Method for impregnating resin powder directly into a laminate lay up
Assignee: Westinghouse Electric Corp
•
Filing: 1982-04-08
•
Granted: 1985-01-29
•
Expires: 2002-04-08
Abstract
Abstract Dry resin powder can be used to impregnate a laminate lay up, by coating a dry resin powder directly onto a bare fibrous sheet, and then subjecting a plurality of sheets including at least one dry resin-coated sheet to an amount of heat and pressure effective to consolidate the sheets.
Inventors
- 👤 Gerhard R. Sprengling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:04
CPC Classifications
B; B32; B32B; B32B38/00; B32B38/08; B29; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/50; B29C70/504; B32B37/00; B32B37/10; B32B37/1027; B32B37/14; B32B37/24; H; H05; H05K; H05K3/00; H05K3/02; H05K3/022; B29K; B29K2101/00; B29K2101/10; B29K2105/00; B29K2105/25; B29K2105/251; B29L; B29L2031/00; B29L2031/34; B29L2031/3425; B32B2457/00; B32B2457/08; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0366; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2203/00; H05K2203/06; H05K2203/068; H05K2203/15; H05K2203/1545; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
155 words
A method of making a metal clad laminate, useful for circuit boards, comprising the steps of: (A) uniformly applying a uniform deposit of dry, thermosettable, B-staged resin particles as a powder, having a particle size of between about 20 microns and about 1,000 microns, directly onto a bare, porous, fibrous sheet material, to provide a sheet uniformly covered with a uniform deposit of resin powder particles, and having resin powder particles sifted into interstices of the porous sheet, (B) contacting the powder coated sheet with a metal foil sheet, and then (C) applying heat and pressure to the sheets, to cause the resin powder particles on top of and sifted within the fibrous sheet material to melt flow into and through the fibrous sheet material, to fill the pores and impregnate the fibrous sheet material, and to also bond said impregnated sheet material to the metal foil, to provide a unitary, consolidated metal clad laminate.
Claim 2
Independent Claim
155 words
A method of making a metal clad laminate, useful for circuit boards, comprising the steps of: (A) uniformly applying a uniform deposit of dry, thermosettable, B-staged resin particles as a powder, having a particle size of between about 20 microns and about 1,000 microns, directly onto a bare, porous, fibrous sheet material, to provide a sheet uniformly covered with a uniform deposit of resin powder particles, and having resin powder particles sifted into interstices of the porous sheet, (B) contacting the powder coated sheet with a metal foil sheet, and then (C) applying heat and pressure to the sheets, to cause the resin powder particles on top of and sifted within the fibrous sheet material to melt flow into and through the fibrous sheet material, to fill the pores and impregnate the fibrous sheet material, and to also bond said impregnated sheet material to the metal foil, to provide a unitary, consolidated metal clad laminate.
Claim 3
Dependent Claim
37 words
The method of claim 1, where non-pattern the metal foil used in step (B) contacts dry resin powder on top of the bare sheet, and the sheets are heat and pressure consolidated in a continuous laminating machine.
Claim 4
Dependent Claim
15 words
The method of claim 1, where the bare, porous sheet is a fibrous nonwoven material.
Claim 5
Dependent Claim
38 words
The method of claim 1, where the dry powder is applied to a plurality of moving bare, porous sheets in step (A) each powder coated sheet being superimposed on another to form a core layer of sheet material.
Claim 6
Dependent Claim
22 words
The method of claim 4, where the metal foil used in step (B) contacts dry resin powder on top of the core.
Claim 7
Dependent Claim
18 words
The method of claim 4, where the metal foil used in step (B) is a flexible copper foil.
Claim 8
Dependent Claim
26 words
The method of claim 4, where the applied dry resin powder is held in place by infrared heat effective to soften the resin immediately after application.
Claim 9
Dependent Claim
55 words
The method of claim 4, where the bare, porous, fibrous sheets are selected from the group consisting of cellulose paper, cotton fabric, polyester fabric, polyethylene terephthalate sheet, polyamide sheet, mica paper, and glass fabric, and the thermosettable resin power is selected from the group consisting of phenolic resin, melamine resin, epoxy resin, and dicyandiamide-formaldehyde resin.
Claim 10
Dependent Claim
15 words
The method of claim 4, where the bare, porous sheets are a fibrous nonwoven material.
Claim 11
Dependent Claim
29 words
The method of claim 4, where at least one of the bare sheets is glass fabric and the metal foil used in step (B) is a flexible copper foil.
Claim 12
Independent Claim
172 words
A method of making a copper clad laminate, useful for circuit boards, comprising the steps of: (A) uniformly applying a uniform deposit of dry, thermosettable, B-staged resin particles as a powder, having a particle size of between about 20 microns and about 1,000 microns, directly onto a moving, bare, porous, fibrous sheet material, to provide a sheet uniformly covered with a uniform deposit of resin powder particles, and having resin powder particles sifted into interstices of the porous sheet, (B) contacting the moving powder coated sheet with a copper foil sheet, and then (C) continuously applying heat and pressure to the moving sheets in a continuous twin belt press laminating machine, to cause the resin powder particles on top of and sifted within the fibrous sheet material to melt flow into and through the fibrous sheet material, to fill the pores, bond all the fibers together and impregnate the fibrous sheet material, and to also bond said impregnated sheet material to the copper foil, to provide a unitary, consolidated copper clad laminate.
Claim 13
Independent Claim
172 words
A method of making a copper clad laminate, useful for circuit boards, comprising the steps of: (A) uniformly applying a uniform deposit of dry, thermosettable, B-staged resin particles as a powder, having a particle size of between about 20 microns and about 1,000 microns, directly onto a moving, bare, porous, fibrous sheet material, to provide a sheet uniformly covered with a uniform deposit of resin powder particles, and having resin powder particles sifted into interstices of the porous sheet, (B) contacting the moving powder coated sheet with a copper foil sheet, and then (C) continuously applying heat and pressure to the moving sheets in a continuous twin belt press laminating machine, to cause the resin powder particles on top of and sifted within the fibrous sheet material to melt flow into and through the fibrous sheet material, to fill the pores, bond all the fibers together and impregnate the fibrous sheet material, and to also bond said impregnated sheet material to the copper foil, to provide a unitary, consolidated copper clad laminate.
Claim 14
Dependent Claim
15 words
The method of claim 11, where the bare, porous fibrous sheet is a nonwoven material.
Claim 15
Dependent Claim
38 words
The method of claim 11, where the dry powder is applied to a plurality of moving bare, porous sheets in step (A), each powder coated sheet being superimposed on another to form a core layer of sheet material.
Claim 16
Dependent Claim
55 words
The method of claim 11, where the bare, porous, fibrous sheets are selected from the group consisting of cellulose paper, cotton fabric, polyester fabric, polyethylene terephthalate sheet, polyamide sheet, mica paper, and glass fabric, and the thermosettable resin powder is selected from the group consisting of phenolic resin, melamine resin, epoxy resin, and dicyandiamideformaldehyde resin.
References Cited (Backward Citations)
US2199597A
Cited
US3540974A
Cited
US3676269A
Cited
US3916065A
Cited
US4061823A
Cited
US4182791A
Cited
US4164386A
Cited
US4326003A
Cited
US4241469A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-29 | 1988-07-30 | 1989-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-29 | 1992-07-30 | 1993-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-29 | 1996-07-30 | 1997-01-29 | $7700.00 | Window Closed / Lapsed |