Antistatic coated polyester film
Assignee: CNA Holdings LLC
•
Filing: 1979-01-31
•
Granted: 1980-07-22
•
Expires: 1999-01-31
Abstract
Abstract A polyester film coated with an antistatic coating is provided. The film includes a polyester film support coated on one side with a latex coating. The coating includes stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate present in a concentration in the range of between about 2.75 percent and 3.25 percent by weight, based on the total weight of the latex coating. The coating further includes a crosslinkable methylmethacrylate-ethylacrylate-methacrylamide terpolymer having a glass transition temperature in the range of between about 40° C. and 50° C. The terpolymer is present in a concentration in the range of between about 0.75 percent and 1.25 percent by weight, based on the total weight of the latex coating. The weight ratio of the nitrate to the terpolymer ranges between about 2.75:1 to below 3:1. A process for forming the above film is also disclosed. In this process a latex coating of the composition described above is coated onto a uniaxially drawn polyester film support. The uniaxially drawn film is then heated to drive off the water and thereafter the uniaxially coated film is stretched in a direction normal to that of the uniaxial drawn film.
Inventors
- 👤 John M. Heberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:01
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/044; C08J7/046; C08J2367/00; C08J2367/02; C08J2433/00; Y; Y10; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/31504; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
116 words
A biaxially oriented polyester film comprising a polyester film support coated on one side with a latex coating, said coating including: stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate, present in a concentration in the range of between 2.75% and 3.25% by weight, based on the total weight of the latex coating; and a crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer, having a glass transition temperature in the range of between about 40° C. and 50° C., present in a concentration in the range of between about 0.75% and 1.25% by weight based on the total weight of the latex coating wherein the weight ratio of said stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate to said crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer is in the range of between about 2.75:1 and 3.25:1.
Claim 2
Dependent Claim
116 words
A biaxially oriented polyester film comprising a polyester film support coated on one side with a latex coating, said coating including: stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate, present in a concentration in the range of between 2.75% and 3.25% by weight, based on the total weight of the latex coating; and a crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer, having a glass transition temperature in the range of between about 40° C. and 50° C., present in a concentration in the range of between about 0.75% and 1.25% by weight based on the total weight of the latex coating wherein the weight ratio of said stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate to said crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer is in the range of between about 2.75:1 and 3.25:1.
Claim 3
Dependent Claim
36 words
A biaxially oriented polyester film in accordance with claim 1 wherein the total dry coating weight of said coating on said polyester film is at least 0.003 pound per 1000 square feet of biaxially oriented film.
Claim 4
Dependent Claim
33 words
A polyester film in accordance with claim 2 wherein said total dry coating weight is in the range of between about 0.003 and 0.007 pound per 1000 square feet of biaxially stretched film.
Claim 5
Dependent Claim
31 words
A film in accordance with claim 1 wherein the weight ratio of said stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate to said crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer is in the range of between about 2.75:1 and 3.0:1.
Claim 6
Dependent Claim
13 words
A film in accordance with claim 1 wherein said polyester is polyethylene terephthalate.
Claim 7
Dependent Claim
40 words
A film in accordance with claim 1 wherein said stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate is present in said latex coating in a concentration in the range of between about 2.9% and 3.1% by weight, based on the total weight of said latex coating.
Claim 8
Dependent Claim
38 words
A film in accordance with claim 6 wherein said stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate is present in said latex coating in a concentration in the range of between about 3.0% by weight, based on the total weight of said latex coating.
Claim 9
Dependent Claim
42 words
A film in accordance with claim 1 wherein said crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer is present in said latex coating in a concentration in the range of between about 0.9% and 1.1% by weight based on the total weight of said latex coating.
Claim 10
Dependent Claim
39 words
A film in accordance with claim 8 wherein said crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer is present in said latex coating in a concentration in the range of about 1.0% by weight, based on the total weight of said latex coating.
Claim 11
Dependent Claim
25 words
A film in accordance with claim 1 wherein said crosslinkable methylmethacrylate-ethylacrylate-methacrylamide terpolymer has a glass transition temperature of between about 43° C. and 47° C.
Claim 12
Dependent Claim
20 words
A film in accordance with claim 10 wherein said crosslinkable methylmethacrylate-ethylacrylate-methacrylamide terpolymer has a glass transition temperature of 45° C.
Claim 13
Dependent Claim
67 words
A film in accordance with claim 1 wherein opposite said latex coating is coated with a second latex coating, said second latex coating comprising a crosslinkable methylmethacrylate-ethylacrylate-methacrylamide terpolymer having a glass transition temperature in the range of between about 40° C. and 50° C., and present in a concentration of between about 3.0% and 4.0% by weight, based on the total weight of said second latex coating.
Claim 14
Dependent Claim
168 words
A process for forming an antistatic biaxially oriented polyester film comprising the steps of: applying a latex coating, said coating comprising stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate, present in a concentration in the range of between about 2.75% and 3.25% by weight, based on the total weight of said latex coating, and a crosslinkable methylmethacrylate-ethylacrylate-methacrylamide terpolymer having a glass transition temperature in the range of between about 40° C. and 50° C. and present in a concentration in the range of between about 0.75% and 1.25% by weight based on the total weight of the latex coating wherein the weight ratio of said nitrate to said terpolymer is in the range of between about 2.75:1 and 3.25:1, to a uniaxially drawn polyester film; heating said coated, uniaxially drawn film at a temperature in the range of between about 90° C. and 110° C. wherein said coating is dried; stretching said coated uniaxially drawn film in a direction normal to the direction of the uniaxially drawn film wherein biaxially drawn film is produced.
Claim 15
Dependent Claim
168 words
A process for forming an antistatic biaxially oriented polyester film comprising the steps of: applying a latex coating, said coating comprising stearamidopropyldimethyl-β-hydroxy-ethylammonium nitrate, present in a concentration in the range of between about 2.75% and 3.25% by weight, based on the total weight of said latex coating, and a crosslinkable methylmethacrylate-ethylacrylate-methacrylamide terpolymer having a glass transition temperature in the range of between about 40° C. and 50° C. and present in a concentration in the range of between about 0.75% and 1.25% by weight based on the total weight of the latex coating wherein the weight ratio of said nitrate to said terpolymer is in the range of between about 2.75:1 and 3.25:1, to a uniaxially drawn polyester film; heating said coated, uniaxially drawn film at a temperature in the range of between about 90° C. and 110° C. wherein said coating is dried; stretching said coated uniaxially drawn film in a direction normal to the direction of the uniaxially drawn film wherein biaxially drawn film is produced.
Claim 16
Dependent Claim
13 words
A process in accordance with claim 13 wherein said polyester is polyethylene terephthalate.
Claim 17
Dependent Claim
29 words
A process in accordance with claim 14 wherein said biaxially drawn film is heat set at a temperature in the range of between about 190° C. and 240° C.
Claim 18
Dependent Claim
20 words
A process in accordance with claim 13 wherein said coating of said uniaxially drawn film is applied by roller coating.
Claim 19
Dependent Claim
18 words
A process in accordance with claim 16 wherein said uniaxially drawn film is applied by reverse gravure coating.
Claim 20
Dependent Claim
21 words
A process in accordance with claim 13 wherein said uniaxially drawn film coated with said latex coating is longitudinally drawn film.
Claim 21
Dependent Claim
79 words
A process in accordance with claim 13 wherein said uniaxially drawn film is coated with a second coating on the side opposite said first coated side, said second coating comprising a latex coating including a crosslinkable methylmethacrylate-ethyl acrylate-methacrylamide terpolymer having a glass transition temperature in the range of between about 40° C. and 50° C., present in a concentration in the range of between 3.0% and 4.0% by weight, based on the total weight of said second latex coating.
Claim 22
Dependent Claim
25 words
A process in accordance with claim 13 wherein said uniaxially drawn film is subjected to a corona discharge prior to the coating of said film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-07-22 | 1984-01-21 | 1984-07-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-07-22 | 1988-01-21 | 1988-07-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-07-22 | 1992-01-21 | 1992-07-22 | $7700.00 | Window Closed / Lapsed |