Polyurethane and method for making stable components thereof
Assignee: Engineered Fabrics Corp
•
Filing: 1983-06-09
•
Granted: 1985-01-29
•
Expires: 2003-06-09
Abstract
Abstract A method for preparing a polyurethane wherein the components thereof have a long shelf life. The formulation is made by separately preparing a prepolymer solution, a crosslinking solution, and a cement solution. Upon utilization, the solutions are mixed together and applied. The urethane has very good fuel resistance and can be used as a coating in fuel tanks as well as to form integral fuel tanks.
Inventors
- 👤 Paul E. Liggett
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:09
CPC Classifications
C; C08; C08L; C08L75/00; C08L75/04; C08L75/06; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0838; C08G18/0842; C08G18/0847; C08G18/0852; C08G18/10; C08K; C08K3/00; C08K3/34; C08L1/00; C08L1/08; C08L1/10; C08L1/14; C08L63/00; C09; C09D; C09D175/00; C09D175/04; C09D175/06; C08G2390/00; C08G2390/40; Y; Y10; Y10S; Y10S524/00; Y10S524/906; Y10S525/00; Y10S525/939
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
368 words
A process for preparing a urethane formulation, comprising the steps of: separately preparing a polymer component, said polymer component comprising a urethane prepolymer and a urethane solvent; the amount of said urethane prepolymer in said urethane component is about 100 parts by weight, wherein said urethane prepolymer is the reaction product of (1) an aliphatic polyisocyanate having from 3 to 12 carbon atoms, or an alicyclic polyisocyanate having from 5 to 25 carbon atoms and (2) a mixed polyester, said mixed polyester being (a) a copolymerization condensation product of, or (b) a separate physical blend of, an aliphatic dicarboxylic acid having from 2 to 12 carbon atoms and an aromatic dicarboxylic acid having from 8 to 12 carbon atoms with (2) a polyol having a molecular weight of 500 or less, the amount of said aliphatic dicarboxylic acid ranging from about 90 percent to about 10 percent by weight, the molecular weight of said polyester made from said acid and said polyol ranging from about 500 to about 4,000, and wherein the equivalent ratio of said isocyanate to the OH end groups in said polyester ranges from about 1.5 to about 3.0; separately preparing a curing component, said curing component comprising a urethane curing agent and a curing agent solvent the equivalent ratio of said curing agent to said isocyante being from about 0.8 to about 1.2; separately preparing a cement component, said cement component comprising about 3 to about 7 parts by weight, per 100 parts by weight of said urethane prepolymer, of an epoxy having solvent leaching resistance, and a solvent; a thixotropic compound, said thixotropic compound located in said curing component, the amount of said thixotropic agent being from about 2 parts by weight to about 8 parts by weight per 100 parts by weight of said urethane prepolymer; maintaining said cement component separate from said polymer component and said curing agent, and maintaining said polymer component separate from said curing component thereby maintaining stability of each of said components; the total amount of solids in said overall formulation ranging from about 20 percent to about 60 percent by weight based upon the total amount of said solvents and said solvents in said overall formulation.
Claim 2
Dependent Claim
368 words
A process for preparing a urethane formulation, comprising the steps of: separately preparing a polymer component, said polymer component comprising a urethane prepolymer and a urethane solvent; the amount of said urethane prepolymer in said urethane component is about 100 parts by weight, wherein said urethane prepolymer is the reaction product of (1) an aliphatic polyisocyanate having from 3 to 12 carbon atoms, or an alicyclic polyisocyanate having from 5 to 25 carbon atoms and (2) a mixed polyester, said mixed polyester being (a) a copolymerization condensation product of, or (b) a separate physical blend of, an aliphatic dicarboxylic acid having from 2 to 12 carbon atoms and an aromatic dicarboxylic acid having from 8 to 12 carbon atoms with (2) a polyol having a molecular weight of 500 or less, the amount of said aliphatic dicarboxylic acid ranging from about 90 percent to about 10 percent by weight, the molecular weight of said polyester made from said acid and said polyol ranging from about 500 to about 4,000, and wherein the equivalent ratio of said isocyanate to the OH end groups in said polyester ranges from about 1.5 to about 3.0; separately preparing a curing component, said curing component comprising a urethane curing agent and a curing agent solvent the equivalent ratio of said curing agent to said isocyante being from about 0.8 to about 1.2; separately preparing a cement component, said cement component comprising about 3 to about 7 parts by weight, per 100 parts by weight of said urethane prepolymer, of an epoxy having solvent leaching resistance, and a solvent; a thixotropic compound, said thixotropic compound located in said curing component, the amount of said thixotropic agent being from about 2 parts by weight to about 8 parts by weight per 100 parts by weight of said urethane prepolymer; maintaining said cement component separate from said polymer component and said curing agent, and maintaining said polymer component separate from said curing component thereby maintaining stability of each of said components; the total amount of solids in said overall formulation ranging from about 20 percent to about 60 percent by weight based upon the total amount of said solvents and said solvents in said overall formulation.
Claim 3
Dependent Claim
83 words
A process according to claim 1, wherein said curing agent is selected from the group consisting of an alkyl diamine having from 2 to 10 carbon atoms, a cycloalkyl diamine having from 4 to 20 carbon atoms, an aromatic or an alkyl substituted aromatic diamine having from 6 to 20 carbon atoms, a polyol having a molecular weight of 500 or less, and wherein the equivalent ratio of said diamine or said polyol to said polyisocyanate ranges from about 0.8 to about 1.2.
Claim 4
Dependent Claim
74 words
A process according to claim 3, wherein the amount of said thixotropic agent ranges from about 2 to about 8 parts by weight, wherein the amount of said epoxy ranges from about 3 to about 7 parts by weight, and an amount of solvent such that the overall formulation has said 20 to 60 percent of solids therein; and wherein said stability of each component has a shelf life of at least ten days.
Claim 5
Dependent Claim
87 words
A process according to claim 3, wherein at least 90 percent of said polyisocyanate is an alkyl diisocyanate having from 6 to 10 carbon atoms or a cycloalkyl diisocyanate having from 8 to 15 carbon atoms wherein said polyol forming said polyester is a glycol having from 2 to 10 carbon atoms, wherein said aliphatic dicarboxylic acid has from 6 to 9 carbon atoms, and wherein the equivalent ratio of said isocyanate to the hydroxyl end groups in said polyester ranges from about 1.8 to about 2.2.
Claim 6
Dependent Claim
151 words
A process according to claim 4, wherein said polyester has a molecular weight of from about 1,000 to about 3,000, wherein said polyol forming said polyester has a molecular weight of 200 or less, wherein the amount of thixotropic agent ranges from about 3 parts to about 6 parts by weight, wherein the amount of solids in said urethane component ranges from about 50 to about 75 percent, wherein the amount of solids in said curing agent component ranges from about 5 to about 30 percent by weight, and wherein the amount of solvent in said cement component ranges from about 25 parts to about 250 parts by weight, based upon 100 parts by weight of said urethane polymer or prepolymer, wherein said curing agent in said curing agent component is a diamine, and wherein the equivalent ratio of said diamine to said isocyanate ranges from about 0.9 to about 0.95.
Claim 7
Dependent Claim
38 words
A process according to claim 5, wherein said thixotropic agent is silicon dioxide, wherein said epoxy is 4,4'-isopropylidenediphenol-epichlorohydrin, and wherein said polyol is hexane diol and wherein said shelf life of each component is at least three weeks.
Claim 8
Dependent Claim
50 words
A process according to claim 6, wherein said polyisocyanate is methylene bis(4-cyclohexylisocyanate), and wherein said aliphatic dicarboxylic acid is azelaic acid, and wherein said aromatic dicarboxylic acid is isophthalic acid, and wherein said diamine is selected from the group consisting of methylenedianiline, (bis-4-aminocyclohexyl) methane, 1,3-bis(aminomethyl)cyclohexane, ethylene diamine, and hexamethylene diamine.
Claim 9
Dependent Claim
54 words
A process according to claim 6, including mixing together said polymeric component, said cement component, and said curing component to form a polyurethane formulation, wherein said thixotropic agent is located in said cure component, including applying said polyurethane formulation to a substrate, and curing said formulation by heating from ambient to about 180° F.
Claim 10
Dependent Claim
44 words
A process according to claim 7, including mixing together said polymeric component, said cement component, and said curing component to form a polyurethane formulation, including applying said polyurethane formulation to a substrate, and curing said formulation by heating from ambient to about 180° F.
Claim 11
Dependent Claim
12 words
A process according to claim 8, wherein said substrate is an airplane.
Claim 12
Dependent Claim
14 words
A process according to claim 9, wherein said substrate is an aircraft wing component.
Claim 13
Dependent Claim
352 words
A polyurethane, said polyurethane made by separately preparing a polymer component, a curing component, and a cement component; said polymer component comprising a urethane prepolymer and a urethane solvent, said curing component comprising a urethane curing agent and a curing agent solvent, said cement component comprising from about 3 to about 7 parts by weight, per 100 parts by weight of said urethane prepolymer, of an epoxy having solvent leaching resistance, and a solvent; the amount of said urethane prepolymer in said urethane component is about 100 parts by weight, wherein said urethane prepolymer is the reaction product of (1) an aliphatic polyisocyanate having from 3 to 12 carbon atoms, or an alicyclic polyisocyanate having from 5 to 25 carbon atoms, (2) a mixed polyester, said mixed polyester being (a) a copolymerization condensation product of, or (b) a separate physical blend of, an aliphatic dicarboxylic acid having from 2 to 12 carbon atoms and an aromatic dicarboxylic acid having from 8 to 12 carbon atoms with (2) a polyol having a molecular weight of 500 or less, the amount of said aliphatic dicarboxylic acid ranging from about 90 percent to about 10 percent by weight, the molecular weight of said polyester made from said acid and said polyol ranging from about 500 to about 4,000, and wherein the equivalent ratio of said isocyanate to the OH end groups in said polyester ranges from about 1.5 to about 3.0; the equivalent ratio of said curing agent to said isocyanate being from about 0.8 to about 1.2; a thixotropic compound, said thixotropic compound located in said curing component, the amount of said thixotropic agent being from about 2 parts by weight to about 8 per 100 parts by weight of said urethane prepolymer; said urethane produced by maintaining said polymer component, said curing component, and said cement component separate from each other until prior to application, maintaining each said component separate from each other and thereby maintaining the stability of each of said components, and subsequently mixing said three components together and curing at a temperature of from about ambient to about 180° F.
Claim 14
Dependent Claim
352 words
A polyurethane, said polyurethane made by separately preparing a polymer component, a curing component, and a cement component; said polymer component comprising a urethane prepolymer and a urethane solvent, said curing component comprising a urethane curing agent and a curing agent solvent, said cement component comprising from about 3 to about 7 parts by weight, per 100 parts by weight of said urethane prepolymer, of an epoxy having solvent leaching resistance, and a solvent; the amount of said urethane prepolymer in said urethane component is about 100 parts by weight, wherein said urethane prepolymer is the reaction product of (1) an aliphatic polyisocyanate having from 3 to 12 carbon atoms, or an alicyclic polyisocyanate having from 5 to 25 carbon atoms, (2) a mixed polyester, said mixed polyester being (a) a copolymerization condensation product of, or (b) a separate physical blend of, an aliphatic dicarboxylic acid having from 2 to 12 carbon atoms and an aromatic dicarboxylic acid having from 8 to 12 carbon atoms with (2) a polyol having a molecular weight of 500 or less, the amount of said aliphatic dicarboxylic acid ranging from about 90 percent to about 10 percent by weight, the molecular weight of said polyester made from said acid and said polyol ranging from about 500 to about 4,000, and wherein the equivalent ratio of said isocyanate to the OH end groups in said polyester ranges from about 1.5 to about 3.0; the equivalent ratio of said curing agent to said isocyanate being from about 0.8 to about 1.2; a thixotropic compound, said thixotropic compound located in said curing component, the amount of said thixotropic agent being from about 2 parts by weight to about 8 per 100 parts by weight of said urethane prepolymer; said urethane produced by maintaining said polymer component, said curing component, and said cement component separate from each other until prior to application, maintaining each said component separate from each other and thereby maintaining the stability of each of said components, and subsequently mixing said three components together and curing at a temperature of from about ambient to about 180° F.
Claim 15
Dependent Claim
99 words
A polyurethane according to claim 12, wherein said curing agent is selected from the group consisting of an alkyl diamine having from 2 to 10 carbon atoms, a cycloalkyl diamine having from 4 to 20 carbon atoms, an aromatic or an alkyl substituted aromatic diamine having from 6 to 20 carbon atoms, a polyol having a molecular weight of 500 or less, and wherein the equivalent ratio of said diamine or said polyol to said polyisocyanate ranges from about 0.8 to about 1.2, and wherein said stability of each component has a shelf life of at least three weeks.
Claim 16
Dependent Claim
140 words
A polyurethane according to claim 13, wherein the amount of said thixotropic agent ranges from about 2 to about 8 parts by weight, wherein the amount of said epoxy ranges from about 3 to about 7 parts by weight, and an amount of solvent such that the overall formulation has said 20 to 60 percent of solids therein, and wherein at least 90 percent of said polyisocyanate is an alkyl diisocyanate having from 6 to 10 carbon atoms or a cycloalkyl diisocyanate having from 8 to 15 carbon atoms, wherein said polyol forming said polyester is a glycol having from 2 to 10 carbon atoms, wherein said aliphatic dicarboxylic acid has from 6 to 9 carbon atoms, and wherein the equivalent ratio of said isocyanate to the hydroxyl end groups in said polyester ranges from about 1.8 to about 2.2.
Claim 17
Dependent Claim
151 words
A polyurethane according to claim 14, wherein said polyester has a molecular weight of from about 1,000 to about 3,000, wherein said polyol forming said polyester has a molecular weight of 200 or less, wherein the amount of thixotropic agent ranges from about 3 parts to about 6 parts by weight, wherein the amount of solids in said urethane component ranges from about 50 to about 75 percent, wherein the amount of solids in said curing agent component ranges from about 5 to about 30 percent by weight, and wherein the amount of solids in said cement component ranges from about 25 parts to about 250 parts by weight, based upon 100 parts by weight of said urethane polymer or prepolymer, wherein said curing agent in said curing agent component is a diamine, and wherein the equivalent ratio of said diamine to said isocyanate ranges from about 0.9 to about 0.95.
Claim 18
Dependent Claim
68 words
A polyurethane according to claim 15, wherein said thixotropic agent is silicon dioxide, wherein said epoxy is 4,4'-isopropylidenediphenol-epichlorohydrin, and wherein said polyisocyanate is methylene bis(4-cyclohexylisocyanate), wherein said aliphatic dicarboxylic acid is azelaic acid, wherein said aromatic dicarboxylic acid is isophthalic acid, and wherein said diamine is selected from the group consisting of methylenedianiline, (bis-4-aminocyclohexyl)methane, or 1,3-bis(aminomethyl)cyclohexane, ethylene diamine, and hexamethylene diamine, and wherein said polyol is hexane diol.
Claim 19
Dependent Claim
19 words
A polyurethane according to claim 14, wherein said urethane is applied to an airplane and forms a sealant layer.
Claim 20
Dependent Claim
13 words
A polyurethane according to claim 16, wherein said urethane forms a fuel tank.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-29 | 1988-07-30 | 1989-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-29 | 1992-07-30 | 1993-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-29 | 1996-07-30 | 1997-01-29 | $7700.00 | Window Closed / Lapsed |