US4515905A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for forming a catalyst and the catalytic product produced by the process
Assignee: Bekaert NV SA
•
Filing: 1983-11-04
•
Granted: 1985-05-07
•
Expires: 2003-11-04
Abstract
Abstract A catalyst comprising a metallic carrier having a catalytically active metal-containing surface layer, the catalytic metal being other than a noble metal, wherein the catalytically active metal-containing surface layer is formed directly on the carrier by an etching treatment with an oxidizing inorganic acid which at least partially removes one or more metals from the surface of the metallic carrier, followed by chemical reduction with hydrogen.
Inventors
- 👤 Jan Uytterhoeven
- 👤 Pierre Jacobs
- 👤 Ludo Adriaensen
- 👤 Jan Geerts
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:48
CPC Classifications
B; B01; B01J; B01J35/00; B01J35/50; B01J35/58; B01J23/00; B01J23/70; B01J23/74; B01J23/745; B01J37/00; B01J37/02; B01J37/0215; B01J37/0225
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
152 words
A process for forming a catalyst having great heat conductivity and mechanical strength comprising a metallic carrier having a catalytically active metal-containing surface layer, the catalytic metal being other than a noble metal, including the steps of: (a) taking wires comprised of a first non-noble metal to provide a carrier therefrom, (b) initially coating said carrier with a matrix comprised of a second non-noble metal, (c) subsequently diffusing said non-noble metal of said matrix into an underlying layer of said carrier by heating and drawing said wires thereby forming reduced diameter fibers, (d) etching with an inorganic oxidizing acid as much as possible said matrix from the surface of said carrier thus exposing and oxidizing said underlying carrier layer, and, (e) subsequently reducing said exposed oxidized carrier layer at a temperature sufficient to reduce said metals in said oxidized layer to form said catalytically active metal-containing surface layer on said metallic carrier.
Claim 2
Dependent Claim
152 words
A process for forming a catalyst having great heat conductivity and mechanical strength comprising a metallic carrier having a catalytically active metal-containing surface layer, the catalytic metal being other than a noble metal, including the steps of: (a) taking wires comprised of a first non-noble metal to provide a carrier therefrom, (b) initially coating said carrier with a matrix comprised of a second non-noble metal, (c) subsequently diffusing said non-noble metal of said matrix into an underlying layer of said carrier by heating and drawing said wires thereby forming reduced diameter fibers, (d) etching with an inorganic oxidizing acid as much as possible said matrix from the surface of said carrier thus exposing and oxidizing said underlying carrier layer, and, (e) subsequently reducing said exposed oxidized carrier layer at a temperature sufficient to reduce said metals in said oxidized layer to form said catalytically active metal-containing surface layer on said metallic carrier.
Claim 3
Dependent Claim
42 words
A process as in claim 1, including the additional steps of: (a) bundling a plurality of said coated wires (b) enveloping said bundled coated wires in a metallic sheet, and (c) transforming said bundled, enveloped wires into fibers by heating and drawing.
Claim 4
Dependent Claim
31 words
A process as in claim 1, including the additional step of: (a) transforming said reduced diameter fibers into any one of a gauze, felt or web prior to said etching treatment.
Claim 5
Dependent Claim
29 words
A process as in claim 3, including the additional step of: (a) forming any one of said gauze, felt or web by sintering said fibers at their contacting surfaces.
Claim 6
Dependent Claim
28 words
A process as in claim 1, including the additional step of: (a) treating the surface of said etched carrier with an alkaline solution prior to said reducing step.
Claim 7
Dependent Claim
25 words
A process as in claim 5, including: (a) treating said surface of said etched carrier with an alkaline hydroxide solution prior to said reducing step.
Claim 8
Dependent Claim
15 words
A process as in claim 1, including: (a) performing said etching treatment with nitric acid.
Claim 9
Dependent Claim
24 words
A process as in claim 1, including: (a) selecting said non-noble metal of said carrier from the group consisting of titanium, iron and chromium.
Claim 10
Dependent Claim
28 words
A process as in claim 8, including: (a) selecting titanium as said non-noble metal of said carrier, and (b) selecting iron as said non-noble metal of said coating.
Claim 11
Dependent Claim
15 words
A process as in claim 1, including: (a) selecting a carrier comprised of an alloy.
Claim 12
Dependent Claim
29 words
A process as in claim 10, including: (a) selecting a carrier comprised of an alloy of iron, chromium, aluminum and yttrium, and (b) selecting a coating comprised of copper.
Claim 13
Dependent Claim
10 words
The catalytic product produced by the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-06 | 1988-11-05 | 1989-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-06 | 1992-11-05 | 1993-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-06 | 1996-11-05 | 1997-05-07 | $7700.00 | Window Closed / Lapsed |