Method and apparatus for applying metal cladding on surfaces and products formed thereby
Assignee: Individual
•
Filing: 1983-12-20
•
Granted: 1985-06-04
•
Expires: 2003-12-20
Abstract
Abstract Small, preferably micronsized hollow glass or ceramic spheres or foaming agents for making such micronsized hollow spaces or voids are incorporated into a resin material which is formed into a layer and after curing of the resin layer, it is abraded, sand or grit blasted so as to rupture the outermost layer of spheres or voids to provide a plurality of undercuts or nooks and crannies. A thermally sprayed metal, such as copper, becomes embedded into the undercuts pores, nooks and crannies, such that the bond or adherent strength is greatly improved. This micronsized glass, ceramic spheres and/or pores greatly increases the bond strength by providing better undercuts in the surface to be sprayed by molten metal and provide the capability of depositing thicker layers without jeopardizing the bond.
Inventors
- 👤 Louis M. Riccio
- 👤 Alexander Bosna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:44
CPC Classifications
B; B05; B05D; B05D5/00; B63; B63B; B63B59/00; B63B59/04; C; C23; C23C; C23C4/00; C23C4/02; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24364; Y10T428/24372; Y10T428/24942; Y10T428/2495; Y10T428/25; Y10T428/252
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
97 words
In a marine surface protected from marine growth by an external layer of a thermally sprayed metal selected from copper and copper based alloys, the improvement wherein a layer of an adhesive resin is between said surface and said external layer of metal, a plurality of fractured inorganic hollow spheres in the interface between said resin and said external metal layer forming undercuts, nooks and crannies, said external layer of metal being constituted by a layer of solidified thermally sprayed metal particles sprayed in a molten state and filling and interlocking with said undercuts, nooks and crannies.
Claim 2
Dependent Claim
97 words
In a marine surface protected from marine growth by an external layer of a thermally sprayed metal selected from copper and copper based alloys, the improvement wherein a layer of an adhesive resin is between said surface and said external layer of metal, a plurality of fractured inorganic hollow spheres in the interface between said resin and said external metal layer forming undercuts, nooks and crannies, said external layer of metal being constituted by a layer of solidified thermally sprayed metal particles sprayed in a molten state and filling and interlocking with said undercuts, nooks and crannies.
Claim 3
Dependent Claim
46 words
The invention defined in claim 1 wherein said adhesive resin layer is a syntactic foam coating having an abraded surface to form said fractured inorganic hollow spheres, and said thermally sprayed metal particles are embedded in said fractured inorganic hollow spheres of said syntactic foam coating.
Claim 4
Dependent Claim
48 words
The invention defined in claim 1 including a first metal layer with metal particles selected from copper and copper-nickel alloys embedded in said adhesive layer and said layer of thermally sprayed metal particles is sprayed in a molten state at a high velocity on said first metal layer.
Claim 5
Dependent Claim
33 words
The invention defined in claim 3 wherein said first metal layer is copper metal and said thermally sprayed metal layer is copper-nickle alloy wherein the copper constitute 90-94% and the remainder is nickel.
Claim 6
Dependent Claim
22 words
The invention defined in claim 3 wherein said first metal layer is copper-nickle alloy and said thermally sprayed metal layer is copper.
Claim 7
Dependent Claim
36 words
The invention defined in claim 1 wherein said marine surface is a hull and said thermally applied metal layer is thicker in areas of possible mechanical abrasion and erosion, including the keel, bow and rudder areas.
Claim 8
Dependent Claim
25 words
The invention defined in claim 3 wherein said first metal layer and said thermally sprayed layer have a combined thickness of at least 3 mils.
Claim 9
Dependent Claim
19 words
The invention defined in claim 7 wherein said first metal layer is thinner than said thermally sprayed metal layer.
Claim 10
Dependent Claim
82 words
A metal clad surface comprising in combination, a layer of the remains of a plurality of ruptured hollow beads, said hollow beads being selected from the group consisting of glass and or ceramic beads and ranging in size to about 300 microns forming a layer of undercuts, an adhesive matrix securing said remains of a plurality of ruptured hollow beads to said surface, and a solidified metal layer filling said layer of undercuts, to mechanically lock said metal layer to said surface.
Claim 11
Dependent Claim
82 words
A metal clad surface comprising in combination, a layer of the remains of a plurality of ruptured hollow beads, said hollow beads being selected from the group consisting of glass and or ceramic beads and ranging in size to about 300 microns forming a layer of undercuts, an adhesive matrix securing said remains of a plurality of ruptured hollow beads to said surface, and a solidified metal layer filling said layer of undercuts, to mechanically lock said metal layer to said surface.
Claim 12
Dependent Claim
17 words
The metal clad surface defined in claim 9 wherein said adhesive matrix is a U.V. cured epoxy.
Claim 13
Dependent Claim
18 words
The metal clad surface defined in claim 9 wherein said metal layer is copper metal including alloys thereof.
Claim 14
Dependent Claim
24 words
The metal clad surface defined in claim 11 wherein said surface is a marine surface and said copper metal inhibits incrustation of said surface.
Claim 15
Dependent Claim
81 words
In a marine surface protected from marine growth by an external layer of a thermally sprayed molten metal selected from copper and copper based alloys, the improvement comprising, a matrix layer of undercuts, nooks and crannies constituted by a layer of fractured, inorganic hollow spherical bodies, an adhesive layer securing said matrix layer to said marine surface and said layer of metal is constituted by a solidified layer of said molten metal filling and interlocking with said undercuts, nooks and crannies.
Claim 16
Dependent Claim
81 words
In a marine surface protected from marine growth by an external layer of a thermally sprayed molten metal selected from copper and copper based alloys, the improvement comprising, a matrix layer of undercuts, nooks and crannies constituted by a layer of fractured, inorganic hollow spherical bodies, an adhesive layer securing said matrix layer to said marine surface and said layer of metal is constituted by a solidified layer of said molten metal filling and interlocking with said undercuts, nooks and crannies.
Claim 17
Dependent Claim
19 words
The invention defined in claim 13 wherein said fractured hollow bodies are the remains of hollow micronsized glass spheres.
Claim 18
Dependent Claim
18 words
The invention defined in claim 13 wherein said fractured hollow bodies are the remains of micronsized ceramic spheres.
Claim 19
Dependent Claim
14 words
The invention defined in claim 13 wherein said adhesive layer is an epoxy resin.
Claim 20
Dependent Claim
23 words
The invention defined in claim 16 wherein said hollow bodies are selected from the group consisting of micronsized glass or ceramic hollow spheres.
Claim 21
Dependent Claim
19 words
The invention defined in claim 17 wherein said spheres range in size from about 10 to about 300 microns.
Claim 22
Dependent Claim
22 words
The invention defined in claim 18 wherein said spheres comprise from at least about 20 percent by volume of said epoxy resin.
Claim 23
Dependent Claim
24 words
The invention defined in claim 19 wherein said hollow spheres are in a proportion greater than 50 percent by volume relative to said adhesive.
Claim 24
Dependent Claim
14 words
The invention defined in claim 18 wherein said hollow spheres are in different sizes.
Claim 25
Dependent Claim
30 words
The invention defined in claim 17 wherein said micronsized spheres range in size from 10 to about 300 microns and comprise at least 20 percent by volume of said resin.
Claim 26
Dependent Claim
18 words
The metal clad surface defined in claim 9 wherein said metal layer is greater than 3 mils thick.
Claim 27
Dependent Claim
19 words
The invention defined in claim 13 wherein said marine surface is a portion of the hull of a vessel.
References Cited (Backward Citations)
US819125A
Cited
US3144349A
Cited
US3325303A
Cited
US3179531A
Cited
US3097932A
Cited
US3476577A
Cited
JPS54135851A
Cited
US4182641A
Cited
US4226906A
Cited
US4303730A
Cited
JPS5633485A
Cited
US4307142A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-03 | 1988-12-03 | 1989-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-03 | 1992-12-03 | 1993-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-03 | 1996-12-03 | 1997-06-04 | $7700.00 | Window Closed / Lapsed |