Catalyst for the reduction of nitrogen oxides in gaseous mixtures and method of making the catalyst
Assignee: Honeywell UOP LLC
•
Filing: 1984-01-25
•
Granted: 1985-05-21
•
Expires: 2004-01-25
Abstract
Abstract A catalyst useful for the reduction of nitrogen oxide comprising vanadium and, optionally, tungsten deposited on an inorganic oxide support, preferably titania. A precursor of the catalyst is treated with an acid from the group comprising the moderately strong organic acids and/or the strong mineral acids, excluding sulfuric acid and phosphoric acid, preferably following the deposition of the metal(s). Other aspects of the invention are a method of preparing the catalyst and a process for its use wherein a gaseous stream of nitrogen oxide and ammonia is contacted with the catalyst at reductive reaction conditions.
Inventors
- 👤 John F. Brennan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:13
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/16; B01J23/24; B01J23/30; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01D53/8621; B01D53/8625; B01D53/8628
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
49 words
A catalyst composition useful for the reduction of nitrogen oxide comprising an inorganic oxide support having tungsten and vanadium deposited thereon, said support having been treated, before or after the deposition of either of said tungsten or vanadium thereon, with a strong mineral acid, excluding sulfuric and phosphoric acids.
Claim 2
Dependent Claim
49 words
A catalyst composition useful for the reduction of nitrogen oxide comprising an inorganic oxide support having tungsten and vanadium deposited thereon, said support having been treated, before or after the deposition of either of said tungsten or vanadium thereon, with a strong mineral acid, excluding sulfuric and phosphoric acids.
Claim 3
Dependent Claim
12 words
The catalyst composition of claim 1 wherein said inorganic acid comprises titania.
Claim 4
Dependent Claim
12 words
The catalyst composition of claim 1 wherein said acid is nitric acid.
Claim 5
Dependent Claim
29 words
The catalyst composition of claim 1 wherein the content of vanadium in said catalyst is from about 0.5 wt. % to about 15 wt. % on an elemental basis.
Claim 6
Dependent Claim
47 words
The catalyst composition of claim 1 wherein said acid treatment is effected at a temperature of from about 60° C. to about 200° C. and with an amount of acid which provides from about 0.05 to about 0.60 moles of hydrogen ions per mole of inorganic oxide.
Claim 7
Independent Claim
96 words
A method of manufacture of a catalyst composition useful for the reduction of nitrogen oxides comprising tungsten and vanadium on an inorganic oxide support, said method comprising depositing a salt of vanadium and a salt of tungsten on said support from an aqueous solution of said salt, thereafter acid treating the resultant tungsten and vanadium-containing support with an acid from the group comprising the strong mineral acids, excluding sulfuric acid and phosphoric acid, by contacting said tungsten and vanadium-containing support with an aqueous solution of said acid, and then drying and calcining the acid treated support.
Claim 8
Independent Claim
96 words
A method of manufacture of a catalyst composition useful for the reduction of nitrogen oxides comprising tungsten and vanadium on an inorganic oxide support, said method comprising depositing a salt of vanadium and a salt of tungsten on said support from an aqueous solution of said salt, thereafter acid treating the resultant tungsten and vanadium-containing support with an acid from the group comprising the strong mineral acids, excluding sulfuric acid and phosphoric acid, by contacting said tungsten and vanadium-containing support with an aqueous solution of said acid, and then drying and calcining the acid treated support.
Claim 9
Dependent Claim
48 words
The method of claim 6 wherein said salts are sequentially deposited on said support by immersing said support in an aqueous solution of one salt, evaporating the solution to dryness, calcining the support, and repeating the immersions, drying and calcining with the aqueous solution of the other salt.
Claim 10
Dependent Claim
11 words
The method of claim 1 wherein said acid is nitric acid.
Claim 11
Dependent Claim
19 words
The method of claim 6 wherein the tungsten salt is deposited prior to the deposition of the vanadium salt.
Claim 12
Dependent Claim
91 words
The method of claim 9 wherein said salts are deposited on said support by the sequential steps of (a) immersing a powder of said support in an aqueous solution of ammonium meta tungstate, (b) evaporating said solution to dryness, (c) calcining the tungsten containing support, (d) immersing the support in an aqueous solution of ammonium meta vanadate and a sufficient amount of a weak acid to reduce the oxidation state of the vanadium ion from +5 to +4, (e) evaporating the solution to dryness, and (f) calcining the metals containing support.
Claim 13
Dependent Claim
76 words
The method of claim 6 wherein said acid treatment is effected with a concentrated aqueous solution of said acid at a temperature of from about 60° C. to about 200° C. and with an amount of acid which provides from about 0.05 to about 0.60 moles of hydrogen ions per mole of inorganic oxide in the support, and then drying and calcining said support having vanadium and tungsten deposited thereon to produce said resultant catalyst composition.
Claim 14
Dependent Claim
21 words
The method of claim 11 wherein the temperature of said calcining step is from about 300° C. to about 600° C.
Claim 15
Dependent Claim
57 words
The method of claim 11 wherein the amount of water in solution with said acid is just enough to form a thick paste of acid and support and prior to drying and calcining said support and acid, the paste is extruded, the extrudate being dried and calcined and then broken and ground to the desired particle sizes.
Claim 16
Dependent Claim
50 words
The method of claim 11 wherein said support with tungsten and vanadium deposited thereon is present in the form of a powder after drying and calcining, said powder then being slurried with water and the slurry then being used to coat a ceramic monolith which is then dried and calcined.
Claim 17
Independent Claim
92 words
A method of manufacture of a catalyst composition useful for the reduction of nitrogen oxides comprising vanadium and tungsten on an inorganic support, said method comprising acid treating said inorganic oxide support with an aqueous solution of a strong mineral acid, excluding sulfuric acid and phosphoric acid, thereafter depositing a salt of vanadium and a salt of tungsten on said acid-treated support from an aqueous solution of said salt of said vanadium and salt of tungsten and then drying and calcining said acid-treating vanadium-containing and tungsten-containing support to form said catalyst composition.
Claim 18
Independent Claim
92 words
A method of manufacture of a catalyst composition useful for the reduction of nitrogen oxides comprising vanadium and tungsten on an inorganic support, said method comprising acid treating said inorganic oxide support with an aqueous solution of a strong mineral acid, excluding sulfuric acid and phosphoric acid, thereafter depositing a salt of vanadium and a salt of tungsten on said acid-treated support from an aqueous solution of said salt of said vanadium and salt of tungsten and then drying and calcining said acid-treating vanadium-containing and tungsten-containing support to form said catalyst composition.
References Cited (Backward Citations)
US4071601A
Cited
US4117081A
Cited
US4048112A
Cited
US4085193A
Cited
US4119703A
Cited
NL7514277A
Cited
US4119568A
Cited
US4096096A
Cited
US4131643A
Cited
US4093561A
Cited
US4138469A
Cited
US4255285A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-20 | 1988-11-19 | 1989-05-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-20 | 1992-11-19 | 1993-05-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-20 | 1996-11-19 | 1997-05-21 | $7700.00 | Window Closed / Lapsed |