Process for manufacture of tamper-resistant polyester credit cards
Assignee: Mitsubishi Chemical America Inc
•
Filing: 1983-04-04
•
Granted: 1985-06-11
•
Expires: 2003-04-04
Abstract
Abstract The present invention relates to a credit card or identification card fabricated from amorphous polyester sheet material wherein at least the area of said card containing embossed numerical or letter characters and the characters themselves are composed of substantially crystalline polyester. Such characters can not readily be altered by either heat treatment or by shaving them off.
Inventors
- 👤 R. Scott Caines
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:00
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/36; B32B27/06; B32B27/08; B32B27/18; B32B27/20; B32B37/00; B32B37/08; B32B38/00; B32B38/04; B32B38/06; B32B7/00; B32B7/04; B32B7/12; B42; B42D; B42D25/00; B42D25/20; B42D25/23; B42D25/40; B42D25/405; B42D25/425; B42D25/45; B42D25/455; B42D25/46; B42D25/465; B42D25/47; B32B2307/00; B32B2307/40; B32B2307/402; B32B2307/4026; B32B2307/41; B32B2307/50; B32B2307/514; B32B2307/518; B32B2307/70; B32B2307/702; B32B2307/704; B32B2309/00; B32B2309/02; B32B2309/08; B32B2309/10; B32B2309/105; B32B2367/00; B32B2425/00; B42D2033/08; B42D2033/14; B42D2033/20; B42D2033/30; B42D2035/08; B42D25/30; B42D25/324; Y; Y10; Y10S; Y10S283/00; Y10S283/904; Y10S428/00; Y10S428/916; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1039; Y10T156/1041; Y10T156/1043; Y10T156/1044; Y10T156/1052; Y10T156/1084
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
74 words
A method of preparing a credit or identification card comprising: (a) providing a supply of substantially amorphous polyester sheet material; (b) embossing a surface of said sheet material under pressure with numerical and/or letter characters; (c) holding said sheet material under restraint while heating said sheet material to a temperature and for a time sufficient to substantially crystallize at least the embossed portion of said amorphous polyester sheet; and (d) cooling said sheet material.
Claim 2
Independent Claim
74 words
A method of preparing a credit or identification card comprising: (a) providing a supply of substantially amorphous polyester sheet material; (b) embossing a surface of said sheet material under pressure with numerical and/or letter characters; (c) holding said sheet material under restraint while heating said sheet material to a temperature and for a time sufficient to substantially crystallize at least the embossed portion of said amorphous polyester sheet; and (d) cooling said sheet material.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein said amorphous polyester is polyethylene terephthalate.
Claim 4
Dependent Claim
21 words
The method of claim 2 wherein said heating temperature is within the range of about 90° C. to about 240° C.
Claim 5
Dependent Claim
20 words
The method of claim 3 wherein said sheet has a thickness within the range of about 5 to 40 mils.
Claim 6
Dependent Claim
27 words
The method of claim 4 wherein said sheet material is cut into a size suitable for use as a credit card before or after said embossing step.
Claim 7
Dependent Claim
15 words
The method of claim 5 wherein said sheet material contains an opaque filler or colorant.
Claim 8
Independent Claim
115 words
A method of preparing a credit or identification card comprising: (a) providing a supply of substantially amorphous polyester sheet material; (b) providing a supply of overlay film; (c) laminating said overlay film to one or both sides of said sheet material under heat and pressure insufficient to substantially crystallize said amorphous polyester sheet to provide a composite sheet; (d) embossing a portion of a surface of said composite sheet under pressure with numerical and/or letter characters; (e) holding said composite sheet under restraint while heating said composite sheet to a temperature and for a time sufficient to substantially crystallize at least the embossed portion of said amorphous polyester sheet; and (f) cooling said sheet material.
Claim 9
Independent Claim
115 words
A method of preparing a credit or identification card comprising: (a) providing a supply of substantially amorphous polyester sheet material; (b) providing a supply of overlay film; (c) laminating said overlay film to one or both sides of said sheet material under heat and pressure insufficient to substantially crystallize said amorphous polyester sheet to provide a composite sheet; (d) embossing a portion of a surface of said composite sheet under pressure with numerical and/or letter characters; (e) holding said composite sheet under restraint while heating said composite sheet to a temperature and for a time sufficient to substantially crystallize at least the embossed portion of said amorphous polyester sheet; and (f) cooling said sheet material.
Claim 10
Dependent Claim
14 words
The method of claim 6 wherein said polyester sheet material is amorphous polyethylene terephthalate.
Claim 11
Dependent Claim
14 words
The method of claim 7 wherein said overlay film is biaxially oriented polyethylene terephthalate.
Claim 12
Dependent Claim
24 words
The method of claim 9 including the step of interposing an adhesive layer between said amorphous sheet and said overlay film prior to lamination.
Claim 13
Dependent Claim
26 words
The method of claim 10 wherein said adhesive layer comprises a water dispersible copolyester having at least one free functional acid group in the polymer chain.
Claim 14
Dependent Claim
21 words
The method of claim 11 wherein said crystallizing temperature is within the range of about 90° C. to about 240° C.
Claim 15
Dependent Claim
13 words
The method of claim 12 wherein said crystallizing temperature is about 125° C.
Claim 16
Dependent Claim
29 words
The method of claim 9 including the step of cutting said composite sheet material into a size suitable for use as credit card before or after said embossing step.
Claim 17
Dependent Claim
39 words
The method of claim 14 wherein said amorphous sheet material has a thickness in the range of about 5 to 40 mils, and said overlay film has a thickness in the range of about 0.25 to about 2 mils.
References Cited (Backward Citations)
GB1078813A
Cited
US3313052A
Cited
US3880706A
Cited
US4455484A
Cited
US4098940A
Cited
US4252885A
Cited
US4304851A
Cited
US4133926A
Cited
US4325196A
Cited
US4214035A
Cited
US4455039A
Cited
US4389472A
Cited
US4343851A
Cited
US4451068A
Cited
US4456639A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-10 | 1988-12-10 | 1989-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-10 | 1992-12-10 | 1993-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-10 | 1996-12-10 | 1997-06-11 | $7700.00 | Window Closed / Lapsed |