Rapidly dissolvable silicates and methods of using the same
Assignee: Halliburton Co
•
Filing: 1982-09-27
•
Granted: 1985-06-04
•
Expires: 2002-09-27
Abstract
Abstract Rapidly dissolvable powdered silicates having a molar ratio of silicon dioxide to alkali metal oxide in the range of from about 1.5:1 to about 3.3:1 wherein the alkali metal is selected from the group consisting of sodium, potassium and mixtures thereof. Methods of using the powdered silicates and resulting solutions in connection with sealing and cementing, especially of well formations, are provided.
Inventors
- 👤 Joseph R. Murphey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:09
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/50; C01; C01B; C01B33/00; C01B33/20; C01B33/32; C01B33/325; C04; C04B; C04B12/00; C04B12/04; C09K8/02; C09K8/04; C09K8/14; C09K8/145; C09K8/42
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
109 words
A method of preparing an earth formation for bonding with cement comprising the steps of preparing an aqueous solution of potassium silicate by dissolving in water a highly dissolvable partially hydrated powdered potassium silicate having a water content in the range of from about 14 percent to about 16 percent by weight of said partially hydrated powdered silicate and wherein said powder is comprised of amorphous particles of said potassium silicate and flushing the earth formation with said aqueous solution of potassium silicate, said partially hydrated amorphous potassium silicate having a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1.
Claim 2
Independent Claim
109 words
A method of preparing an earth formation for bonding with cement comprising the steps of preparing an aqueous solution of potassium silicate by dissolving in water a highly dissolvable partially hydrated powdered potassium silicate having a water content in the range of from about 14 percent to about 16 percent by weight of said partially hydrated powdered silicate and wherein said powder is comprised of amorphous particles of said potassium silicate and flushing the earth formation with said aqueous solution of potassium silicate, said partially hydrated amorphous potassium silicate having a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1.
Claim 3
Independent Claim
98 words
A method of preparing an anhydrite earth formation for bonding with cement comprising the steps of preparing an aqueous solution of potassium silicate by dissolving in water a highly dissolvable, partially hydrated, powdered amorphous potassium silicate having a water content in the range of from about 14 percent to about 16 percent by weight of said partially hydrated silicate and flushing said anhydrite earth formation with said aqueous solution of potassium silicate, said partially hydrated amorphous potassium silicate having a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1.
Claim 4
Independent Claim
98 words
A method of preparing an anhydrite earth formation for bonding with cement comprising the steps of preparing an aqueous solution of potassium silicate by dissolving in water a highly dissolvable, partially hydrated, powdered amorphous potassium silicate having a water content in the range of from about 14 percent to about 16 percent by weight of said partially hydrated silicate and flushing said anhydrite earth formation with said aqueous solution of potassium silicate, said partially hydrated amorphous potassium silicate having a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1.
Claim 5
Independent Claim
91 words
A method of preparing an earthen formation for bonding with cement comprising: preparing an aqueous solution of potassium silicate by dissolving a highly dissolvable partially hydrated amorphous potassium silicate having a water content in the range of from about 12 to about 20 percent by weight and a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1 in an aqueous fluid; and flushing said earthen formation with said prepared aqueous solution of potassium silicate to prepare said formation for bonding with cement.
Claim 6
Independent Claim
91 words
A method of preparing an earthen formation for bonding with cement comprising: preparing an aqueous solution of potassium silicate by dissolving a highly dissolvable partially hydrated amorphous potassium silicate having a water content in the range of from about 12 to about 20 percent by weight and a molar ratio of silicon dioxide to potassium oxide in the range of from about 1.5:1 to about 3.3:1 in an aqueous fluid; and flushing said earthen formation with said prepared aqueous solution of potassium silicate to prepare said formation for bonding with cement.
Claim 7
Dependent Claim
29 words
The method of claim 3 wherein said partially hydrated amorphous potassium silicate has a moisture content in the range of from about 14 to about 16 percent by weight.
Claim 8
Dependent Claim
26 words
The method of claim 3 wherein said molar ratio of silicon dioxide to potassium oxide is in the range of from about 2.0:1 to about 2.7:1.
Claim 9
Dependent Claim
14 words
The method of claim 3 wherein said earthen formation is an anhydrite earth formation.
References Cited (Backward Citations)
US3094846A
Cited
US3411582A
Cited
US3679001A
Cited
US3865600A
Cited
US4081029A
Cited
US4257483A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-03 | 1988-12-03 | 1989-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-03 | 1992-12-03 | 1993-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-03 | 1996-12-03 | 1997-06-04 | $7700.00 | Window Closed / Lapsed |