US4520040A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ferromagnetic films for high density recording and methods of production
Assignee: VARLIAN ASSOCIATESS Inc A DE CORP
•
Filing: 1983-12-15
•
Granted: 1985-05-28
•
Expires: 2003-12-15
Abstract
Abstract A ferromagnetic film for magnetic recording comprises a copper substrate having particles of iron and iron oxides dispersed in the surface layer of the copper. The particles have maximum dimensions in the range between 50 and 500 Angstroms. The ferromagnetic film can be formed by ion implantation of iron ions into the copper substrate followed by heat treatment to permit growth of ferromagnetic particles to the desired size. As an alternative to ion implantation, the iron can be deposited on the copper substrate by sputtering or evaporation and mixed with the copper by ion beam mixing.
Inventors
- 👤 Bernhard F. Cordts
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:35
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/16; C23C14/165; C23C14/22; C23C14/48; C23C14/58; C23C14/5806; C23C14/5826; C23C14/5833; C23C14/584; C23C14/5893; G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70605; G11B5/70615; G11B5/70626; G11B5/70642; G11B5/73; G11B5/739; G11B5/73911; G11B5/73917; G11B5/84; G11B5/85; G11B5/851
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
52 words
A method for fabricating a ferromagnetic film comprising the steps of: providing a substrate of a material having low solubility for a selected ferromagnetic material; implanting ions of the selected ferromagnetic material into a surface layer of said substrate; and heating said substrate to permit growth of particles of said ferromagnetic material.
Claim 2
Independent Claim
52 words
A method for fabricating a ferromagnetic film comprising the steps of: providing a substrate of a material having low solubility for a selected ferromagnetic material; implanting ions of the selected ferromagnetic material into a surface layer of said substrate; and heating said substrate to permit growth of particles of said ferromagnetic material.
Claim 3
Dependent Claim
21 words
The method as defined in claim 1 wherein said selected ferromagnetic material comprises iron and wherein said substrate material comprises copper.
Claim 4
Dependent Claim
28 words
The method as defined in claim 2 wherein said step of heating said substrate is sufficient to produce particles having a maximum dimension between 50 and 500 Angstroms.
Claim 5
Dependent Claim
23 words
The method as defined in claim 2 wherein said step of heating said substrate is performed simultaneously with said step of implanting ions.
Claim 6
Dependent Claim
38 words
The method as defined in claim 3 wherein said iron ions are implanted in said substrate at energies between 80 KeV and 120 KeV and at doses between 5×10 16 ions/cm 2 and 5×10 17 ions/cm 2 .
Claim 7
Independent Claim
85 words
A method for fabricating a ferromagnetic film comprising the steps of: providing a substrate of a material having low solubility for a selected ferromagnetic material; depositing a thin layer of said selected ferromagnetic material on the surface of said substrate; irradiating said layer of ferromagnetic material with an ion beam of an inert material so as to cause ion beam mixing of said ferromagnetic material into a surface layer of said substrate; and heating said substrate to permit growth of particles of said ferromagnetic material.
Claim 8
Independent Claim
85 words
A method for fabricating a ferromagnetic film comprising the steps of: providing a substrate of a material having low solubility for a selected ferromagnetic material; depositing a thin layer of said selected ferromagnetic material on the surface of said substrate; irradiating said layer of ferromagnetic material with an ion beam of an inert material so as to cause ion beam mixing of said ferromagnetic material into a surface layer of said substrate; and heating said substrate to permit growth of particles of said ferromagnetic material.
Claim 9
Dependent Claim
21 words
The method as defined in claim 6 wherein said selected ferromagnetic material comprises iron and wherein said substrate material comprises copper.
Claim 10
Dependent Claim
21 words
The method as defined in claim 6 wherein said thin layer of ferromagnetic material is deposited on said substrate by sputtering.
Claim 11
Dependent Claim
23 words
The method as defined in claim 7 wherein said layer of ferromagnetic material is deposited to a thickness between 200 and 500 Angstroms.
Claim 12
Dependent Claim
28 words
The method as defined in claim 7 wherein said step of heating said substrate is sufficient to produce particles having a maximum dimension between 50 and 500 Angstroms.
Claim 13
Dependent Claim
23 words
The method as defined in claim 10 wherein said ion beam comprises ions selected from the group consisting of argon, xenon and krypton.
Claim 14
Dependent Claim
33 words
The method as defined in claim 11 wherein said ion beam comprises argon and irradiates said layer of ferromagnetic material at doses between 5×10 16 ion/cm 2 and 5×10 17 ions/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-27 | 1988-11-26 | 1989-05-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-27 | 1992-11-26 | 1993-05-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-27 | 1996-11-26 | 1997-05-28 | $7700.00 | Window Closed / Lapsed |