Two-stage chemical treatment of mechanical wood pulp with sodium sulfite
Assignee: MacMillan Bloedel Ltd
•
Filing: 1982-06-04
•
Granted: 1985-03-05
•
Expires: 2002-06-04
Abstract
Abstract A two-stage chemical treatment process is disclosed for increasing the density, strength and brightness properties of mechanical wood pulp. The method comprises the steps of: applying an aqueous solution of sodium sulfite in the range of about 1%-10% sodium sulfite based on bone dry weight of wood to wood particles, the solution having a pH in the range of about 4.5-11; heating the sodium sulfite treated wood particles to a temperature in the range of about 100°-160° C. and maintaining the particles in the temperature range for a period of time in the range of about 20 seconds to 10 minutes; refining the heated sodium sulfite treated wood particles into mechanical wood pulp; separating the pulp into a reject fraction and an accept fraction, the reject fraction containing a higher proportion of shives and long fiber material; applying an aqueous solution of sodium sulfite, in the range of about 4%-50% sodium sulfite based on bone dry weight of wood, to the reject fraction, the solution having a pH in the range of about 4.5-11; cooking the sodium sulfite treated reject fraction at a temperature in the range of about 100°-160° C. for a period of time in the range of about 2-120 minutes; refining the cooked sodium sulfite treated reject fraction; and recombining at least part of the refined reject fraction with at least part of the accept fraction.
Inventors
- 👤 David M. Mackie
- 👤 Peter Joyce
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:58
CPC Classifications
D; D21; D21B; D21B1/00; D21B1/02; D21B1/021; D21C; D21C3/00; D21C3/22; D21C3/26; D21C3/266
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
357 words
A method of improving the properties of mechanical refiner wood pulp, comprising the steps of: applying an aqueous solution of sodium sulfite, in the range of about 1%-10% sodium sulfite based on bone dry weight of wood, to wood particles, selected from the group consisting of wood chips, shredded wood chips, and shavings, the solution having a pH in the range of about 4.5-11; heating the sodium sulfite treated wood particles to a temperature in the range of about 100°-160° C. and maintaining the particles in the temperature range for a period of time in the range of about 20 seconds to 10 minutes; refining the heated sodium sulfite treated wood particles into mechanical wood pulp; separating the pulp into a long fiber fraction and an accept fraction, the long fiber fraction containing a higher proportion of shives and long fiber material, said long fiber fraction representing about 10%-65% by weight of the whole refiner pulp; applying an aqueous solution of sodium sulfite in the range of about 4%-50% sodium sulfite based on bone dry weight of wood, to the long fiber fraction, the solution having a pH in the range of about 4.5-11; cooking the sodium sulfite treated long fiber fraction at a temperature in the range of about 100°-160° C. for a period of time in the range of about 2-120 minutes; refining the cooked sodium sulfite treated long fiber fraction to provide a refined long fiber fraction that provides handsheets prepared according to TAPPI standard T205 om-81 and, when tested according to TAPPI standard T220 os-71, having a freeness in the range of about 100-300 ml, sheet density in the range of about 0.4-0.55 g/cm 3 , burst index in the range of about 3.2-4.6 g/cm 3 , breaking length in the range of about 6500-7800 m and tear index in the range of about 8-14 mN.m 2 /g; recombining at least part of the refined long fiber fraction with at least part of the accept fraction; and the combined weight of the accept fraction and the refined long fiber fraction, being at least about 90% based on bone dry weight of wood particles.
Claim 2
Independent Claim
357 words
A method of improving the properties of mechanical refiner wood pulp, comprising the steps of: applying an aqueous solution of sodium sulfite, in the range of about 1%-10% sodium sulfite based on bone dry weight of wood, to wood particles, selected from the group consisting of wood chips, shredded wood chips, and shavings, the solution having a pH in the range of about 4.5-11; heating the sodium sulfite treated wood particles to a temperature in the range of about 100°-160° C. and maintaining the particles in the temperature range for a period of time in the range of about 20 seconds to 10 minutes; refining the heated sodium sulfite treated wood particles into mechanical wood pulp; separating the pulp into a long fiber fraction and an accept fraction, the long fiber fraction containing a higher proportion of shives and long fiber material, said long fiber fraction representing about 10%-65% by weight of the whole refiner pulp; applying an aqueous solution of sodium sulfite in the range of about 4%-50% sodium sulfite based on bone dry weight of wood, to the long fiber fraction, the solution having a pH in the range of about 4.5-11; cooking the sodium sulfite treated long fiber fraction at a temperature in the range of about 100°-160° C. for a period of time in the range of about 2-120 minutes; refining the cooked sodium sulfite treated long fiber fraction to provide a refined long fiber fraction that provides handsheets prepared according to TAPPI standard T205 om-81 and, when tested according to TAPPI standard T220 os-71, having a freeness in the range of about 100-300 ml, sheet density in the range of about 0.4-0.55 g/cm 3 , burst index in the range of about 3.2-4.6 g/cm 3 , breaking length in the range of about 6500-7800 m and tear index in the range of about 8-14 mN.m 2 /g; recombining at least part of the refined long fiber fraction with at least part of the accept fraction; and the combined weight of the accept fraction and the refined long fiber fraction, being at least about 90% based on bone dry weight of wood particles.
Claim 3
Dependent Claim
27 words
The method according to claim 1 wherein the aqueous solution of sodium sulfite applied to the wood particles is in the range of about 3%-7% sodium sulfite.
Claim 4
Dependent Claim
27 words
The method according to claim 1 wherein the aqueous solution of sodium sulfite applied to the wood particles has a pH in the range of about 5.5-9.5.
Claim 5
Dependent Claim
33 words
The method according to claim 1 wherein the sodium sulfite treated wood particles are heated and maintained within the temperature range for a period of time in the range of about 2-4 minutes.
Claim 6
Dependent Claim
27 words
The method according to claim 1 wherein the heating of the sodium sulfite treated wood particles occurs at a temperature in the range of about 115°-155° C.
Claim 7
Dependent Claim
28 words
The method according to claim 1 wherein the aqueous solution of sodium sulfite applied to the long fiber fraction is in the range of about 8%-18% sodium sulfite.
Claim 8
Dependent Claim
28 words
The method according to claim 1 wherein the aqueous solution of sodium sulfite applied to the long fiber fraction has a pH in the range of about 5.5-9.5.
Claim 9
Dependent Claim
28 words
The method according to claim 1 wherein the sodium sulfite treated long fiber fraction is cooked for a period of time in the range of about 2-30 minutes.
Claim 10
Dependent Claim
26 words
The method according to claim 1 wherein the sodium sulfite treated long fiber fraction is cooked at a temperature in the range of about 130°-155° C.
Claim 11
Dependent Claim
32 words
The method according to claim 1 wherein sufficient aqueous solution of sodium sulfite is applied to the wood particles to provide a liquid/wood ratio in the range of about 1/1 to 3/1.
Claim 12
Independent Claim
354 words
A method of improving the properties of mechanical refiner wood pulp, comprising the steps of; applying an aqueous solution of sodium sulfite, in the range of about 3%-7% sodium sulfite based on bone dry weight of wood, to wood particles, selected from the group consisting of wood chips, shredded wood chips and shavings, the solution having a pH in the range of about 5.5-9.5; heating the sodium sulfite treated wood particles to a temperature in the range of about 115°-155° C. and maintaining the particles in the temperature range for a period of time in the range of about 2-4 minutes; refining the heated sodium sulfite treated wood particles into mechanical wood pulp; separating the pulp into a long fiber fraction and in accept fraction, the long fiber fraction containing a higher proportion of shives and long fiber material, said long fiber fraction representing about 10%-65% by weight of the whole refiner pulp; applying an aqueous solution of sodium sulfite in the range of about 8%-18% sodium sulfite based on bone dry weight of wood, to the long fiber fraction, the solution having a pH in the range of about 5.5-9.5; cooking the sodium sulfite treated long fiber fraction at a temperature in the range of about 130°-155° C. for a period of time in the range of about 2-30 minutes; refining the cooked sodium sulfite treated long fiber fraction to provide a refined long fiber fraction that provides handsheets prepared according to TAPPI standard T205 om-81 and, when tested according to TAPPI standard T220 os-71, having a freeness in the range of about 100-300 ml, sheet density in the range of about 0.4-0.55 g/cm 3 , burst index in the range of about 3.2-4.6 g/cm 3 , breaking length in the range of about 6500-7800 m and tear index in the range of about 8-14 mN.m 2 /g; recombining at least part of the refined long fiber fraction with at least part of the accept fraction; and the combined weight of the accept fraction and the refined long fiber fraction being at least about 90% based on bone dry weight of wood particles.
Claim 13
Independent Claim
354 words
A method of improving the properties of mechanical refiner wood pulp, comprising the steps of; applying an aqueous solution of sodium sulfite, in the range of about 3%-7% sodium sulfite based on bone dry weight of wood, to wood particles, selected from the group consisting of wood chips, shredded wood chips and shavings, the solution having a pH in the range of about 5.5-9.5; heating the sodium sulfite treated wood particles to a temperature in the range of about 115°-155° C. and maintaining the particles in the temperature range for a period of time in the range of about 2-4 minutes; refining the heated sodium sulfite treated wood particles into mechanical wood pulp; separating the pulp into a long fiber fraction and in accept fraction, the long fiber fraction containing a higher proportion of shives and long fiber material, said long fiber fraction representing about 10%-65% by weight of the whole refiner pulp; applying an aqueous solution of sodium sulfite in the range of about 8%-18% sodium sulfite based on bone dry weight of wood, to the long fiber fraction, the solution having a pH in the range of about 5.5-9.5; cooking the sodium sulfite treated long fiber fraction at a temperature in the range of about 130°-155° C. for a period of time in the range of about 2-30 minutes; refining the cooked sodium sulfite treated long fiber fraction to provide a refined long fiber fraction that provides handsheets prepared according to TAPPI standard T205 om-81 and, when tested according to TAPPI standard T220 os-71, having a freeness in the range of about 100-300 ml, sheet density in the range of about 0.4-0.55 g/cm 3 , burst index in the range of about 3.2-4.6 g/cm 3 , breaking length in the range of about 6500-7800 m and tear index in the range of about 8-14 mN.m 2 /g; recombining at least part of the refined long fiber fraction with at least part of the accept fraction; and the combined weight of the accept fraction and the refined long fiber fraction being at least about 90% based on bone dry weight of wood particles.
Claim 14
Dependent Claim
32 words
The method according to claim 11 wherein sufficient aqueous solution of sodium sulfite is applied to the wood particles to provide a liquid/wood ratio in the range of about 2/1 to 3/1.
Claim 15
Dependent Claim
40 words
The method according to claim 1 or claim 11 wherein the yield of the wood particles after being treated with sodium sulfite and prior to being refined is at least about 91% based on bone dry weight of wood particles.
Claim 16
Dependent Claim
32 words
The method according to claim 1 or claim 11 wherein the accept fraction combined with the long fiber fraction is in the range of about 50%-85% by weight of the recombined pulp.
Claim 17
Dependent Claim
34 words
The method according to claim 1 or claim 11 wherein the long fiber fraction has a pulp consistency in the range of about 10%-50% prior to application of the aqueous solution of sodium sulfite.
Claim 18
Dependent Claim
23 words
The method according to claim 1 or claim 11 wherein the wood particles have a moisture content in the range of about 25%-60%.
Claim 19
Dependent Claim
34 words
The method according to claim 1 or claim 11 wherein the wood particles are first squeezed to reduce moisture content in a screw press, followed by application of the aqueous solution of sodium sulfite.
Claim 20
Dependent Claim
36 words
The method according to claim 1 or claim 11 wherein the wood particles are first squeezed to reduce moisture content to a range of about 45%-50%, followed by application of the aqueous solution of sodium sulfite.
Claim 21
Dependent Claim
14 words
The method according to claim 1 or claim 11 wherein said wood is softwood.
Claim 22
Dependent Claim
26 words
The method according to claim 1 or claim 11 wherein the long fiber fraction represents about 10%-35% by weight of the whole mechanical refiner wood pulp.
Claim 23
Dependent Claim
16 words
The method according to claim 1 or claim 11 wherein the wood particles are wood chips.
Claim 24
Dependent Claim
17 words
The method according to claim 1 or claim 11 wherein the wood particles are shredded wood chips.
Claim 25
Dependent Claim
15 words
The method according to claim 1 or claim 11 wherein the wood particles are shavings.
Claim 26
Dependent Claim
30 words
The method according to claim 1 or claim 11 wherein sheet density of TAPPI handsheets prepared from the combined fractions is in the range of about 0.375-0.42 g/cm 3 .
Claim 27
Dependent Claim
18 words
The method according to claim 1 wherein sodium sulfite applied to the wood particles is at least 3%.
Claim 28
Dependent Claim
42 words
The method according to claim 1 or claim 11 wherein sodium sulfite applied to the wood particles is at least 3% and including application of sodium hydrosulfite to the recombined mechanical refiner wood pulp prior to the pulp being processed into paper.
References Cited (Backward Citations)
US3597310A
Cited
US3607613A
Cited
US4259148A
Cited
US4145246A
Cited
CA1071805A
Cited
SU827656A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-03-04 | 1988-09-03 | 1989-03-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-03-04 | 1992-09-03 | 1993-03-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-03-04 | 1996-09-03 | 1997-03-05 | $7700.00 | Window Closed / Lapsed |