Fabricating shaped laminated transparencies
Assignee: PPG Industries Ohio Inc
•
Filing: 1983-11-07
•
Granted: 1985-03-12
•
Expires: 2003-11-07
Abstract
Abstract The present invention relates to the simultaneous shaping and lamination of lightweight laminated transparencies, particularly those that are suitable for use in aircraft. The plies of an assembly to be shaped and laminated are assembled with additional elements to form a flexible cell of air impervious material. The cell includes an air impervious flexible wall defining a peripheral space around the assembly and porous material in the space. The cell containing the assembly is mounted over a vacuum mold and heated to sag the cell and its assembly to the contour of the mold while evacuating the cell while the cell and said assembly are exposed to atmospheric pressure. The cell is cooled while still under evacuation until the shape of the assembly is set, then is separated from the vacuum mold. The resulting assembly thus shaped and laminated is separated from the cell.
Inventors
- 👤 John E. Radzwill
- 👤 Roger F. Bartoli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:57
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/26; B29C51/28; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10807; B32B17/10816; B32B17/10825; B32B17/10834; B32B17/10844; B32B17/10853; B32B17/10889; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29L; B29L2009/00; B32B2309/00; B32B2309/02; B32B2309/025; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1043; Y10T156/1044
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
437 words
A method of simultaneously shaping and laminating a lightweight laminated transparency comprising elements including a pair of outer relatively rigid plies of acrylic or polycarbonate plastic and a flexible interlayer composed of a material selected from the group consisting of polyurethane and plasticized polyvinyl butyral comprising assembling at least one layer of said interlayer material between said pair of relatively rigid plies to form an assembly to be simultaneously shaped and laminated, supporting said assembly to be shaped and laminated on a base of a flexible, non-porous sheet larger in outline than said assembly in such a manner that said sheet forms the bottom wall of a cell and the perimeter of said assembly to be simultaneously shaped and laminated is in spaced relation within a flexible wall of air impervious material enclosing said cell, applying a flexible, non-porous sheet of air impervious material larger in outline than said assembly to the upper surface of said air impervious enclosing wall of said cell and against the upper surface of said assembly to form a roof for said cell, communicating said cell to a vacuum source to put said cell including the interfaces between the elements of said assembly within said cell under subatmospheric pressure, mounting said cell over a vacuum mold having an upward facing shaping surface of concave elevation conforming to the shape desired for said transparency including a vacuum opening so that said cell faces said vacuum opening and forms a collapsible chamber with said mold, supporting the portions of said flexible sheets of air impervious material extending beyond said assembly in fluid-tight relation to said wall enclosing said cell, heating said cell and said assembly while the latter are under vacuum to a deformation temperature of said assembly to sag said cell toward said upper shaping surface and applying vacuum through the vacuum opening of said mold while said cell is so heated and sealed to conform said cell to said shaping surface, the atmospheric pressure above said roof of said cell causing said layers of relatively rigid plastic to laminate to opposite sides of said interlayer while forcing said cell to conform to the shape of said shaping surface and the layers of said assembly within said cell to laminate at a maximum pressure less than ten percent above atmospheric pressure to convert said assembly to a bent laminated transparency, cooling said cell after it conforms to said shaping surface while maintaining said vacuum within said cell until said bent, laminated transparency within said cell retains its shape, separating said cell from said mold and separating said shaped, laminated transparency from said cell.
Claim 2
Independent Claim
437 words
A method of simultaneously shaping and laminating a lightweight laminated transparency comprising elements including a pair of outer relatively rigid plies of acrylic or polycarbonate plastic and a flexible interlayer composed of a material selected from the group consisting of polyurethane and plasticized polyvinyl butyral comprising assembling at least one layer of said interlayer material between said pair of relatively rigid plies to form an assembly to be simultaneously shaped and laminated, supporting said assembly to be shaped and laminated on a base of a flexible, non-porous sheet larger in outline than said assembly in such a manner that said sheet forms the bottom wall of a cell and the perimeter of said assembly to be simultaneously shaped and laminated is in spaced relation within a flexible wall of air impervious material enclosing said cell, applying a flexible, non-porous sheet of air impervious material larger in outline than said assembly to the upper surface of said air impervious enclosing wall of said cell and against the upper surface of said assembly to form a roof for said cell, communicating said cell to a vacuum source to put said cell including the interfaces between the elements of said assembly within said cell under subatmospheric pressure, mounting said cell over a vacuum mold having an upward facing shaping surface of concave elevation conforming to the shape desired for said transparency including a vacuum opening so that said cell faces said vacuum opening and forms a collapsible chamber with said mold, supporting the portions of said flexible sheets of air impervious material extending beyond said assembly in fluid-tight relation to said wall enclosing said cell, heating said cell and said assembly while the latter are under vacuum to a deformation temperature of said assembly to sag said cell toward said upper shaping surface and applying vacuum through the vacuum opening of said mold while said cell is so heated and sealed to conform said cell to said shaping surface, the atmospheric pressure above said roof of said cell causing said layers of relatively rigid plastic to laminate to opposite sides of said interlayer while forcing said cell to conform to the shape of said shaping surface and the layers of said assembly within said cell to laminate at a maximum pressure less than ten percent above atmospheric pressure to convert said assembly to a bent laminated transparency, cooling said cell after it conforms to said shaping surface while maintaining said vacuum within said cell until said bent, laminated transparency within said cell retains its shape, separating said cell from said mold and separating said shaped, laminated transparency from said cell.
Claim 3
Dependent Claim
29 words
The method as in claim 1, wherein said assembly within said cell is subjected to a stronger vacuum through said enclosing wall than said collapsible chamber is subjected to.
Claim 4
Dependent Claim
24 words
The method as in claim 2, wherein said cell comprises an assembly of alternate relatively rigid plies of acrylic plastic and flexible interlayer material.
Claim 5
Dependent Claim
24 words
The method as in claim 2, wherein said assembly and cell are heated to a temperature of 210° F.±10° l F. (99° C.±6° C.).
Claim 6
Dependent Claim
55 words
The method as in claim 2, wherein said cell is subjected to a vacuum equivalent to a mercury column of about 28 to 29 inches (711 mm to 737 mm) and said collapsible chamber is subjected to a vacuum equivalent to a mercury column of about 5 to 10 inches (127 mm to 254 mm).
Claim 7
Dependent Claim
60 words
The method as in claim 2, wherein said assembly and flexible cell are heated to the deformation temperature of said assembly but below a temperature at which the plies become degraded with vacuum applied to said cell for at least one hour before vacuum is applied to said collapsible chamber between said vacuum mold and said lower flexible, non-porous sheet.
Claim 8
Dependent Claim
60 words
The method as in claim 2, wherein said assembly is supported on a horizontally disposed base of said cell comprising a sheet of deformable foam material and a film of parting material bonded to the upper surface of said sheet of deformable foam material and said flexible wall in air-tight relation to the peripheral portion of said flexible wall base.
Claim 9
Dependent Claim
15 words
The method as in claim 2, wherein said heating is accomplished using hot recirculating fluid.
Claim 10
Dependent Claim
58 words
The method as in claim 8, wherein said heating is accomplished by recirculating hot fluid in said collapsible chamber and also in a chamber above said cell until said assembly reaches deformation temperature, then removing hot fluid from said collapsible chamber until said cell conforms to said shaping surface, then cooling said assembly until its shape is set.
Claim 11
Dependent Claim
42 words
The method as in claim 2, further including providing the peripheral space between said wall and said assembly with a porous material that does not adhere to the elements of the assembly to be laminated under conditions of exposure during said method.
Claim 12
Independent Claim
432 words
A method of simultaneously shaping and laminating a lightweight laminated transparency comprising elements including a pair of outer relatively rigid plies of acrylic or polycarbonate plastic and a flexible interlayer composed of a material selected from the group consisting of polyurethane and plasticized polyvinyl butyral comprising assembling at least one layer of said interlayer material between said pair of relatively rigid plies to form an assembly to be simultaneously shaped and laminated, supporting said assembly to be shaped and laminated on a base of a flexible, non-porous cell larger in outline than said assembly in such a manner that the perimeter of said assembly to be simultaneously shaped and laminated is in spaced relation within a flexible wall of air impervious material enclosing said cell, bonding a first flexible diaphragm of air impervious material to the upper surface of said air impervious wall of said cell to form a roof for said cell, communicating said cell to a vacuum source to put said cell including the interfaces between the elements of said assembly within said cell under subatmospheric pressure, mounting said cell over a vacuum mold having an upward facing shaping surface of concave elevation conforming to the shape desired for said transparency including a vacuum opening so that said cell faces said vacuum opening, applying a second flexible diaphragm of air impervious material extending beyond said first flexible diaphragm over said first flexible diaphragm, adhering the portion of said second flexible diaphragm that extends beyond the first flexible diaphragm to the surface of said mold in spaced relation to the periphery of said cell to form a collapsible chamber surrounding said cell, heating said cell and said assembly while the latter are under vacuum to a deformation temperature of said assembly to sag said cell toward said upper shaping surface and applying vacuum through the vacuum opening of said mold while said cell is so heated and sealed to conform said cell to said shaping surface, the atmospheric pressure above said second diaphragm causing said layers of relatively rigid plastic to laminate to opposite sides of said interlayer while forcing said cell to conform to the shape of said shaping surface, and the layers of said assembly within said cell to laminate at a pressure not exceeding atmospheric pressure to convert said assembly to a bent laminated transparency, cooling said cell after it conforms to said shaping surface while maintaining said vacuum within said cell until said bent, laminated transparency within said cell retains its shape, separating said cell from said mold and separating said shaped, laminated transparency from said cell.
Claim 13
Independent Claim
432 words
A method of simultaneously shaping and laminating a lightweight laminated transparency comprising elements including a pair of outer relatively rigid plies of acrylic or polycarbonate plastic and a flexible interlayer composed of a material selected from the group consisting of polyurethane and plasticized polyvinyl butyral comprising assembling at least one layer of said interlayer material between said pair of relatively rigid plies to form an assembly to be simultaneously shaped and laminated, supporting said assembly to be shaped and laminated on a base of a flexible, non-porous cell larger in outline than said assembly in such a manner that the perimeter of said assembly to be simultaneously shaped and laminated is in spaced relation within a flexible wall of air impervious material enclosing said cell, bonding a first flexible diaphragm of air impervious material to the upper surface of said air impervious wall of said cell to form a roof for said cell, communicating said cell to a vacuum source to put said cell including the interfaces between the elements of said assembly within said cell under subatmospheric pressure, mounting said cell over a vacuum mold having an upward facing shaping surface of concave elevation conforming to the shape desired for said transparency including a vacuum opening so that said cell faces said vacuum opening, applying a second flexible diaphragm of air impervious material extending beyond said first flexible diaphragm over said first flexible diaphragm, adhering the portion of said second flexible diaphragm that extends beyond the first flexible diaphragm to the surface of said mold in spaced relation to the periphery of said cell to form a collapsible chamber surrounding said cell, heating said cell and said assembly while the latter are under vacuum to a deformation temperature of said assembly to sag said cell toward said upper shaping surface and applying vacuum through the vacuum opening of said mold while said cell is so heated and sealed to conform said cell to said shaping surface, the atmospheric pressure above said second diaphragm causing said layers of relatively rigid plastic to laminate to opposite sides of said interlayer while forcing said cell to conform to the shape of said shaping surface, and the layers of said assembly within said cell to laminate at a pressure not exceeding atmospheric pressure to convert said assembly to a bent laminated transparency, cooling said cell after it conforms to said shaping surface while maintaining said vacuum within said cell until said bent, laminated transparency within said cell retains its shape, separating said cell from said mold and separating said shaped, laminated transparency from said cell.
Claim 14
Dependent Claim
36 words
The method as in claim 11, wherein said assembly within said cell is subjected to a stronger vacuum through said wall than said chamber between said second flexible diaphragm and said vacuum mold is subjected to.
Claim 15
Dependent Claim
24 words
The method as in claim 12, wherein said cell comprises an assembly of alternate relatively rigid plies of acrylic plastic and flexible interlayer material.
Claim 16
Dependent Claim
23 words
The method as in claim 12, wherein said assembly and cell are heated to a temperature of 210° F.±10° F. (99° C.±6° C.)
Claim 17
Dependent Claim
55 words
The method as in claim 12, wherein said cell is subjected to a vacuum equivalent to a mercury column of about 28 to 29 inches (711 mm to 737 mm) and said collapsible chamber is subjected to a vacuum equivalent to a mercury column of about 5 to 10 inches (127 mm to 254 mm).
Claim 18
Dependent Claim
53 words
The method as in claim 12, wherein said assembly and flexible cell are heated to the deformation temperature of said assembly but below a temperature at which the plies become degraded with vacuum applied to said cell for at least two hours before vacuum is applied to said collapsible chamber outside said cell.
Claim 19
Dependent Claim
59 words
The method as in claim 12, wherein said assembly is supported on a horizontally disposed base of said cell comprising a sheet of deformable foam material and a film of parting material bonded to the upper surface of said sheet of deformable foam material and said flexible wall is bonded to the peripheral portion of said flexible wall base.
Claim 20
Dependent Claim
17 words
The method as in claim 12, wherein said heating is accomplished using hot air within an oven.
Claim 21
Dependent Claim
42 words
The method as in claim 12, further including providing the peripheral space between said wall and said assembly with a porous material that does not adhere to the elements of the assembly to the laminated under conditions of exposure during said method.
References Cited (Backward Citations)
US2466735A
Cited
US3051054A
Cited
US3228330A
Cited
US4180426A
Cited
US3769133A
Cited
US3960627A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-11 | 1988-09-10 | 1989-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-11 | 1992-09-10 | 1993-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-11 | 1996-09-10 | 1997-03-12 | $7700.00 | Window Closed / Lapsed |