Composite refractory articles and method of manufacturing them
Assignee: AGC Glass Europe SA
•
Filing: 1982-09-17
•
Granted: 1985-02-05
•
Expires: 2002-09-17
Abstract
Abstract A method of manufacturing a composite refractory article having a flow passage through which a molten metal stream may be conducted and comprising a first body of refractory material which defines a surface of that passage, the first body being bonded to a second body of refractory material. The second body is provided to define a passageway of greater cross-sectional dimensions than the flow passage. Within the passageway, the first body of refractory material is provided for defining the flow passage surface, the first body being formed in the larger passageway by causing its refractory material to cohere and bond to the second body by fusion or partial fusion in situ.
Inventors
- 👤 Pierre Robyn
- 👤 Pierre Deschepper
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:15
CPC Classifications
B; B22; B22D; B22D41/00; B22D41/14; B22D41/22; B22D41/28
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
132 words
A method for manufacturing a composite refractory article having a flow passage through which a molten metal stream may be conducted, said article comprising a first body of a relatively high grade refractory material which defines an axially extending surface of that passage, said first body being fused to a second body of relatively lower grade refractory material; comprising the steps of producing said second body defining a passageway of greater cross-sectional dimensions than said flow passage and providing within said passageway said first body of refractory material for defining said flow passage surface, said first body being formed in a sliding gate valve plate and being formed in the larger passageway by causing its refractory material to cohere and bond to said second body by fusion or partial fusion in situ.
Claim 2
Independent Claim
132 words
A method for manufacturing a composite refractory article having a flow passage through which a molten metal stream may be conducted, said article comprising a first body of a relatively high grade refractory material which defines an axially extending surface of that passage, said first body being fused to a second body of relatively lower grade refractory material; comprising the steps of producing said second body defining a passageway of greater cross-sectional dimensions than said flow passage and providing within said passageway said first body of refractory material for defining said flow passage surface, said first body being formed in a sliding gate valve plate and being formed in the larger passageway by causing its refractory material to cohere and bond to said second body by fusion or partial fusion in situ.
Claim 3
Dependent Claim
20 words
A method according to claim 1 wherein said first refractory body is composed of fused or partially fused refractory material.
Claim 4
Dependent Claim
17 words
A method according to claim 1, wherein said first refractory body is formed by a spraying technique.
Claim 5
Dependent Claim
33 words
A method according to claim 3, wherein said first refractory body is formed by flame spraying a mixture of exothermically oxidizable material and other material so as to form a coherent refractory mass.
Claim 6
Dependent Claim
32 words
A method according to claim 4, wherein said oxidizable material is sprayed in the form of particles having an average size of less than 50 μm and preferably less than 10 μm.
Claim 7
Dependent Claim
28 words
A method according to claim 4, wherein said oxidizable material is sprayed in the form of particles having a specific surface of at least 500 cm 2 /gram
Claim 8
Independent Claim
28 words
A method according to any of claims 4 to 6, wherein said other material is sprayed in the form of particles having an average size below 500 μm.
Claim 9
Dependent Claim
20 words
A method according to claim 4, wherein said oxidizable material consists at least in part of a metal or metalloid.
Claim 10
Dependent Claim
20 words
A method according to claim 4, wherein said oxidizable material constitutes less than 35% by weight of the mixture sprayed.
Claim 11
Dependent Claim
21 words
A method according to claim 4, wherein said other material comprises one or more of zirconia, zircon, silica, alumina, chrome-magnesia, magnesia.
Claim 12
Dependent Claim
24 words
A method according to claim 1, wherein said valve plate has an integral collector nozzle at least partially lined by said first refractory body.
Claim 13
Dependent Claim
30 words
A method according to claim 1, wherein said first refractory body is formed in a hole made by removing material from around a flow passage of a used refractory article.
Claim 14
Dependent Claim
29 words
A method according to claim 8, wherein the metal or metalloid is selected from the group: aluminum, magnesium, silicon, zirconium and mixtures of two or more of such materials.
Claim 15
Dependent Claim
28 words
A method according to claim 4, wherein said oxidizable material is sprayed in the form of particles having a specific surface of at least 3000 cm 2 /gram.
Claim 16
Independent Claim
110 words
A method of manufacturing a composite refractory article having a flow passage through which a molten metal stream may be conducted and comprising a first body of refractory material which defines a surface of that passage, said first body being bonded to a second body of refractory material, comprising the steps of providing said second body defining a passageway of greater cross-sectional dimensions than said flow passage surface, said first body being formed in the larger passageway by causing its refractory material to cohere and bond to said second body, by fusion or partial fusion, in situ, said first body being formed and then drilled to define said flow passage.
Claim 17
Independent Claim
110 words
A method of manufacturing a composite refractory article having a flow passage through which a molten metal stream may be conducted and comprising a first body of refractory material which defines a surface of that passage, said first body being bonded to a second body of refractory material, comprising the steps of providing said second body defining a passageway of greater cross-sectional dimensions than said flow passage surface, said first body being formed in the larger passageway by causing its refractory material to cohere and bond to said second body, by fusion or partial fusion, in situ, said first body being formed and then drilled to define said flow passage.
Claim 18
Dependent Claim
20 words
A method according to claim 15 wherein said first refractory body is composed of fused or partially fused refractory material.
Claim 19
Dependent Claim
33 words
A method according to claim 15, wherein said first refractory body is formed as a relatively high grade refractory body and said second body is formed as a relatively lower grade refractory body.
Claim 20
Dependent Claim
17 words
A method according to claim 15, wherein said first refractory body is formed by a spraying techinque.
Claim 21
Dependent Claim
33 words
A method according to claim 18, wherein said first refractory body is formed by flame spraying a mixture of exothermically oxidizable material and other material so as to form a coherent refractory mass.
Claim 22
Dependent Claim
32 words
A method according to claim 19, wherein said oxidizable material is sprayed in the form of particles having an average size of less than 50 μm and preferably less than 10 μm.
Claim 23
Dependent Claim
28 words
A method according to claim 19, wherein said oxidizable material is sprayed in the form of particles having a specific surface of at least 500 cm 2 /gram.
Claim 24
Dependent Claim
28 words
A method according to claim 19, wherein said oxidizable material is sprayed in the form of particles having a specific surface of at least 3000 cm 2 /gram.
Claim 25
Dependent Claim
24 words
A method according to claim 19, wherein said other material is sprayed in the form of particles having an average size below 500 μm.
Claim 26
Dependent Claim
20 words
A method according to claim 19, wherein said oxidizable material consists at least in part of a metal or metalloid.
Claim 27
Dependent Claim
21 words
A method according to claim 19, wherein said oxidizable material constitutes less than 35 percent by weight of the mixture sprayed.
Claim 28
Dependent Claim
21 words
A method according to claim 19, wherein said other material comprises one or more of zirconia, zircon, silica, alumina, chrome-magnesia, magnesia.
Claim 29
Dependent Claim
19 words
A method according to claim 15, wherein said first refractory body is formed in a sliding gate valve plate.
Claim 30
Dependent Claim
24 words
A method according to claim 27, wherein said valve plate has an integral collector nozzle at least partially lined by said first refractory body.
Claim 31
Dependent Claim
30 words
A method according to claim 15, wherein said first refractory body is formed in a hole made by removing material from around a flow passage of a used refractory article.
Claim 32
Dependent Claim
111 words
A composite refractory article having a flow passage through which a molten metal stream may be conducted and comprising a first body of a relatively high grade refractory material which defines a surface of that passage, said refractory article surrounding a flow passage in a sliding gate valve plate, said first body being bonded to a second body of a relatively lower grade refractory material, wherein said first body is formed within a passageway formed in said second body, such passageway being of greater cross sectional dimesions than said flow passage and in that said first body coheres and bonds to the second body by fusion or partial fusion in situ.
Claim 33
Dependent Claim
111 words
A composite refractory article having a flow passage through which a molten metal stream may be conducted and comprising a first body of a relatively high grade refractory material which defines a surface of that passage, said refractory article surrounding a flow passage in a sliding gate valve plate, said first body being bonded to a second body of a relatively lower grade refractory material, wherein said first body is formed within a passageway formed in said second body, such passageway being of greater cross sectional dimesions than said flow passage and in that said first body coheres and bonds to the second body by fusion or partial fusion in situ.
Claim 34
Dependent Claim
20 words
An article according to claim 30, wherein said first refractory body is composed of fused or partially fused refractory material.
Claim 35
Dependent Claim
22 words
An article according to claim 30, wherein said first refractory body comprises one or more of zirconia, zircon, silica, alumina, chrome-magnesia, magnesia.
Claim 36
Dependent Claim
24 words
An article according to claim 30, wherein said valve plate has an integral collector nozzle at least partially lined by said first refractory body.
Claim 37
Dependent Claim
18 words
An article according to claim 30, wherein the materials of said refractory bodies interpenetrate at a boundary layer.
References Cited (Backward Citations)
US1663660A
Cited
GB694057A
Cited
GB836472A
Cited
GB1330895A
Cited
GB1330894A
Cited
US3685707A
Cited
US3737489A
Cited
US4085894A
Cited
US4192460A
Cited
GB2060842A
Cited
GB2065278A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-02-05 | 1988-08-06 | 1989-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-02-05 | 1992-08-06 | 1993-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-02-05 | 1996-08-06 | 1997-02-05 | $7700.00 | Window Closed / Lapsed |