US4515919A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Protective coating composition and process for aluminum and aluminum alloys
Assignee: Lockheed Martin Corp
•
Filing: 1983-05-09
•
Granted: 1985-05-07
•
Expires: 2003-05-09
Abstract
Abstract A protective coating composition and process is described for simultaneously sealing and priming the anodic coating applied to aluminum and alloys thereof without the need for elevated temperatures during a subsequent curing step. The composition comprises a colloidal, water-borne polyurethane resin which is an aromatic, aliphatic or alicyclic copolymer. The composition is curable at ambient temperatures but may include a cross-linking agent as well as a thermosetting catalyst. The process comprises the steps of anodizing the component to be coated, applying the coating composition at elevated temperatures to thereby simultaneously seal and prime the component and curing the sealed and primed component at ambient temperatures. If cross-linking agents are employed then elevated cure temperatures are utilized.
Inventors
- 👤 Robert E. Bradley
- 👤 William R. Keithler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:45
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; C25D11/24; C08; C08G; C08G18/00; C08G18/06; C08G18/83; C09; C09D; C09D175/00; C09D175/04; C09D5/00; C09D5/08; C08G2150/00; C08G2150/90
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
51 words
A protective coating composition for application to aluminum and aluminum alloy components during the sealing step of a typical anodizing process to seal and prime the component, said composition comprising: (a) a colloidal, water-borne polyurethane elastomer resin; (b) a cross-linking agent; (c) a thermosetting catalyst; and (d) a corrosion inhibiting agent.
Claim 2
Dependent Claim
51 words
A protective coating composition for application to aluminum and aluminum alloy components during the sealing step of a typical anodizing process to seal and prime the component, said composition comprising: (a) a colloidal, water-borne polyurethane elastomer resin; (b) a cross-linking agent; (c) a thermosetting catalyst; and (d) a corrosion inhibiting agent.
Claim 3
Dependent Claim
24 words
The protective coating composition of claim 1 wherein said elastomer resin is a polyurethane resin formed from an aromatic, aliphatic or alicyclic isocyanate copolymer.
Claim 4
Dependent Claim
38 words
The protective coating composition of claim 2, wherein said copolymer is formed from isocyanate prepolymers based on such monomers as 2,4-toluene diisocyanate; 2,6-toluene diisocyanate; 1,4-cyclohexane diisocyanate; dicyclohexylmethane 4,4'-diisocyanate; xylene diisocyanate; 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethylcyclohexane; hexamethylene diisocyanate; methylcyclohexyl diisocyanate or 2,4,4-trimethylhexylmethylene diisocyanate.
Claim 5
Dependent Claim
17 words
The protective coating composition of claim 1, wherein said cross-linking agent is aziridine or a substituted melamine.
Claim 6
Dependent Claim
15 words
The protective coating composition of claim 4, wherein said cross-linking agent is hexamethoxy methyl melamine.
Claim 7
Dependent Claim
30 words
The protective coating composition of claim 1, wherein said thermosetting catalyst is a Friedal- Krafts acid catalyst, a boron trifluoride or a titanate complex comprising pyrophosphate titanate or phosphite titanate.
Claim 8
Dependent Claim
19 words
The protective coating composition of claim 1 wherein said corrosion inhibiting agent is zinc, strontium, calcium, sodium, or potassium.
Claim 9
Dependent Claim
33 words
The protective coating composition of claim 1 wherein said corrosion inhibiting agent comprises soluble or unsoluble chromates, dichromates, tungstates or molybdates including amine complexes of molybdic or tungstic acids or organic titanate complexes.
Claim 10
Dependent Claim
104 words
A protective coating process for aluminum and aluminum alloy components comprising the steps of: (a) anodizing the component to be coated; (b) applying a coating composition comprising a colloidal, water-borne polyurethane resin, a cross-linking agent, a thermosetting catalyst and a corrosion-inhibiting agent to the anodized component at a temperature in the range of approximately 170° F. (76° C.) to about 200° F. (93° C.) for a period ranging from about 30 to 60 minutes, the time and temperature being inversely related whereby said composition seals and anodized component through hydration and simultaneously primes the anodized component; and (c) curing the sealed and primed component.
Claim 11
Dependent Claim
104 words
A protective coating process for aluminum and aluminum alloy components comprising the steps of: (a) anodizing the component to be coated; (b) applying a coating composition comprising a colloidal, water-borne polyurethane resin, a cross-linking agent, a thermosetting catalyst and a corrosion-inhibiting agent to the anodized component at a temperature in the range of approximately 170° F. (76° C.) to about 200° F. (93° C.) for a period ranging from about 30 to 60 minutes, the time and temperature being inversely related whereby said composition seals and anodized component through hydration and simultaneously primes the anodized component; and (c) curing the sealed and primed component.
Claim 12
Dependent Claim
47 words
The process according to claim 9, wherein said curing step is carried out at a temperature in the range of approximately 300° F. (148° C.) to 500° F. (260° C.) for a period ranging from 10 minutes to 1 minute, the time and temperature being inversely proportional.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-06 | 1988-11-05 | 1989-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-06 | 1992-11-05 | 1993-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-06 | 1996-11-05 | 1997-05-07 | $7700.00 | Window Closed / Lapsed |