Toughened thermoset laminates
Assignee: Honeywell International Inc
•
Filing: 1984-03-20
•
Granted: 1985-06-18
•
Expires: 2004-03-20
Abstract
Abstract Disclosed is a water-based thermosetting epoxy composition of a water compatible epoxy resin, about 5 to about 35%, based on a total solids, of a water compatible impact modifier, about 1.5 to about 7%, based on the weight of the epoxy resin, of a water compatible epoxy hardener, up to about 0.3%, based on the weight of the epoxy resin, of a catalyst, and sufficient water to provide a viscosity of about 100 to about 500 centipoises. The impact modifier is a copolymer of about 10 to about 60% ethylene, propylene, or mixtures thereof, and about 40 to about 90% vinyl acetate, vinyl chloride, or mixtures thereof. Also disclosed are laminates prepared from this composition and a method of preparing them.
Inventors
- 👤 Joseph R. Marchetti
- 👤 Zal N. Sanjana
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 08:28
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B27/00; B32B27/04; B32B37/00; B32B37/06; C; C08; C08J; C08J3/00; C08J3/12; C08J3/122; C08L; C08L63/00; B32B2250/00; B32B2250/20; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/023; B32B2260/04; B32B2260/046; C08J2363/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T442/00; Y10T442/20; Y10T442/2861
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
150 words
A composition comprising: (A) a water emulsifiable thermosettable epoxy resin; (B) an effective amount of a water compatible epoxy hardener; (C) an effective amount of a water compatible catalyst for said epoxy resin; (D) about 5 to about 35%, based on total resin solids, of a water compatible terpolymer polymerized from about 10 to about 60% of an ethylenic monomer selected from the group consisting of ethylene, propylene, and mixtures thereof, and about 40 to about 90% of a vinylic monomer selected from the group consisting of vinyl acetate, vinyl chloride, and mixtures thereof, and an acrylic monomer selected from the group consisting of acrylamide, acrylic acid, methacrylic acid, and mixtures thereof, where the amount of said acrylic monomer is sufficient to give an acid number of about 1 to about 60; and (E) sufficient water to produce a viscosity of about 100 to about 100 to about 400 centipoises.
Claim 2
Dependent Claim
150 words
A composition comprising: (A) a water emulsifiable thermosettable epoxy resin; (B) an effective amount of a water compatible epoxy hardener; (C) an effective amount of a water compatible catalyst for said epoxy resin; (D) about 5 to about 35%, based on total resin solids, of a water compatible terpolymer polymerized from about 10 to about 60% of an ethylenic monomer selected from the group consisting of ethylene, propylene, and mixtures thereof, and about 40 to about 90% of a vinylic monomer selected from the group consisting of vinyl acetate, vinyl chloride, and mixtures thereof, and an acrylic monomer selected from the group consisting of acrylamide, acrylic acid, methacrylic acid, and mixtures thereof, where the amount of said acrylic monomer is sufficient to give an acid number of about 1 to about 60; and (E) sufficient water to produce a viscosity of about 100 to about 100 to about 400 centipoises.
Claim 3
Dependent Claim
18 words
A composition according to claim 1 wherein epoxy resin has a pH of about 6 to about 8.
Claim 4
Dependent Claim
12 words
A composition according to claim 1 wherein said epoxy hardener is dicyandiamide.
Claim 5
Dependent Claim
12 words
A composition according to claim 1 wherein said catalyst is 2-methyl imidazole.
Claim 6
Dependent Claim
24 words
A composition according to claim 1 wherein said acrylic monomer is selected from the group consisting of acrylic acid, methacrylic acid, and mixtures thereof.
Claim 7
Dependent Claim
12 words
A composition according to claim 1 wherein said ethylenic monomer is ethylene.
Claim 8
Dependent Claim
13 words
An article comprising a substrate impregnated with a composition according to claim 1.
Claim 9
Dependent Claim
15 words
An article according to claim 7 wherein said substrate is a sheet of fibrous material.
Claim 10
Dependent Claim
14 words
An article according to claim 8 wherein said composition has been B-staged after impregnation.
Claim 11
Dependent Claim
21 words
A laminate comprising a stack of said articles according to claim 9, the compositions of which have been C-staged after stacking.
Claim 12
Dependent Claim
11 words
A powder comprising a spray dried composition according to claim 1.
Claim 13
Dependent Claim
54 words
A method of making a laminate comprising: (A) impregnating sheets of a fibrous material with a composition according to claim 1; (B) heating said sheets to coacervate or coagulate said composition, evaporate said water, and B-stage said composition; (C) stacking said sheets; and (D) heating and pressing said stacked sheets to C-stage said composition.
Claim 14
Dependent Claim
39 words
A composition according to claim 1 wherein the amount of said hardener is about 1.5 to about 7%, based on epoxy resin weight, and the amount of said catalyst is up to about 0.3%, based on epoxy resin weight.
Claim 15
Dependent Claim
19 words
A composition according to claim 1 wherein said epoxy resin has an E.E.W. of about 100 to about 1000.
Claim 16
Dependent Claim
165 words
A composition comprising (A) a water emulsifiable thermosettable epoxy resin having an E.E.W. of about 100 to about 1000, and a pH of about 6 to about 8; (B) about 1.5 to about 7%, based on said epoxy resin weight, of a water compatible epoxy hardener; (C) up to about 0.3%, based on said epoxy resin weight, of a water compatible catalyst for said epoxy resin; (D) about 5 to about 35%, based on total resin solids, of a water compatible terpolymer polymerized from about 10 to about 60% ethylene, about 40 to about 90% of a vinylic monomer selected from the groups consisting of vinyl acetate, vinyl chloride, and mixtures thereof, and an acrylic monomer selected from the group consisting of acrylamide, acrylic acid, methacrylic acid, and mixtures thereof, where the amount of said acrylic monomer is sufficient to give an acid number of about 1 to about 60; and (E) sufficient water to produce a viscosity of about 100 to about 400 centipoises.
Claim 17
Dependent Claim
165 words
A composition comprising (A) a water emulsifiable thermosettable epoxy resin having an E.E.W. of about 100 to about 1000, and a pH of about 6 to about 8; (B) about 1.5 to about 7%, based on said epoxy resin weight, of a water compatible epoxy hardener; (C) up to about 0.3%, based on said epoxy resin weight, of a water compatible catalyst for said epoxy resin; (D) about 5 to about 35%, based on total resin solids, of a water compatible terpolymer polymerized from about 10 to about 60% ethylene, about 40 to about 90% of a vinylic monomer selected from the groups consisting of vinyl acetate, vinyl chloride, and mixtures thereof, and an acrylic monomer selected from the group consisting of acrylamide, acrylic acid, methacrylic acid, and mixtures thereof, where the amount of said acrylic monomer is sufficient to give an acid number of about 1 to about 60; and (E) sufficient water to produce a viscosity of about 100 to about 400 centipoises.
Claim 18
Dependent Claim
22 words
A composition according to claim 15 wherein said water compatible epoxy hardener is dicyandiamide, and said water compatible catalyst is 2-methyl imidazole.
References Cited (Backward Citations)
GB949460A
Cited
US3641195A
Cited
US3806483A
Cited
US3905931A
Cited
US3941857A
Cited
US4009224A
Cited
US4222918A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-17 | 1988-12-17 | 1989-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-17 | 1992-12-17 | 1993-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-17 | 1996-12-17 | 1997-06-18 | $7700.00 | Window Closed / Lapsed |