Abstract
Abstract A method for applying a blown polyurethane coating to carpeting or other sheet material. The method includes the step of adding a filler to the polyurethane components to assure that the liquid does not unduly penetrate porous goods. The mixed polyurethane components are then placed in a puddle on the sheet material and leveled to a uniform coating. Steam is passed through the sheet material and the coating to initiate the reaction of the components. The steam also adds water to the coating, so the formulation is such that additional water is needed, and the needed water is added by the steaming. After the polyurethane has completed blowing, and before the polyurethane has cured beyond its plastic state, the foam may be compressed to decrease the thickness. A second sheet of material can be placed over the polyurethane to prevent the polyurethane from adhering to the compressing roller.
Inventors
- 👤 Paul Walker
- 👤 Glen F. Hamrick
- 👤 B. Lamar Sosebee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:42
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/3415; B29C44/3426; B29C44/20; B29C44/32; B29C44/321; B29C44/36; B29C44/46; B29C44/467; D; D06; D06N; D06N3/00; D06N3/12; D06N3/14; D06N7/00; D06N7/0063; D06N7/0071; D06N7/0086; D06N2203/00; D06N2203/06; D06N2203/068; D06N2205/00; D06N2205/20; D06N2207/00; D06N2207/04
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
155 words
A method for forming a blown polyurethane coating on porous sheet material, said polyurethane coating being formed by reaction of urethane forming components including at least a polyol, an isocyanate and water, said reaction requiring heat for initiation, said method including the steps of cooling said components to a temperature substantially below the temperature for initiation of the reaction, preparing a formulation of said urethane forming components having an excess of the isocyanate relative to the water compared to the desired coating formulation to provide a liquid mix, placing a quantity of said liquid mix on said porous sheet material in a puddle, leveling said puddle to provide a uniform coating of said liquid mix on said porous sheet material, passing steam through said sheet material and into said uniform coating for adding water to said liquid mix for reaction with said excess of isocyanate and for heating said liquid mix to start said reaction.
Claim 2
Independent Claim
155 words
A method for forming a blown polyurethane coating on porous sheet material, said polyurethane coating being formed by reaction of urethane forming components including at least a polyol, an isocyanate and water, said reaction requiring heat for initiation, said method including the steps of cooling said components to a temperature substantially below the temperature for initiation of the reaction, preparing a formulation of said urethane forming components having an excess of the isocyanate relative to the water compared to the desired coating formulation to provide a liquid mix, placing a quantity of said liquid mix on said porous sheet material in a puddle, leveling said puddle to provide a uniform coating of said liquid mix on said porous sheet material, passing steam through said sheet material and into said uniform coating for adding water to said liquid mix for reaction with said excess of isocyanate and for heating said liquid mix to start said reaction.
Claim 3
Dependent Claim
62 words
A method as claimed in claim 1, and further including the steps of applying a detackifying means to the surface of the polyurethane, and compressing the polyurethane to reduce the thickness of the polyurethane, the application of detackifying means and the compressing being carried out after the liquid mix has completed blowing and before the polyurethane has cured beyond its plastic state.
Claim 4
Dependent Claim
48 words
A method as claimed in claim 1, said sheet material comprising porous textile goods, said method further including the step of adding a filler to said formulation for thickening said liquid mix for causing said liquid mix to remain substantially on the surface of said porous textile goods.
Claim 5
Dependent Claim
62 words
A method as claimed in claim 3, and further including the steps of applying a detackifying means to the surface of the polyurethane, and compressing the polyurethane to reduce the thickness of the polyurethane, the application of detackifying means and the compressing being carried out after the liquid mix has completed blowing and before the polyurethane has cured beyond its plastic state.
Claim 6
Dependent Claim
53 words
A method as claimed in claim 4, said porous textile goods consisting of tufted carpeting comprising a primary backing and face yarns tufted thereinto, the step of adding a filler to said formulation including adding sufficient filler to prevent said liquid mix from passing through said primary backing and into said face yarns.
Claim 7
Dependent Claim
54 words
A method as claimed in claim 5, said steps of applying a detackifying means and compressing the polyurethane being performed generally simultaneously by passing a second sheet of material over a compression roll so that said second sheet of material adheres to the polyurethane and prevents adherence of said compression roll to the polyurethane.
Claim 8
Dependent Claim
16 words
A method as claimed in claim 6, said second sheet of material consisting of polyethylene film.
Claim 9
Dependent Claim
17 words
A method as claimed in claim 6, said second sheet of material consisting of a textile fabric.
Claim 10
Dependent Claim
44 words
A method as claimed in claim 6, said second sheet of material consisting of a secondary backing for said tufted carpeting, and further including the step of compressing the polyurethane to the extent that said secondary backing is substantially adhered to said primary backing.
Claim 11
Dependent Claim
40 words
A method as claimed in claim 1, the step of leveling said puddle including the steps of placing a doctor blade above said sheet material for leveling said puddle, and passing a sheet of perforate material over said doctor blade.
Claim 12
Dependent Claim
65 words
A method as claimed in claim 1, and further including the steps of directing said sheet material along a path having an upwardly inclined portion, said puddle being formed on said upwardly inclined portion, said step of leveling said puddle being carried out by using an air knife with the blade directed above said puddle at an angle with respect to said upwardly inclined portion.
Claim 13
Dependent Claim
14 words
A method as claimed in claim 2, said detackifying means consisting of tufted carpeting.
Claim 14
Dependent Claim
25 words
A method as claimed in claim 1, said excess of isocyanate consisting of approximately five parts of isocyanate for each one hundred parts of polyol.
Claim 15
Dependent Claim
24 words
A method as claimed in claim 1, said excess of isocyanate consisting of from approximately 5% to approximately 15% increase over said desired formulation.
Claim 16
Dependent Claim
35 words
A method as claimed in claim 3, wherein the step of adding a filler to said formulation includes adding between approximately one and approximately two hundred fifty parts filler for each one hundred parts polyol.
Claim 17
Dependent Claim
26 words
A method as claimed in claim 15, wherein said filler is selected from the group consisting of barium sulphate, calcium carbonate, alumina trihydrate, clay and starch.
Claim 18
Dependent Claim
14 words
A method as claimed in claim 15 wherein said filler consists of calcium carbonate.
References Cited (Backward Citations)
US3518102A
Cited
US3519526A
Cited
US3926700A
Cited
US3705834A
Cited
US4132817A
Cited
US4171395A
Cited
US4239821A
Cited
US4278482A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-06 | 1988-11-05 | 1989-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-06 | 1992-11-05 | 1993-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-06 | 1996-11-05 | 1997-05-07 | $7700.00 | Window Closed / Lapsed |