Flexographic printing plates and process for making the same
Assignee: Nippon Paint Co Ltd
•
Filing: 1982-08-13
•
Granted: 1985-05-14
•
Expires: 2002-08-13
Abstract
Abstract A photosensitive resin composition useful for preparation of flexographic printing plates, which comprises syndiotactic 1,2-polybutadiene, an ethylenically unsaturated monomer and a photo-polymerization initiator, the syndiotactic 1,2-polybutadiene having an average molecular weight of from about 10,000 to 300,000, a 1,2-unit content of at least about 80 percent and a crystallinity of about 10 to 30 percent, said ethylenically unsaturated monomer being an ester of acrylic or methacrylic acid with an alkanol having from 4 to 20 carbon atoms, and the photo-polymerization initiator being benzoin or an alkyl ether thereof. The photosensitive resin composition, when formed into sheets, exhibits satisfactory resistance to liquids used for washing out the uncured areas and at also to aqueous or alcoholic printing inks, thereby producing patterns in relief that give excellent overall sharpness. It also possesses desired hardness and elasticity for flexographic printing plates.
Inventors
- 👤 Kiyomi Sakurai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:46
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/027; G03F7/032; G03F7/033; Y; Y10; Y10S; Y10S430/00; Y10S430/1053; Y10S430/1055; Y10S430/114; Y10S430/118; Y10S430/119
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
100 words
A molded sheet suitable for use as a flexographic printing plate which is melt-molded from a photosensitive resin composition comprising syndiotactic 1,2-polybutadiene permeated with a solution of an ethylenically unsaturated monomer and a photo-polymerization initiator, the syndiotactic 1,2-polybutadiene having an average molecular weight of from about 10,000 to 300,000, a 1,2-unit content of at least about 80 percent and a crystallinity of about 10 to 30 percent, the ethylenically unsaturated monomer being an ester of acrylic or methacrylic acid with an alkanol having from 4 to 20 carbon atoms, and the photo-polymerization initiator being benzoin or an alkyl ether thereof.
Claim 2
Dependent Claim
100 words
A molded sheet suitable for use as a flexographic printing plate which is melt-molded from a photosensitive resin composition comprising syndiotactic 1,2-polybutadiene permeated with a solution of an ethylenically unsaturated monomer and a photo-polymerization initiator, the syndiotactic 1,2-polybutadiene having an average molecular weight of from about 10,000 to 300,000, a 1,2-unit content of at least about 80 percent and a crystallinity of about 10 to 30 percent, the ethylenically unsaturated monomer being an ester of acrylic or methacrylic acid with an alkanol having from 4 to 20 carbon atoms, and the photo-polymerization initiator being benzoin or an alkyl ether thereof.
Claim 3
Dependent Claim
126 words
A process for making a molded sheet suitable for use as a flexographic printing plate comprising: (a) immersing syndiotactic 1,2-polybutadiene pellets in a solution of an ethylenically unsaturated monomer and a photo-polymerization initiator so that the solution permeates the pellets, the syndiotactic 1,2-polybutadiene having an average molecular weight of from about 10,000 to 300,000, a 1,2-unit content of at least about 80 percent and a crystallinity of about 10 to 30 percent, the ethylenically unsaturated monomer being an ester of acrylic or methacrylic acid with an alkanol having from 4 to 20 carbon atoms, and the photopolymerication initiator being benzoin or an alkyl ether thereof; and then (b) melt molding said pellets into sheets having a thickness in the range of about 0.1 to 10 mm.
Claim 4
Dependent Claim
126 words
A process for making a molded sheet suitable for use as a flexographic printing plate comprising: (a) immersing syndiotactic 1,2-polybutadiene pellets in a solution of an ethylenically unsaturated monomer and a photo-polymerization initiator so that the solution permeates the pellets, the syndiotactic 1,2-polybutadiene having an average molecular weight of from about 10,000 to 300,000, a 1,2-unit content of at least about 80 percent and a crystallinity of about 10 to 30 percent, the ethylenically unsaturated monomer being an ester of acrylic or methacrylic acid with an alkanol having from 4 to 20 carbon atoms, and the photopolymerication initiator being benzoin or an alkyl ether thereof; and then (b) melt molding said pellets into sheets having a thickness in the range of about 0.1 to 10 mm.
Claim 5
Dependent Claim
19 words
The process of claim 2 wherein said melt molding is carried out at a temperature of about 90°-160° C.
References Cited (Backward Citations)
US3615469A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-13 | 1988-11-12 | 1989-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-13 | 1992-11-12 | 1993-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-13 | 1996-11-12 | 1997-05-14 | $7700.00 | Window Closed / Lapsed |