Method and apparatus for the production of a high-strength, tear-resistant polymer composite
Assignee: Mobil Oil AS
•
Filing: 1982-11-05
•
Granted: 1985-05-28
•
Expires: 2002-11-05
Abstract
Abstract A method and an apparatus for the production of a composite plastic material consisting of oriented polymer filaments and a polymer film web, and more particularly, the production of a composite material which possesses an improved physical strength and higher tear resistance in comparison with plastic film materials which are not reinforced. An extrusion die is used for example, a conventional tubular extrusion die for extruding a continuous blown tubular plastic film web and wherein the die orifice is encompassed by spinerette apertures through which there are concurrently extruded a plurality of polymer filaments which are oriented and initially conveyed along a path substantially parallel to but not in adherence with the blown tubular plastic film web. Upon a further separation of the filaments and the tubular film, the filaments may be at least partially coated with a suitable adhesive material and, thereafter, adhesively bonded or laminated to the surface of the film web in order to produce a composite material constituted of filaments and film.
Inventors
- 👤 Gordon V. Sharps, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:21
CPC Classifications
B; B29; B29C; B29C66/00; B29C66/40; B29C66/47; B29C66/474; B29C48/00; B29C48/03; B29C48/05; B29C48/07; B29C48/08; B29C48/09; B29C48/10; B29C48/25; B29C48/30; B29C48/345; B29C65/00; B29C65/48; B29C65/4805; B29C65/481; B29C65/4815; B29C66/01; B29C66/05; B29C66/10; B29C66/11; B29C66/112; B29C66/1122; B29C66/70; B29C66/73; B29C66/739; B29C66/7392; B29C66/80; B29C66/83; B29C66/834; B29C66/8341; B29C66/83411; B29C66/83413; B29C66/83415; B29C48/001; B29C48/0018; B29C48/0019; B29C65/02; B29C65/18; B29C66/472; B29C66/4722; B29C66/71; B29C66/72; B29C66/721; B29C66/7212; B29C66/7214; B29C66/72141; Y; Y10; Y10S; Y10S264/00; Y10S264/81
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
240 words
A method of producing a continuous coextruded plastic composite material consisting of a thermoplastic film web and polymer filaments adhesively bonded thereto; comprising: (a) extruding a continuous web of a thermoplastic film material from an extrusion die; (b) concurrently extruding a plurality of oriented thermoplastic filaments from said extrusion die in spaced relationship with said film web, substantially immediately directing the filaments away from the film web to facilitate cooling of the filaments and prevent distortion of the film web and maintaining said film web and filaments apart for a predetermined time interval subsequent to the extrusion from said die to allow for cooling of the filaments and film web; (c) contacting said film web with said filaments and conveying the superimposed film webs and filaments between first nip rolls after the filaments and film web have been sufficiently cooled to avoid adherence between the filaments and film web and deformation of the web subsequent cooling; (d) separating said filaments from said film web and imparting tension to said filaments to maintain uniform filament tension and maintain the filaments under a predetermined tensile load; (e) applying an adhesive to said filaments on at least the surfaces facing towards said film web; (f) and contacting said film web and the adhesive-coated surfaces of said filaments; and conveying said contacted film web and filaments between second nip rolls to adhesively bond said filaments to said film web and form said composite material.
Claim 2
Independent Claim
240 words
A method of producing a continuous coextruded plastic composite material consisting of a thermoplastic film web and polymer filaments adhesively bonded thereto; comprising: (a) extruding a continuous web of a thermoplastic film material from an extrusion die; (b) concurrently extruding a plurality of oriented thermoplastic filaments from said extrusion die in spaced relationship with said film web, substantially immediately directing the filaments away from the film web to facilitate cooling of the filaments and prevent distortion of the film web and maintaining said film web and filaments apart for a predetermined time interval subsequent to the extrusion from said die to allow for cooling of the filaments and film web; (c) contacting said film web with said filaments and conveying the superimposed film webs and filaments between first nip rolls after the filaments and film web have been sufficiently cooled to avoid adherence between the filaments and film web and deformation of the web subsequent cooling; (d) separating said filaments from said film web and imparting tension to said filaments to maintain uniform filament tension and maintain the filaments under a predetermined tensile load; (e) applying an adhesive to said filaments on at least the surfaces facing towards said film web; (f) and contacting said film web and the adhesive-coated surfaces of said filaments; and conveying said contacted film web and filaments between second nip rolls to adhesively bond said filaments to said film web and form said composite material.
Claim 3
Dependent Claim
30 words
A method as claimed in claim 1, comprising controlling the temperature of said second nip rolls for regulating the extent of adhesive bonding between said filaments and said film web.
Claim 4
Dependent Claim
38 words
A method as claimed in claim 1, comprising cooling said filaments prior to initial contacting of said filaments with said film web subsequent to extrusion thereof so as to preclude said filaments from adhering to said film web.
Claim 5
Dependent Claim
38 words
A method as claimed in claim 1, comprising controlling the speed of said second nip rolls relative to the speed of said first nip rolls to maintain a predetermined film web tension during adhesive bonding with said filaments.
Claim 6
Dependent Claim
34 words
A method as claimed in claim 1, said film web comprising a tubular film extruded from an annular die, said filaments being extruded through spinerette apertures spaced about the circumference of said annular die.
Claim 7
Dependent Claim
14 words
A method as claimed in claim 1, said filaments consisting of low density polyethylene.
Claim 8
Dependent Claim
20 words
A method as claimed in claim 1, said filaments consisting of circular strands having a diameter of about 0.020 inches.
Claim 9
Independent Claim
218 words
An apparatus for the production of a continuous coextruded plastic composite material consisting of a thermoplastic film web and polymer filaments adhesively bonded thereto; comprising: (a) a coextrusion die for concurrently extruding a continuous web of thermoplastic material and a plurality of oriented polymer filaments in spaced relationship with said film web and means for substantially immediately directing the filaments away from the film web after extrusion thereof to facilitate cooling of the filaments and to prevent film web distortion (b) means for orienting and cooling said filaments prior to contacting said film web to prevent adhesion between said film web and said filaments upon superposition therebetween and permitting the filaments and film web to be sufficiently cooled to facilitate avoiding adherence between the filaments and film web thereafter and distortion of the film during subsequent cooling; (c) first nip rolls contacting said film web and said filaments, said film web and said filaments being separated after passing between said first nip rolls; (d) means for imparting a predetermined tension to said filaments and maintaining the filaments under a predetermined tensile load; (e) means for applying an adhesive to said filaments; (f) and second nip rolls receiving said film web and adhesive-coated filaments and applying pressure thereto to form said adhesively bonded film web and filament composite material.
Claim 10
Independent Claim
218 words
An apparatus for the production of a continuous coextruded plastic composite material consisting of a thermoplastic film web and polymer filaments adhesively bonded thereto; comprising: (a) a coextrusion die for concurrently extruding a continuous web of thermoplastic material and a plurality of oriented polymer filaments in spaced relationship with said film web and means for substantially immediately directing the filaments away from the film web after extrusion thereof to facilitate cooling of the filaments and to prevent film web distortion (b) means for orienting and cooling said filaments prior to contacting said film web to prevent adhesion between said film web and said filaments upon superposition therebetween and permitting the filaments and film web to be sufficiently cooled to facilitate avoiding adherence between the filaments and film web thereafter and distortion of the film during subsequent cooling; (c) first nip rolls contacting said film web and said filaments, said film web and said filaments being separated after passing between said first nip rolls; (d) means for imparting a predetermined tension to said filaments and maintaining the filaments under a predetermined tensile load; (e) means for applying an adhesive to said filaments; (f) and second nip rolls receiving said film web and adhesive-coated filaments and applying pressure thereto to form said adhesively bonded film web and filament composite material.
Claim 11
Dependent Claim
34 words
An apparatus as claimed in claim 8, wherein said second nip rolls are temperature-controlled for regulating the temperature of said adhesive-coated filaments and film web during adhesive bonding thereof between said second nip rolls.
Claim 12
Dependent Claim
41 words
An apparatus as claimed in claim 8, wherein the speed of said second nip rolls is regulated relative to the speed of said first nip rolls to maintain a predetermined tension in said film web during adhesive bonding with said filaments.
Claim 13
Dependent Claim
23 words
An apparatus as claimed in claim 8, said filament cooling means comprising means for directing a flow of cooling air against said filaments.
Claim 14
Dependent Claim
21 words
An apparatus as claimed in claim 8, said means for applying adhesive to said filaments comprising a hot melt adhesive applicator.
Claim 15
Dependent Claim
34 words
An apparatus as claimed in claim 8, said coextrusion die comprising an annular die for extruding a tubular film web; and spinerette apertures being spaced about said annular die for concurrently extruding said filaments.
Claim 16
Dependent Claim
23 words
An apparatus as claimed in claim 13, said filament cooling means including a cooling ring directing a flow of air against said filaments.
Claim 17
Dependent Claim
19 words
An apparatus as claimed in claim 14, comprising guide roller means for directing said filaments past said cooling means.
References Cited (Backward Citations)
US3034941A
Cited
US3534437A
Cited
US3589958A
Cited
US3770539A
Cited
US3926706A
Cited
US3915776A
Cited
US3957566A
Cited
US3959057A
Cited
US4350549A
Cited
US4428791A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-27 | 1988-11-26 | 1989-05-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-27 | 1992-11-26 | 1993-05-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-27 | 1996-11-26 | 1997-05-28 | $7700.00 | Window Closed / Lapsed |