Surfactant treated polyolefinic microporous materials capable of multiple re-wetting with aqueous solutions
Assignee: Celanese Corp
•
Filing: 1983-06-17
•
Granted: 1985-02-26
•
Expires: 2003-06-17
Abstract
Abstract Disclosed are hydrophilic polyolefinic microporous materials and a method for the preparation thereof. Such materials are prepared by impregnating a normally hydrophobic polyolefinic microporous substrate material with a solution of a nonionic alkylphenoxy poly(ethyleneoxy) ethanol surfactant having an HLB of from about 10 to 15 in a solvent system comprising from about 55 to about 65 volume percent methanol or acetone and from about 35 to about 45 volume percent water. It has been discovered that polyolefinic microporous materials rendered hydrophilic by this technique not only wet rapidly, but in addition may be multiply re-wet with aqueous solutions, such as aqueous alkali solutions, with excellent retention of their hydrophilic properties. The hydrophilic polyolefinic microporous materials of this invention find particular application as battery separators and as membranes for use in various chemical, medical and biotechnical processes.
Inventors
- 👤 Thyagaraja Sarada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:15
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0088; C; C08; C08J; C08J9/00; C08J9/36; C08J9/40; C08J9/42; D; D06; D06M; D06M13/00; D06M13/10; D06M13/165; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/489; H01M50/491; C08J2323/00; C08J2323/02; C08J2471/00; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249978; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2935
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
152 words
A hydrophilic polyolefinic microporous material comprising a normally hydrophobic polyolefinic open-celled microporous substrate impregnated with at least one nonionic surfactant of the class of alkylphenoxy poly(ethyleneoxy) ethanol compounds having an HLB in the range of from about 10 to about 15 in an amount sufficient to render said hydrophobic polyolefinic microporous substrate wettable with aqueous solutions; said surfactant being present in a solvent mixture comprising from about 55 to about 65 volume percent of methanol or acetone and from about 35 to about 45 volume percent water; and wherein said hydrophobic polyolefinic microporous substrate has a reduced bulk density as compared with the bulk density of a corresponding non-porous polyolefinic material, a crystallinity of at least about 30 percent, an average pore size of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of at least about 10 m 2 /gram.
Claim 2
Dependent Claim
152 words
A hydrophilic polyolefinic microporous material comprising a normally hydrophobic polyolefinic open-celled microporous substrate impregnated with at least one nonionic surfactant of the class of alkylphenoxy poly(ethyleneoxy) ethanol compounds having an HLB in the range of from about 10 to about 15 in an amount sufficient to render said hydrophobic polyolefinic microporous substrate wettable with aqueous solutions; said surfactant being present in a solvent mixture comprising from about 55 to about 65 volume percent of methanol or acetone and from about 35 to about 45 volume percent water; and wherein said hydrophobic polyolefinic microporous substrate has a reduced bulk density as compared with the bulk density of a corresponding non-porous polyolefinic material, a crystallinity of at least about 30 percent, an average pore size of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of at least about 10 m 2 /gram.
Claim 3
Dependent Claim
28 words
The hydrophilic polyolefinic microporous material of claim 1, wherein said material when treated with said surfactant has an electrical resistance of less than about 15 milliohms-in 2 .
Claim 4
Dependent Claim
19 words
The hydrophilic polyolefinic microporous material of claim 1, wherein said microporous material comprises a microporous film or hollow fiber.
Claim 5
Dependent Claim
21 words
The hydrophilic polyolefinic microporous material of claim 3, wherein said surfactant has an HLB of from about 12 to about 13.
Claim 6
Dependent Claim
36 words
The hydrophilic polyolefinic microporous material of claim 4, wherein said hydrophobic microporous substrate is impregnated with said surfactant in an amount sufficient to provide a surfactant add-on of from about 10 to about 15% by weight.
Claim 7
Dependent Claim
141 words
A hydrophilic polyolefinic microporous material comprising a hydrophilic polyolefinic open-celled microporous substrate having a reduced bulk density as compared with the bulk density of a corresponding non-porous polyolefinic material, a crystallinity of from about 50 to about 100 percent, an average pore size of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of from about 20 to 100 m 2 /g, impregnated with a nonionic surfactant of the class of alkylphenoxy poly(ethyleneoxy) ethanol compounds having an HLB in the range of from about 12 to 13 in a solvent mixture comprising from about 55 to about 65 volume percent of methanol and from about 35 to about 45 volume percent water in an amount sufficient to provide a surfactant add-on of from about 10 to about 15% by weight.
Claim 8
Dependent Claim
141 words
A hydrophilic polyolefinic microporous material comprising a hydrophilic polyolefinic open-celled microporous substrate having a reduced bulk density as compared with the bulk density of a corresponding non-porous polyolefinic material, a crystallinity of from about 50 to about 100 percent, an average pore size of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of from about 20 to 100 m 2 /g, impregnated with a nonionic surfactant of the class of alkylphenoxy poly(ethyleneoxy) ethanol compounds having an HLB in the range of from about 12 to 13 in a solvent mixture comprising from about 55 to about 65 volume percent of methanol and from about 35 to about 45 volume percent water in an amount sufficient to provide a surfactant add-on of from about 10 to about 15% by weight.
Claim 9
Dependent Claim
22 words
The hydrophilic polyolefinic microporous material of claim 6, wherein said microporous material is in the form of a film or hollow fiber.
Claim 10
Independent Claim
89 words
A method for preparing a hydrophilic polyolefinic microporous material capable of multiple re-wetting with aqueous solutions comprising contacting a polyolefinic open-celled microporous substrate with a surfactant solution comprising at least one nonionic alkylphenoxy poly(ethyleneoxy) ethanol surfactant having an HLB in the range of from about 10 to 15 in a solvent mixture comprising from about 55 to about 65 volume percent of methanol or acetone and from about 35 to about 45 volume percent water in a manner sufficient to render said polyolefinic microporous substrate wettable with aqueous solutions.
Claim 11
Independent Claim
89 words
A method for preparing a hydrophilic polyolefinic microporous material capable of multiple re-wetting with aqueous solutions comprising contacting a polyolefinic open-celled microporous substrate with a surfactant solution comprising at least one nonionic alkylphenoxy poly(ethyleneoxy) ethanol surfactant having an HLB in the range of from about 10 to 15 in a solvent mixture comprising from about 55 to about 65 volume percent of methanol or acetone and from about 35 to about 45 volume percent water in a manner sufficient to render said polyolefinic microporous substrate wettable with aqueous solutions.
Claim 12
Dependent Claim
65 words
The method of claim 8, wherein said surfactant solution comprises from about 1 to about 10% by weight of said alkylphenoxy poly(ethyleneoxy) ethanol surfactant in an approximately 60:40 volume percent methanol or acetone to water solvent mixture, and said polyolefinic microporous substrate is contacted with said solution in a manner sufficient to provide a surfactant add-on of from about 10 to about 15% by weight.
Claim 13
Dependent Claim
17 words
The method of claim 9, wherein said surfactant has an HLB of from about 12 to 13.
Claim 14
Dependent Claim
72 words
The method of claim 9, wherein said hydrophobic polyolefinic microporous substrate has a reduced bulk density as compared with the bulk density of a corresponding non-porous polyolefinic material, a crystallinity of from about 50 to about 100 percent, on average pore size of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of from about 20 to 100 m 2 /g.
Claim 15
Dependent Claim
178 words
A hydrophilic polyolefinic microporous material capable of multiple re-wetting with aqueous solutions comprising a normally hydrophobic polyolefinic open-celled microporous substrate impregnated with at least one nonionic surfactant of the class of alkylphenoxy poly(ethyleneoxy) ethanol compounds having an HLB in the range of from about 10 to about 15, said hydrophilic polyolefinic microporous material being prepared by contacting said normally hydrophobic polyolefinic microporous substrate with a solution of said alkylphenoxy poly(ethyleneoxy) ethanol surfactant in a solvent mixture comprising from about 55 to about 65 volume percent of acetone or methanol with from about 35 to about 45 volume percent of water in a manner sufficient to render said polyolefinic microporous material wettable with aqueous solutions, wherein said hydrophobic polyolefinic microporous substrate has a reduced bulk density as compared with the bulk density of a corresponding nonporous polyolefinic material, a crystallinity of at least about 30 percent, an average pore sizes of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of at least above 10 m 2 /gram.
Claim 16
Dependent Claim
178 words
A hydrophilic polyolefinic microporous material capable of multiple re-wetting with aqueous solutions comprising a normally hydrophobic polyolefinic open-celled microporous substrate impregnated with at least one nonionic surfactant of the class of alkylphenoxy poly(ethyleneoxy) ethanol compounds having an HLB in the range of from about 10 to about 15, said hydrophilic polyolefinic microporous material being prepared by contacting said normally hydrophobic polyolefinic microporous substrate with a solution of said alkylphenoxy poly(ethyleneoxy) ethanol surfactant in a solvent mixture comprising from about 55 to about 65 volume percent of acetone or methanol with from about 35 to about 45 volume percent of water in a manner sufficient to render said polyolefinic microporous material wettable with aqueous solutions, wherein said hydrophobic polyolefinic microporous substrate has a reduced bulk density as compared with the bulk density of a corresponding nonporous polyolefinic material, a crystallinity of at least about 30 percent, an average pore sizes of from about 100 to about 5000 Angstroms, a porosity of from about 40 to about 90%, and a surface area of at least above 10 m 2 /gram.
Claim 17
Dependent Claim
72 words
The hydrophilic polyolefinic microporous material of claim 12, wherein said material is prepared by contacting said normally hydrophobic polyolefinic substrate with a surfactant solution comprising from about 1 to about 10% by weight of said alkylphenoxy poly(ethyleneoxy) ethanol surfactant in an approximately 60:40 volume percent methanol or acetone to water solvent mixture for a period of time sufficient to produce a surfactant add-on of from about 10 to about 15% by weight.
Claim 18
Dependent Claim
22 words
The hydrophilic polyolefinic microporous material of claim 13, wherein said microporous material is in the form of a film or hollow fiber.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-26 | 1988-08-27 | 1989-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-26 | 1992-08-27 | 1993-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-26 | 1996-08-27 | 1997-02-26 | $7700.00 | Window Closed / Lapsed |