Method for forming a layer of blown cellular urethane on a carpet backing
Assignee: Textile Rubber and Chemical Co Inc
•
Filing: 1978-01-25
•
Granted: 1979-01-02
•
Expires: 1998-01-25
Abstract
Abstract A method of forming a layer of blown cellular urethane on a primary carpet backing comprising the steps of preparing a mixture of reactive urethane forming agents, controlling the temperature of the reactive mixture, shaping the reactive mixture into a layer upon a latex film, heating the urethane forming mixture to initiate chemical blowing of the mixture, applying the underside of a previously tufted and heated primary carpet backing directly to the upper surface of the mixture, heating the mixture to a predetermined temperature, applying pressure to the carpet and mixture and stripping the carpet and cellular urethane layer from the conveyor belt.
Inventors
- 👤 John G. Tillotson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:13
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/245; B32B37/00; B32B37/10; B32B37/1027; B32B5/18; B32B5/20; D; D06; D06N; D06N7/00; D06N7/0063; D06N7/0071; D06N7/0073; D06N7/0086; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2266/0278; B32B2305/00; B32B2305/02; B32B2471/00; B32B2471/02; D06N2203/00; D06N2203/04; D06N2203/041; D06N2203/06; D06N2203/068; D06N2205/00; D06N2205/04; D06N2207/00; D06N2207/08; Y; Y10; Y10T; Y10T156/00; Y10T156/17; Y10T156/1702; Y10T156/1712; Y10T156/1741; Y10T428/00; Y10T428/23907; Y10T428/23979; Y10T428/23993; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249991
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
192 words
Method of forming a layer of blown cellular urethane on a carpet backing fabric comprising the steps of: (a) preparing a mixture of reactive urethane forming agents containing sufficient water to cause chemical blowing of the mixture when heated sufficiently, and controlling the temperature of the mixture to a temperature of between about 60° and 100° F.; (b) providing an endless conveyor belt; (c) applying an elastomeric film to said conveyor belt; (d) depositing the mixture of reactive urethane forming agents onto the film and conveyor belt while the temperature of the film and belt are controlled as to temperature; (e) preheating the lower surface of an uncoated carpet material to a temperature of between 100° and 300° F.; (f) heating the urethane forming mixture to cause chemical blowing thereof and bringing the lower surface of the preheated carpet into flush contact with the heated urethane forming mixture; (g) applying pressure to the carpet material while the reactive mixture is undergoing chemical blowing; (h) heating the urethane forming mixture after the preheated carpet is brought into flush contact with the mixture; and (i) stripping the coated carpet material from the conveyor belt.
Claim 2
Dependent Claim
192 words
Method of forming a layer of blown cellular urethane on a carpet backing fabric comprising the steps of: (a) preparing a mixture of reactive urethane forming agents containing sufficient water to cause chemical blowing of the mixture when heated sufficiently, and controlling the temperature of the mixture to a temperature of between about 60° and 100° F.; (b) providing an endless conveyor belt; (c) applying an elastomeric film to said conveyor belt; (d) depositing the mixture of reactive urethane forming agents onto the film and conveyor belt while the temperature of the film and belt are controlled as to temperature; (e) preheating the lower surface of an uncoated carpet material to a temperature of between 100° and 300° F.; (f) heating the urethane forming mixture to cause chemical blowing thereof and bringing the lower surface of the preheated carpet into flush contact with the heated urethane forming mixture; (g) applying pressure to the carpet material while the reactive mixture is undergoing chemical blowing; (h) heating the urethane forming mixture after the preheated carpet is brought into flush contact with the mixture; and (i) stripping the coated carpet material from the conveyor belt.
Claim 3
Dependent Claim
35 words
The method of claim 1 wherein step (c) includes coating the conveyor belt with a layer of liquid latex material and drying said layer to form a latex film, in situ, on the conveyor belt.
Claim 4
Dependent Claim
42 words
The method of claim 1 wherein chilled, dry air is blown onto the conveyor belt so as to bring the temperature of the conveyor belt to approximately 50° to 100° F. before the urethane forming mixture is deposited onto the latex film.
Claim 5
Dependent Claim
88 words
The method of claim 1 wherein: the conveyor belt is tensioned by applying a linear force of approximately 1 to 10 pounds; the conveyor belt is flattened as the urethane forming mixture is deposited onto the belt; the urethane forming mixture is spread into a uniform layer by means of an air knife; the temperature of the air in said air knife is controlled to approximately 50° to 100° F.; and the pressure of the air in said air knife is controlled to approximately 2 to 60 ounces.
Claim 6
Dependent Claim
51 words
The method of claim 4 wherein: the conveyor belt is tensioned by applying a linear force of 5 pounds; the temperature of the air in said air knife is controlled to 65° F; and the pressure of the air in said air knife is controlled to approximately 6 to 24 ounces.
Claim 7
Dependent Claim
41 words
The method of claim 1 wherein a heated platen is disposed below the conveyor belt to heat the urethane forming mixture to approximately 90° to 150° F. before said preheated carpet is brought into flush contact with the urethane forming mixture.
Claim 8
Dependent Claim
34 words
The method of claim 6 wherein said heated platen heats the urethane forming mixture to approximately 110° to 130° F. before said preheated carpet is brought into flush contact with the urethane forming mixture.
Claim 9
Dependent Claim
29 words
The method of claim 1 wherein a pressure blanket is applied to the upper surface of the carpet at a force of 0.2 to 5 ounces per square inch.
Claim 10
Dependent Claim
29 words
The method of claim 8 wherein said pressure blanket is applied to the upper surface of the carpet at a force of 1 to 2 ounces per square inch.
Claim 11
Dependent Claim
43 words
The method of claim 1 wherein heated platens are disposed below the conveyor belt to heat the urethane forming mixture to a temperature of about 120° to 200° F. during chemical blowing of the mixture and to about 150° to 300° F. thereafter.
Claim 12
Dependent Claim
42 words
The method of claim 10 wherein: said heated platens heat the urethane forming mixture to a temperature of about 140° to 150° F. during the chemical blowing of the mixture; and the mixture is heated to about 250° to 300° F. thereafter.
Claim 13
Dependent Claim
23 words
The method of claim 1 wherein the conveyor belt follows a path which is substantially convex during curing of the urethane forming agents.
Claim 14
Dependent Claim
46 words
The method of claim 1 wherein pressure is applied to the upper surface of the carpet after the mixture has substantially completed its chemical blowing but before the reactive mixture has cured by means of passing the upper surface of the carpet under a gauge roller.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-01-01 | 1982-07-03 | 1983-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-01-01 | 1986-07-03 | 1987-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-01-01 | 1990-07-03 | 1991-01-02 | $7700.00 | Window Closed / Lapsed |