Forming of thick-layer, hybrid electronic printed circuits
Assignee: Novartis Corp
•
Filing: 1982-11-12
•
Granted: 1985-05-14
•
Expires: 2002-11-12
Abstract
Abstract Thick-layer hybrid electronic printed circuits are formed by printing predetermined circuit pattern onto an insulating substrate by deposition of predetermined ink pattern thereupon, advantageously by silk-screening or masking, and then baking said ink circuit pattern, and repeating the deposition/baking steps as required, the subject forming process featuring use of an insulating ink comprising a non-conductive metallic oxide extender, desirably cuprous oxide, which ink is thus either potentially conductive or potentially resistive, and the development of such conductivity or resistivity, after baking, by treating the ink pattern with a reducing agent, desirably a borohydride, as to readily and quantitatively convert said metal oxide into a conducting metal.
Inventors
- 👤 Robert Cassat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:09
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/105; H01; H01B; H01B1/00; H01B1/14; H01B1/16; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/097; H10; H10D; H10D84/00; H10D84/01; H05K2203/00; H05K2203/11; H05K2203/1157; H05K2203/12; H05K2203/125
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
106 words
In a process for forming a thick-layer hybrid electronic printed circuit, including printing predetermined circuit pattern onto an insulating substrate by deposition of predetermined ink pattern thereupon and thence baking said ink circuit pattern, and repeating said deposition/baking steps as required, the improvement which comprises employing an insulating ink comprising a non-conducting oxide derived from a non-noble metal which is either potentially conducting or potentially resistant, and then developing either the conductivity or resistivity of the said ink after it has been deposited and baked, by reducing same with a borohydride reducing agent adapted to readily and quantitatively convert said metal oxide into a conducting metal.
Claim 2
Dependent Claim
106 words
In a process for forming a thick-layer hybrid electronic printed circuit, including printing predetermined circuit pattern onto an insulating substrate by deposition of predetermined ink pattern thereupon and thence baking said ink circuit pattern, and repeating said deposition/baking steps as required, the improvement which comprises employing an insulating ink comprising a non-conducting oxide derived from a non-noble metal which is either potentially conducting or potentially resistant, and then developing either the conductivity or resistivity of the said ink after it has been deposited and baked, by reducing same with a borohydride reducing agent adapted to readily and quantitatively convert said metal oxide into a conducting metal.
Claim 3
Dependent Claim
25 words
The process as defined by claim 1, said insulating ink comprising, before baking, at least one cuprous oxide extender, a binder and a diluent therefor.
Claim 4
Dependent Claim
53 words
The process as defined by claim 2, said insulating ink comprising a potentially conducting ink including a single cuprous oxide extender, present in an amount ranging from 40 to 70% of the weight of the ink, and a binder in an amount of from 4 to 10% of the weight of the ink.
Claim 5
Dependent Claim
78 words
The process as defined by claim 2, said insulating ink comprising a potentially resistant ink including a mixture of extenders comprising from 40 to 60% by weight of cuprous oxide and 60 to 40% by weight of an inert insulating extender, such mixture of extenders being present in an amount of from 30 to 60% of the weight of the ink, and a binder in an amount of from 10 to 30% of the weight of the ink.
Claim 6
Dependent Claim
25 words
The process as defined by claim 2, wherein the binder comprising said ink comprises a thermosetting prepolymer of phenolic, unsaturated polyester, epoxy or polyimide type.
Claim 7
Dependent Claim
52 words
The process as defined by claim 5, wherein the binder comprising said ink comprises a prepolymer of polyimide type, obtained by reaction of an unsaturated dicarboxylic acid N,N'-bis-imide with a primary polyamine, and optionally an adjuvant comprising a mono-imide, an ethylenically unsaturated polymerizable comonomer, an unsaturated polyester or a hydroxylated organosilicon compound.
Claim 8
Dependent Claim
26 words
The process as defined by claim 2, wherein the diluent comprising said ink comprises an ether of an alkanol or glycol, or of a terpene alcohol.
Claim 9
Dependent Claim
41 words
The process as defined by claim 2, wherein the borohydride comprising said reducing agent comprises an unsubstituted alkali metal borohydride or a substituted borohydride in which up to three hydrogen atoms of the borohydride ion have been replaced by inert substituents.
Claim 10
Dependent Claim
56 words
The process as defined by claim 2, wherein the reducing agent is contacted with the ink, after baking, in the form of a solution in water or in a mixture of water and an inert polar solvent, the concentration of which, expressed as percentage by weight of the borohydride in solution, ranges from 0.5 to 10%.
Claim 11
Dependent Claim
39 words
The process as defined by claim 2, comprising selectively depositing the potentially conducting or resistant ink by silk-screen printing, next baking the ink, thence developing the deposit by reduction, and repeating said deposition, baking and reduction steps as required.
Claim 12
Dependent Claim
50 words
The process as defined by claim 2, comprising uniformly depositing the potentially conducting or resistant ink, next baking the ink, thence selectively developing the desired conducting or resistant portions of the circuit by reduction of the deposit employing masking technique, and repeating said deposition, baking and reduction steps as required.
Claim 13
Dependent Claim
28 words
The process as defined by claim 2, comprising printing at least one first level of circuits by silk-screening, and at least one next level of circuits by masking.
Claim 14
Dependent Claim
39 words
The process as defined by claim 2, comprising, successively, first depositing at least one circuit pattern by silk-screening, next depositing at least one additional circuit pattern by masking, and thence depositing at least one other circuit pattern by silk-screening.
Claim 15
Dependent Claim
45 words
The process as defined by claim 2, said insulating substrate comprising a completely polymerized resin matrix of phenolic, unsaturated polyester, epoxy or polyimide type, reinforced with a reinforcing amount of a cellulosic paper, cotton fabric, asbestos fabric, asbestos paper, glass fabric or glass mat filler.
Claim 16
Dependent Claim
23 words
The process as defined by claim 3, said insulating ink, after baking and reduction, having a surface resistivity of at most 0.1 Ω/□.
Claim 17
Dependent Claim
26 words
The process as defined by claim 4, said insulating ink, after baking and reduction, having a surface resistivity of at least 10 to 10 3 Ω/□.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-13 | 1988-11-12 | 1989-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-13 | 1992-11-12 | 1993-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-13 | 1996-11-12 | 1997-05-14 | $7700.00 | Window Closed / Lapsed |