US4512829A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing printed circuit boards
Assignee: Satosen Co Ltd
•
Filing: 1984-04-06
•
Granted: 1985-04-23
•
Expires: 2004-04-06
Abstract
Abstract This invention provides a process for producing a printed circuit board characterized by the steps of drilling holes in a copper clad laminate, treating the entire surface of the laminate including the hole-defining inner surfaces with a catalyst, removing the catalyst from the surface of the copper foil of the laminate by mechanically cleaning the surface of the copper foil, depositing electroless nickel only on the hole-defining inner surfaces, forming a pattern with an etching resist, etching away the copper foil except at the pattern area, removing the etching resist, masking with a solder resist the entire surface except at the hole-defining inner surfaces and the lands, and subjecting the hole-defining inner surfaces and the lands to electroless copper plating.
Inventors
- 👤 Hideo Ohta
- 👤 Tatuzo Hakuzen
- 👤 Yasunori Ito
- 👤 Fusao Takagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:23
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/243; H05K3/40; H05K3/42; H05K3/425; H05K3/427; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0344; H05K2201/09; H05K2201/09209; H05K2201/09654; H05K2201/09736; H05K2203/00; H05K2203/02; H05K2203/025; H05K2203/05; H05K2203/0562; H05K2203/0571; H05K3/10; H05K3/18; H05K3/181; H05K3/187; H05K3/28; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
117 words
A process for producing a printed circuit board characterized by the steps of drilling holes in a copper clad laminate, treating the entire surface of the laminate including the hole-defining inner surfaces with a catalyst, removing the catalyst from the surface of the copper foil of the laminate by mechanically cleaning the surface of the copper foil, depositing electroless nickel only on the hole-defining inner surfaces, forming a pattern with an etching resist, etching away the copper foil except at the pattern area, removing the etching resist, masking with a solder resist the entire surface except at the hole-defining inner surfaces and the lands, and subjecting the hole-defining inner surfaces and the lands to electroless copper plating.
Claim 2
Dependent Claim
117 words
A process for producing a printed circuit board characterized by the steps of drilling holes in a copper clad laminate, treating the entire surface of the laminate including the hole-defining inner surfaces with a catalyst, removing the catalyst from the surface of the copper foil of the laminate by mechanically cleaning the surface of the copper foil, depositing electroless nickel only on the hole-defining inner surfaces, forming a pattern with an etching resist, etching away the copper foil except at the pattern area, removing the etching resist, masking with a solder resist the entire surface except at the hole-defining inner surfaces and the lands, and subjecting the hole-defining inner surfaces and the lands to electroless copper plating.
Claim 3
Dependent Claim
81 words
A process as defined in claim 1 wherein the electroless nickel is deposited only on the hole-defining inner surfaces with use of an electroless nickel plating bath containing about 3 to about 9 g/l of a nickel salt calculated as nickel, about 15 to about 30 g/l of sodium citrate and about 30 to about 50 g/l of sodium hypophosphite and having a pH of about 2.1 to about 2.6 and a bath temperature of about 65° to about 75° C.
Claim 4
Dependent Claim
23 words
A process as defined in claim 1 wherein the electroless nickel is deposited to the thickness of about 0.3 to about 1 μm.
Claim 5
Dependent Claim
32 words
A process as defined in claim 1 wherein the electroless copper plating is deposited on the hole-defining inner surfaces and the lands to the thickness of about 20 to about 35 μm.
Claim 6
Dependent Claim
139 words
A process for subjecting a copper clad laminate to electroless nickel plating limitedly only on the inner surfaces defining holes formed therein, the process being characterized by the steps of depositing catalyst on the entire surface of the laminate including the hole-defining inner surfaces, removing catalyst from the surface of the copper foil on the laminate by mechanically cleaning the surface of the copper foil to leave catalyst only on the hole-defining inner surfaces and immersing the resulting laminate in an electroless nickel plating bath at a temperature of about 65° to about 75° C., the plating bath comprising about 3 to about 9 g/l of a nickel salt calculated as nickel, 15 to 30 g/l of sodium citrate and about 30 to about 50 g/l of sodium hypophosphite and having a pH of about 2.1 to about 2.6.
Claim 7
Dependent Claim
139 words
A process for subjecting a copper clad laminate to electroless nickel plating limitedly only on the inner surfaces defining holes formed therein, the process being characterized by the steps of depositing catalyst on the entire surface of the laminate including the hole-defining inner surfaces, removing catalyst from the surface of the copper foil on the laminate by mechanically cleaning the surface of the copper foil to leave catalyst only on the hole-defining inner surfaces and immersing the resulting laminate in an electroless nickel plating bath at a temperature of about 65° to about 75° C., the plating bath comprising about 3 to about 9 g/l of a nickel salt calculated as nickel, 15 to 30 g/l of sodium citrate and about 30 to about 50 g/l of sodium hypophosphite and having a pH of about 2.1 to about 2.6.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-22 | 1988-10-22 | 1989-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-22 | 1992-10-22 | 1993-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-22 | 1996-10-22 | 1997-04-23 | $7700.00 | Window Closed / Lapsed |