Method for coating a semiconductor device with a phosphosilicate glass
Assignee: Fujitsu Ltd
•
Filing: 1983-08-01
•
Granted: 1985-04-23
•
Expires: 2003-08-01
Abstract
Abstract A semiconductor device having a deposited phosphosilicate glass film, containing an insubstantial amount of hydrogen and a low phosphorus concentration, is manufactured at a high mass productivity. This semiconductor device is manufactured by first placing plural substrates for semiconductor devices to be treated in a reaction tube so that the main surfaces of the substrates are substantially vertically aligned with respect to one another and are substantially perpendicularly intersected by the central axis of the reaction tube, the reaction tube being provided with at least two gas feed pipes having plural small openings pierced along the longitudinal direction thereof. Second, a silicon compound gas is introduced through one of the gas feed pipes into the reaction tube and an oxidizing gas is introduced through the other of the gas feed pipes into the reaction tube, while the inside of the reaction tube is maintained a reduced low pressure, whereby phosphosilicate glass films are deposited on the main surfaces of the substrates.
Inventors
- 👤 Hidekazu Miyamoto
- 👤 Yoshimi Shioya
- 👤 Mamoru Maeda
- 👤 Mikio Takagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 15:47
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/455; C23C16/45514; C23C16/45563; C23C16/45578; H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6923
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
259 words
A method for manufacturing semiconductor devices in a reaction tube provided with a gas inlet adjacent one end of the reaction tube, a gas outlet adjacent the opposite end of the reaction tube and at least two gas feed pipes having plural small openings pierced along the longitudinal direction thereof, comprising the steps of: (a) positioning plural substrates for the semiconductor devices to be treated in the reaction tube so that the main surfaces of the plural substrates are substantially vertically aligned with respect to one another and are substantially perpendicularly intersected by the longitudinal axis of the reaction tube; (b) introducing a silicon compound gas including a phosphorus compound gas through one of the at least two gas feed pipes having plural small openings into the reaction tube and introducing an oxidizing gas through the other of the at least two gas feed pipes out the plural small openings into the reaction tube, while maintaining the inside of the reaction tube under a reduced pressure by evacuating the inside of the reaction tube through the gas outlet; and (c) introducing a gas into the reaction tube through the gas inlet to establish a gas flow, for the gases introduced into the reaction tube in said steps (b) and (c), in a direction along the longitudinal axis of the reaction tube from the gas inlet, via the periphery of the plural substrates, toward the gas outlet to expose the plural substrates to the gas flow, whereby phosphosilicate glass films are deposited on the main surfaces of the plural substrates.
Claim 2
Independent Claim
259 words
A method for manufacturing semiconductor devices in a reaction tube provided with a gas inlet adjacent one end of the reaction tube, a gas outlet adjacent the opposite end of the reaction tube and at least two gas feed pipes having plural small openings pierced along the longitudinal direction thereof, comprising the steps of: (a) positioning plural substrates for the semiconductor devices to be treated in the reaction tube so that the main surfaces of the plural substrates are substantially vertically aligned with respect to one another and are substantially perpendicularly intersected by the longitudinal axis of the reaction tube; (b) introducing a silicon compound gas including a phosphorus compound gas through one of the at least two gas feed pipes having plural small openings into the reaction tube and introducing an oxidizing gas through the other of the at least two gas feed pipes out the plural small openings into the reaction tube, while maintaining the inside of the reaction tube under a reduced pressure by evacuating the inside of the reaction tube through the gas outlet; and (c) introducing a gas into the reaction tube through the gas inlet to establish a gas flow, for the gases introduced into the reaction tube in said steps (b) and (c), in a direction along the longitudinal axis of the reaction tube from the gas inlet, via the periphery of the plural substrates, toward the gas outlet to expose the plural substrates to the gas flow, whereby phosphosilicate glass films are deposited on the main surfaces of the plural substrates.
Claim 3
Dependent Claim
38 words
A method as claimed in claim 1, wherein said silicon compound gas introducing step comprises introducing monosilane (SiH 4 ) and phosphine (PH 3 ) and wherein said oxidizing gas introducing step comprises introducing oxygen (O 2 ).
Claim 4
Dependent Claim
28 words
A method as claimed in claim 2, wherein the mol ratio of phosphine to phosphine and monosilane (PH 3 /PH 3 +SiH 4 ) is 0.08 or less.
Claim 5
Dependent Claim
29 words
A method as claimed in claim 2, wherein the mol ratio of oxygen to phosphine and monosilane (O 2 /PH 3 +SiH 4 ) is from 2 to 3.
Claim 6
Dependent Claim
29 words
A method as claimed in claim 3, wherein the mol ratio of phosphine to phosphine and monosilane (PH 3 /PH 3 +SiH 4 ) is from 0.03 to 0.08.
Claim 7
Dependent Claim
29 words
A method as claimed in claim 3, wherein the mol ratio of oxygen to phosphine and monosilane (O 2 /PH 3 +SiH 4 ) is from 2 to 3.
Claim 8
Dependent Claim
16 words
A method as claimed in claim 1, wherein the reduced low pressure is from 0.1-0.2 torr.
Claim 9
Dependent Claim
13 words
A method as claimed in claim 1, further comprising heating the reaction tube.
Claim 10
Dependent Claim
22 words
A method as claimed in claim 8, wherein the reaction tube is heated in a range from 425° C. to 450° C.
References Cited (Backward Citations)
US4005240A
Cited
US4196232A
Cited
US4098923A
Cited
US4033286A
Cited
JPS5358760A
Cited
JPS54125979A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-22 | 1988-10-22 | 1989-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-22 | 1992-10-22 | 1993-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-22 | 1996-10-22 | 1997-04-23 | $7700.00 | Window Closed / Lapsed |