US4504298A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing infrared light transmitting optical fiber
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1983-10-19
•
Granted: 1985-03-12
•
Expires: 2003-10-19
Abstract
Abstract A process is disclosed for producing an infrared light transmitting optical fiber by drawing a rod of single crystal or polycrystalline metal halide into a fiber through a die; also disclosed is a process for producing an infrared light transmitting optical fiber of step-index type by forming around a single crystal or polycrystalline fiber core, an intimate cladding crystal layer having a lower refractive index than the core by working in the temperature range that does not cause recrystallization of the core or cladding during working.
Inventors
- 👤 Minoru Yokota
- 👤 Kazuhito Murakami
- 👤 Kenichi Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:56
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/102; C; C03; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/022; C03B37/023; C03C; C03C13/00; C03C13/008; C30; C30B; C30B29/00; C30B29/10; C30B29/12; C30B33/00; C03B2201/00; C03B2201/80; C03B2201/84
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
117 words
An improved process for producing a step-index infrared light transmitting optical fiber by drawing a rod of single crystal or polycrystalline silver halide, thallium halide, or a mixed crystal thereof into a fiber core through a die, forming around said fiber core an intimate cladding crystal layer having a lower refractive index than the core, wherein the improvement comprises plastic working the core and the cladding by rolling or drawing through a die in a temperature range that does not cause recrystallization of the core or cladding during working, whereby the crystal grains of the core and the crystal grains of the cladding crystal do not intermesh with each other and thereby retain their initial surface smoothness.
Claim 2
Dependent Claim
117 words
An improved process for producing a step-index infrared light transmitting optical fiber by drawing a rod of single crystal or polycrystalline silver halide, thallium halide, or a mixed crystal thereof into a fiber core through a die, forming around said fiber core an intimate cladding crystal layer having a lower refractive index than the core, wherein the improvement comprises plastic working the core and the cladding by rolling or drawing through a die in a temperature range that does not cause recrystallization of the core or cladding during working, whereby the crystal grains of the core and the crystal grains of the cladding crystal do not intermesh with each other and thereby retain their initial surface smoothness.
Claim 3
Dependent Claim
32 words
A process according to claim 1, wherein the drawing through a die is performed in such a manner that the reduction in the cross-sectional area per pass is not more than 20%.
Claim 4
Dependent Claim
34 words
A process according to claim 1, wherein the working in a temperature range that does not cause recrystallization of the core or cladding during working is conducted by rolling or drawing through a die.
Claim 5
Dependent Claim
29 words
A process according to claim 1 or 3, wherein the core and cladding crystal layer are produced from a silver halide, a thallium halide, or a mixed crystal thereof.
Claim 6
Dependent Claim
30 words
A process according to claim 1 or 3, wherein the cladding crystal layer is further coated with a resin or metal protective layer by extrusion, or by coating and baking.
Claim 7
Dependent Claim
28 words
A process according to claim 4, wherein the cladding crystal layer is further coated with a resin or metal protective layer by extrusion, or by coating and baking.
Claim 8
Dependent Claim
20 words
A process according to claim 1, or 3, wherein the drawing through a die is performed using a liquid lubricant.
Claim 9
Dependent Claim
30 words
A process according to claim 7, wherein the liquid lubricant is selected from the group consisting of silicone oil, spindle oil, turbine oil, castor oil, palm oil, and whale oil.
Claim 10
Dependent Claim
18 words
A process according to claim 4, wherein the drawing through a die is performed using a liquid lubricant.
Claim 11
Dependent Claim
30 words
A process according to claim 9, wherein the liquid lubricant is selected from the group consisting of silicone oil, spindle oil, turbine oil, castor oil, palm oil, and whale oil.
Claim 12
Dependent Claim
51 words
The process according to claim 1, wherein the core is held between two thin sheets of a cladding crystal material, wherein the core and the cladding combination is cold-rolled by grooved rolls to form the cladding material into a cladding crystal layer in intimate contact with the periphery of the core.
Claim 13
Dependent Claim
55 words
The process according to claim 1, wherein a thin sheet of infrared light transmitting cladding crystal material is shaped into a tubular form by roll forming around the core, and the core and cladding combination is cold-rolled by grooved rolls to form a cladding crystal layer in intimate contact with the periphery of the core.
Claim 14
Dependent Claim
55 words
The process according to claim 1, wherein the core is inserted in the hollow part of a pipe that is made of an infrared light transmitting cladding material, and the pipe is drawn through a die to form the cladding material into a cladding crystal layer in intimate contact with the periphery of the core.
Claim 15
Dependent Claim
16 words
The process according to claim 13, wherein a protective layer is formed around the cladding layer.
Claim 16
Dependent Claim
20 words
The process according to claim 14, wherein the protective layer is formed by applying and baking a highly corrosion-resistant material.
Claim 17
Dependent Claim
43 words
The process according to claim 15, wherein the material used in forming the protective layer is selected from the group consisting of polyester imide resin, polyester resin, polyurethane resin, polyimide resin, tetrafluoride resin, silicone resin, epoxy resin, cyanacrylate resin and a mixture thereof.
Claim 18
Dependent Claim
49 words
The process according to claim 14, wherein the protective layer is formed by melt-extruding a material selected from the group consisting of acrylonitrile-butadiene-styrene copolymer resin, polybutadiene resin, polypropylene resin, polyethylene resin, polycarbonate resin, polyvinyl chloride resin, polyphenylene oxide resin, polysulfone resin and a mixture thereof over the cladding layer.
Claim 19
Dependent Claim
21 words
The process according to claim 14, wherein the protective layer is formed by extruding a low-melting metal over the cladding layer.
Claim 20
Dependent Claim
21 words
The process according to claim 14, wherein a plurality of metal and/or resin protective layers are formed over the cladding layer.
Claim 21
Dependent Claim
28 words
The process according to claim 19, wherein a resin layer is formed directly on the cladding layer and the metal layer is then formed on the resin layer.
References Cited (Backward Citations)
US2109312A
Cited
US2203751A
Cited
US2986527A
Cited
US3551051A
Cited
JPS522745A
Cited
US4253731A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-11 | 1988-09-10 | 1989-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-11 | 1992-09-10 | 1993-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-11 | 1996-09-10 | 1997-03-12 | $7700.00 | Window Closed / Lapsed |