Bonding agent cold-hardening under the formation of polyurethane for molded parts, its manufacture and its application
Assignee: Centre for Higher Education
•
Filing: 1983-10-04
•
Granted: 1985-03-26
•
Expires: 2003-10-04
Abstract
Abstract This relates to a bonding agent which is used for the production of molded foundry parts and which is composed of two basic components which harden out cold in the mixture of the molded material in the presence of a catalyst under the formation of polyurethane. One basic component is a polyol in the form of a solution of a co-condensate containing an OH group consisting of phenol, aldehyde and an alkyl phenyl siloxane with a contents of at least 3% by weight in free OH groups, if applicable in mixture with a phenol aldehyde condensate containing an OH group, and the second basic component is a polyisocyanate likewise dissolved under normal conditions. Appropriately the solvent has a content in vegetable oils, preferably castor oil.
Inventors
- 👤 Marek A. Torbus
- 👤 Aleksandar Vujevic
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:32
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/42; B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/205; B22C1/22; B22C1/2233; B22C1/2273; B22C1/24; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/54; C08G18/542; C08G8/00; C08G8/28; C08G8/38
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
76 words
A bonding agent cold-hardening under the formation of polyurethane for the production of molded foundry parts, consisting essentially of a polyol in the form of a solution of a phenol aldehyde condensate containing an OH group and a polyisocyanate, wherein the phenol aldehyde condensate is replaced wholly or partly by a co-condensate consisting of phenols, aldehydes and a hydroxy functional alkyl phenyl siloxane with a content of at least 3% by weight of free OH groups.
Claim 2
Dependent Claim
76 words
A bonding agent cold-hardening under the formation of polyurethane for the production of molded foundry parts, consisting essentially of a polyol in the form of a solution of a phenol aldehyde condensate containing an OH group and a polyisocyanate, wherein the phenol aldehyde condensate is replaced wholly or partly by a co-condensate consisting of phenols, aldehydes and a hydroxy functional alkyl phenyl siloxane with a content of at least 3% by weight of free OH groups.
Claim 3
Dependent Claim
18 words
The bonding agent as defined in claim 1, wherein the polyol is in a solution containing vegetable oils.
Claim 4
Dependent Claim
48 words
A method for the production of the bonding agent as defined in claim 1, comprising the step of forming the polyol by condensation of phenols with aldehydes in the presence of 0.1 to 5% by weight, related to the final product, of the hydroxy functional alkyl phenyl siloxane.
Claim 5
Dependent Claim
49 words
The method as defined in claim 3 for the production of the bonding agent as defined in claim 2, comprising the additional step of picking up the obtained the co-condensate with a solvent which contains from 1 to 10% by weight, related to the final product, of vegetable oil.
Claim 6
Independent Claim
81 words
A method for the production of molded foundry parts which are treated with a water slur comprising the step of mixing foundry sand with a polyol in the form of a solution of a phenol aldehyde condensate containing an OH group and a polyisocyanate, wherein the phenol aldehyde condensate is replaced wholly or partly by a co-condensate consisting of phenols, aldehydes and a hydroxy functional alkyl phenol siloxane with a content of at least 3% by weight of free OH groups.
Claim 7
Independent Claim
81 words
A method for the production of molded foundry parts which are treated with a water slur comprising the step of mixing foundry sand with a polyol in the form of a solution of a phenol aldehyde condensate containing an OH group and a polyisocyanate, wherein the phenol aldehyde condensate is replaced wholly or partly by a co-condensate consisting of phenols, aldehydes and a hydroxy functional alkyl phenol siloxane with a content of at least 3% by weight of free OH groups.
Claim 8
Dependent Claim
15 words
The bonding agent as defined in claim 1 wherein the vegetable oil is castor oil.
Claim 9
Dependent Claim
19 words
The method for the production of a bonding agent of claim 4 wherein the vegetable oil is castor oil.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-25 | 1988-09-24 | 1989-03-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-25 | 1992-09-24 | 1993-03-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-25 | 1996-09-24 | 1997-03-26 | $7700.00 | Window Closed / Lapsed |