Solar-selective layers and method for producing same
Assignee: Hoechst AG
•
Filing: 1982-09-29
•
Granted: 1985-04-16
•
Expires: 2002-09-29
Abstract
Abstract An improved solar-selective layer and method for producing the same on suitable substrates is discussed. In accordance with this invention, a metal layer is first of all deposited on a suitable substrate of a collector and is then oxidized at elevated temperature and pressure.
Inventors
- 👤 Boy Cornils
- 👤 Jurgen Weber
- 👤 Bela Tihanyi
- 👤 Werner DeWin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:50
CPC Classifications
C; C23; C23C; C23C26/00; C23C8/00; C23C8/06; C23C8/08; C23C8/10; F; F24; F24S; F24S70/00; F24S70/20; F24S70/225; F24S70/25; Y; Y02; Y02E; Y02E10/00; Y02E10/40; Y10; Y10S; Y10S126/00; Y10S126/907; Y10S126/908
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
69 words
A method for producing solar-selective layers on a converter for converting solar radiation into thermal energy by means of a metal oxide layer applied to the surface of said converter which includes the steps of depositing a metal layer on the surface of said converter and then oxidizing said layer at a temperature of between 100° C. and 400° C. and a pressure of between 50 and 250 bars.
Claim 2
Independent Claim
69 words
A method for producing solar-selective layers on a converter for converting solar radiation into thermal energy by means of a metal oxide layer applied to the surface of said converter which includes the steps of depositing a metal layer on the surface of said converter and then oxidizing said layer at a temperature of between 100° C. and 400° C. and a pressure of between 50 and 250 bars.
Claim 3
Dependent Claim
15 words
Method according to claim 1 in which the oxidizing is effected with an oxidizing gas.
Claim 4
Dependent Claim
16 words
Method according to claim 1 in which the oxidizing is effected with an oxidizing gas mixture.
Claim 5
Dependent Claim
14 words
Method according to claim 1 in which the oxidizing is effected with pure oxygen.
Claim 6
Dependent Claim
19 words
Method according to claim 1 in which said metal layer is chosen from the group of nickel or cobalt.
Claim 7
Dependent Claim
13 words
Method according to claim 1 in which said metal layer is electrolytically deposited.
Claim 8
Dependent Claim
50 words
In an apparatus for converting solar energy into heat, in which a converter is provided with a heat-absorbing surface, the improvement comprising a metal layer deposited on said surface, said layer having been oxidized at temperatures between 100° C. and 400° C. and pressure of between 50 and 250 bars.
Claim 9
Dependent Claim
50 words
In an apparatus for converting solar energy into heat, in which a converter is provided with a heat-absorbing surface, the improvement comprising a metal layer deposited on said surface, said layer having been oxidized at temperatures between 100° C. and 400° C. and pressure of between 50 and 250 bars.
Claim 10
Dependent Claim
20 words
An apparatus according to claim 7 in which said metal layer is chosen from the group of nickel or cobalt.
References Cited (Backward Citations)
US31339A
Cited
US3944440A
Cited
US4119761A
Cited
US4235226A
Cited
US4104134A
Cited
JPS54153348A
Cited
US4239604A
Cited
US4189331A
Cited
US4228220A
Cited
DE2843571A1
Cited
US4392920A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-15 | 1988-10-15 | 1989-04-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-15 | 1992-10-15 | 1993-04-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-15 | 1996-10-15 | 1997-04-16 | $7700.00 | Window Closed / Lapsed |