Compositions and method of preparation by chlorosulfonation of difficultly sulfonatable poly(ether sulfone)
Assignee: Albany International Corp
•
Filing: 1983-09-22
•
Granted: 1985-04-02
•
Expires: 2003-09-22
Abstract
Abstract Novel chlorosulfonated polyarylethersulfones derived by controlled treatment with chlorosulfonic acid of difficultly sulfonatable polyarylethersulfone of recurring units of the formula: ##STR1## wherein Ar 1 and Ar 2 represent phenylene or phenylene substituted with non-deactivating groups where Ar 1 and Ar 2 may be the same or different are described with the method of their preparation. The partially sulfonated-sulfochlorinated polyarylethersulfones may be subsequently converted to cation-exchange materials or ion-exchange materials with mixed cation and anion exchange sites.
Inventors
- 👤 Benjamin Bikson
- 👤 Myron J. Coplan
- 👤 Gertrud Gotz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:45
CPC Classifications
C; C08; C08G; C08G75/00; C08G75/20; C08G75/23; B; B01; B01J; B01J39/00; B01J39/08; B01J39/16; B01J39/18; C08G65/00; C08G65/34; C08G65/48
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
122 words
A chlorosulfonated polyarylethersulfone resin which may be linear or branched and which comprises a plurality of repeating units of the formula: ##STR4## wherein Ar 1 and Ar 2 each represent phenylene or phenylene partially substituted with non-deactivating groups and where Ar 1 and Ar 2 may be the same or different and wherein some of the phenylene moieties are also substituted with hydroxysulfonyl groups and some of the phenylene moieties are also substituted with chlorosulfonyl groups, the ratio of chlorosulfonyl groups to hydroxysulfonyl groups being within the range of from 0.01-20:1 while the combined contents of both hydroxysulfonyl and chlorosulfonyl groups in the above mentioned polymer range from about 0.05 to about 4 milliequivalents per gram of dry resin; L represents oxygen.
Claim 2
Dependent Claim
122 words
A chlorosulfonated polyarylethersulfone resin which may be linear or branched and which comprises a plurality of repeating units of the formula: ##STR4## wherein Ar 1 and Ar 2 each represent phenylene or phenylene partially substituted with non-deactivating groups and where Ar 1 and Ar 2 may be the same or different and wherein some of the phenylene moieties are also substituted with hydroxysulfonyl groups and some of the phenylene moieties are also substituted with chlorosulfonyl groups, the ratio of chlorosulfonyl groups to hydroxysulfonyl groups being within the range of from 0.01-20:1 while the combined contents of both hydroxysulfonyl and chlorosulfonyl groups in the above mentioned polymer range from about 0.05 to about 4 milliequivalents per gram of dry resin; L represents oxygen.
Claim 3
Dependent Claim
34 words
A sulfonated polyarylethersulfone that is the product of the hydrolysis of the resin of claim 1, that contains from 0.05 to 4 milliequivalents per gram of hydroxysulfonyl radicals in the form of free acid.
Claim 4
Dependent Claim
21 words
A sulfonated polysulfone according to claim 2 which is in the form of an ammonium salt or alkaline earth metal salt.
Claim 5
Dependent Claim
76 words
The product obtained upon reaction of the resin of claim 1 with primary or secondary mono or poly functional amines to give an ion exchange resin material with mixed strong cation exchange and weak anion exchange sites, the ratio of the sulfonic acid groups to the weakly anionic ones being varied from 0.05 to 25 with the degree of substitution of the aromatic rings with both strong cationic and anionic sites ranging from 0.05 to 0.6.
Claim 6
Dependent Claim
45 words
An ion exchange resin with mixed strong cationic and weak anionic groups according to claim 4 that is reacted with haloalkanes to yield an ion exchange resin with mixed strong cation exchange sites and strong anion exchange sites in the form of quaternary ammonium groups.
Claim 7
Dependent Claim
23 words
A semipermeable composite membrane comprising a thin semipermeable film of the resin of claim 1 deposited on one side of a microporous substrate.
Claim 8
Dependent Claim
101 words
A process for the chlorosulfonation of a poly(ether sulfone) containing repeating units of the formula; ##STR5## wherein Ar 1 and Ar 2 each represent phenylene or phenylene partially substituted with non-deactivating groups and where Ar 1 and Ar 2 may be the same or different; L represents oxygen, which comprises: chlorosulfonating said poly(ether sulfone) dissolved in an inert organic solvent with chlorosulfonic acid under homogenous reaction conditions at a temperature within the range of from 40° C. to 151° C., the proportion of chlorosulfonic acid employed being within the range of 0.2 to 10 moles per mole of poly(ether sulfone) reactant.
Claim 9
Dependent Claim
101 words
A process for the chlorosulfonation of a poly(ether sulfone) containing repeating units of the formula; ##STR5## wherein Ar 1 and Ar 2 each represent phenylene or phenylene partially substituted with non-deactivating groups and where Ar 1 and Ar 2 may be the same or different; L represents oxygen, which comprises: chlorosulfonating said poly(ether sulfone) dissolved in an inert organic solvent with chlorosulfonic acid under homogenous reaction conditions at a temperature within the range of from 40° C. to 151° C., the proportion of chlorosulfonic acid employed being within the range of 0.2 to 10 moles per mole of poly(ether sulfone) reactant.
Claim 10
Dependent Claim
14 words
A membrane prepared from the poly(ether sulfone) chlorosulfonated by the process of claim 7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-01 | 1988-10-01 | 1989-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-01 | 1992-10-01 | 1993-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-01 | 1996-10-01 | 1997-04-02 | $7700.00 | Window Closed / Lapsed |