Press-molding process for preparing a powder compact
Assignee: Brother Industries Ltd
•
Filing: 1982-06-24
•
Granted: 1985-04-02
•
Expires: 2002-06-24
Abstract
Abstract A flux-path forming member of a motor is prepared from a mixture mass by evenly mixing up to 4% of a thermosetting resin binder and molybdenum disulfide with at least 96% of a metal powder, fibrous metal, or a combination thereof; a second step of compacting in a mold under pressure the mixture mass into a desired shape; and a third step of heating, concurrently with or subsequently to the second step, the mixture mass to an elevated temperature to cure the binder portion thereof. The compact prepared by the above process is also disclosed. The content of the thermosetting resin at least 0.2 percent by weight, and the content of the molybdenum disulfide is at least 0.1 percent by weight. The curing operation is conducted at a temperature not higher than 300 DEG C.
Inventors
- 👤 Shigeru Mizuno
- 👤 Masahiko Suzuki
- 👤 Haruki Mizuno
- 👤 Masutaro Katsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:46
CPC Classifications
H; H02; H02K; H02K1/00; H02K1/02; B; B22; B22F; B22F1/00; C; C22; C22C; C22C32/00; C22C32/0094; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49009
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
164 words
A flux-path forming member of a motor made of a compacted and cured mixture mass and having high radial crushing strength and density, said flux-path forming member being prepared by a process comprising: a first step of preparing a mixture mass by evenly mixing not less than 0.2 percent by weight of thermosetting resin binder and not less than 0.1 percent by weight of molybdenum disulfide with not less than 96 percent by weight of a major portion of said mixture mass, said major portion being a member selected from the group consisting of metal powder, fibrous metal, and a combination thereof, the total content of said thermosetting resin and said molybdenum disulfide being not more than 4 percent by weight; a second step of compacting in a mold under pressure said mixture mass into a predetermined shape; and a third step of heating, concurrently with or subsequently to said second step, said mass to an elevated temperature to cure the binder portion thereof.
Claim 2
Dependent Claim
164 words
A flux-path forming member of a motor made of a compacted and cured mixture mass and having high radial crushing strength and density, said flux-path forming member being prepared by a process comprising: a first step of preparing a mixture mass by evenly mixing not less than 0.2 percent by weight of thermosetting resin binder and not less than 0.1 percent by weight of molybdenum disulfide with not less than 96 percent by weight of a major portion of said mixture mass, said major portion being a member selected from the group consisting of metal powder, fibrous metal, and a combination thereof, the total content of said thermosetting resin and said molybdenum disulfide being not more than 4 percent by weight; a second step of compacting in a mold under pressure said mixture mass into a predetermined shape; and a third step of heating, concurrently with or subsequently to said second step, said mass to an elevated temperature to cure the binder portion thereof.
Claim 3
Dependent Claim
23 words
A flux-path forming member as recited in claim 1, wherein said third step is conducted at a temperature not higher than 300° C.
Claim 4
Dependent Claim
20 words
A flux-path forming member as recited in claim 2, wherein said elevated temperature ranges from 120° C. to 200° C.
Claim 5
Dependent Claim
17 words
A flux-path forming member as recited in claim 1, wherein said thermosetting resin binder is epoxy resin.
Claim 6
Dependent Claim
25 words
A flux-path forming member as recited in claim 1, wherein said fibrous metal consists of fibers having a length of between 0.5 and 10 mm.
Claim 7
Dependent Claim
123 words
A flux-path forming member of a motor made of a press-mold compacted and cured mixture mass and having high radial crushing strength and density, said compact comprising: not less than 0.2 percent by weight of thermosetting resin, not less than 0.1 percent by weight of molybdenum disulfide, the total content of said thermosetting resin and said molybdenum disulfide being not more than 4 percent by weight; and not less than 96 percent by weight of powdered and/or fibrous metal; a mixture mass of said thermosetting resin, molybdenum disulfide and powdered and/or fibrous metal being compacted in a mold under pressure into said compact, said thermosetting resin being cured at an elevated temperature concurrently with or subsequently to the compaction of said mixture mass.
Claim 8
Dependent Claim
123 words
A flux-path forming member of a motor made of a press-mold compacted and cured mixture mass and having high radial crushing strength and density, said compact comprising: not less than 0.2 percent by weight of thermosetting resin, not less than 0.1 percent by weight of molybdenum disulfide, the total content of said thermosetting resin and said molybdenum disulfide being not more than 4 percent by weight; and not less than 96 percent by weight of powdered and/or fibrous metal; a mixture mass of said thermosetting resin, molybdenum disulfide and powdered and/or fibrous metal being compacted in a mold under pressure into said compact, said thermosetting resin being cured at an elevated temperature concurrently with or subsequently to the compaction of said mixture mass.
Claim 9
Dependent Claim
16 words
A flux-path forming member as recited in claim 6, which constitutes a core of a motor.
Claim 10
Dependent Claim
16 words
A flux-path forming member as recited in claim 6, which constitutes a yoke of a motor.
Claim 11
Dependent Claim
24 words
A flux-path forming member as recited in claim 1, wherein in said second step, said pressure is at least about 6 tons/cm 2 .
References Cited (Backward Citations)
US3463047A
Cited
US3732617A
Cited
US4104176A
Cited
US4246316A
Cited
SU750584A1
Cited
SU765891A1
Cited
JPS5550605A
Cited
JPS5591803A
Cited
US4242398A
Cited
JPS55130103A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-04-01 | 1988-10-01 | 1989-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-04-01 | 1992-10-01 | 1993-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-04-01 | 1996-10-01 | 1997-04-02 | $7700.00 | Window Closed / Lapsed |