The method of claim 9 wherein the direction of the remanent polarization of said first plate is from said bottom tip to said top tip, and the direction of the remanent polarization of said second plate is from said top tip to said bottom tip, such that the illuminated plate expands along the axis and the length of the other plate decreases along the axis, and the tips bend away from the source of the illumination.
Claim 13
Dependent Claim
53 words
The method of claim 10 further comprising the steps of: a. attaching first electrode means to the top tips of said plates for electrically connecting the top tips to each other; and b. attaching second electrode means to the bottom tips of said plates for electrically connecting the bottom tips to each other.
Claim 14
Dependent Claim
26 words
The method of claim 9 wherein the direction of the remanent polarization of said plates is the same and normal to said axis of each plate.
Claim 15
Dependent Claim
110 words
The method of claim 12 further comprising the steps of: a. attaching a first transparent electrode to one face of the pair of bonded plates; b. attaching a second electrode to the other face of the pair of bonded plates; c. electrically connecting said transparent electrode to said second electrode; d. attaching third electrode means to the bottom tips of said plates for electrically connecting the bottom tips to each other; and e. illuminating said transparent electrode so as to cause the illuminated plate to decrease in length along its axis, the other plate increases in length along its axis, and said tips to bend toward the source of illumination.
Claim 16
Dependent Claim
13 words
The method of claim 8 wherein said materials comprise photovoltaic, piezoelectric, ferroelectric ceramics.
Claim 17
Dependent Claim
76 words
The method of claim 14 wherein said ceramic is a solid solution of lead titanate and lead zirconate having the compositional formula Pb(Zr 0 .53 Ti 0 .47)O 3 to which is added 1% by weight of niobium oxide, or said ceramic is a solid solution of lead titanate with 5% by weight of magnesium oxide and 5% of weight of tungsten oxide having the compositional formula 0.9PbTiO 3 -0.1Pb(Mg 1/2 W 1/2 )O 3 .
Claim 18
Independent Claim
254 words
A method comprising the steps of: a. attaching a plurality of parallel strip electrodes to the first planar face of a plate of ferroelectric material which exhibits a length-dependent photoelectric effect; b. attaching a plurality of parallel strip electrodes to the second planar face of said plate, said second face being parallel to said first face; c. said plate has opposite top and bottom tips a specified distance apart which define an axis and between which extend said first and second planar faces to form a rectangular polyhedron; d. said electrodes are normal to said axis, extend across the width of the plate, and are evenly separated from each other along the length of the plate; e. applying a positive tangential poling field to the electrodes of the first face of the plate such that the poling field penetrates approximately one half of the thickness of the plate and causing a remanent polarization in said plate along said axis from said bottom tip to said top tip; f. applying a negative tangential poling field to the electrodes of the second face of the plate such that the poling field penetrates approximately one half of the thickness of the plate and causing a remanent polarization in said plate along said axis from said top tip to said bottom tip; g. removing both the positive tangential poling field and the negative tangential poling field, and h. illuminating said plate such that it expands along said axis and said tips bend away from the source of light.
Claim 19
Independent Claim
254 words
A method comprising the steps of: a. attaching a plurality of parallel strip electrodes to the first planar face of a plate of ferroelectric material which exhibits a length-dependent photoelectric effect; b. attaching a plurality of parallel strip electrodes to the second planar face of said plate, said second face being parallel to said first face; c. said plate has opposite top and bottom tips a specified distance apart which define an axis and between which extend said first and second planar faces to form a rectangular polyhedron; d. said electrodes are normal to said axis, extend across the width of the plate, and are evenly separated from each other along the length of the plate; e. applying a positive tangential poling field to the electrodes of the first face of the plate such that the poling field penetrates approximately one half of the thickness of the plate and causing a remanent polarization in said plate along said axis from said bottom tip to said top tip; f. applying a negative tangential poling field to the electrodes of the second face of the plate such that the poling field penetrates approximately one half of the thickness of the plate and causing a remanent polarization in said plate along said axis from said top tip to said bottom tip; g. removing both the positive tangential poling field and the negative tangential poling field, and h. illuminating said plate such that it expands along said axis and said tips bend away from the source of light.
Claim 20
Dependent Claim
49 words
The method of claim 16 further comprising the steps of: a. removing the strip electrodes from the first and second faces of said plate; b. attaching a first electrode to the top tip of said plate; and c. attaching a second electrode to the bottom tip of said plate.
Claim 21
Dependent Claim
31 words
The method of claim 16 wherein the wavelength of the illumination is such that it will not be transmitted through more than approximately one half of the thickness of said plate.
Claim 22
Dependent Claim
13 words
The method of claim 16 wherein said ferroelectric materials comprise photovoltaic, piezoelectric ceramics.
Claim 23
Dependent Claim
76 words
The method of claim 19 wherein said ceramic is a solid solution of lead titanate and lead zirconate having the compositional formula Pb(Zr 0 .53 Ti 0 .47)O 3 to which is added 1% by weight of niobium oxide, or said ceramic is a solid solution of lead titanate with 5% by weight of magnesium oxide and 5% by weight of tungsten oxide having the compositional formula 0.9PbTiO 3 -0.1Pb(Mg 1/2 W 1/2 )O 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-17 | 1988-12-17 | 1989-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-17 | 1992-12-17 | 1993-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-17 | 1996-12-17 | 1997-06-18 | $7700.00 | Window Closed / Lapsed |