Nacreous pigments, their preparation and use

Claim 2

Nacreous pigments having improved transparency and tinctorial strength, comprising mica flakes whose surfaces are coated with a metal oxide layer wherein said metal oxide layer consists essentially of a homogeneous mixture of titanium dioxide, silicon dioxide and aluminum oxide.

Claim 3

Nacreous pigments of claim 1, wherein the metal oxide layer contains about 0.1 to about 20 percent by weight of SiO 2 and about 0.1 to about 20 percent by weight of Al 2 O 3 .

Claim 4

Nacreous pigments of claim 2 wherein, in the metal oxide layer, the amount of SiO 2 is about 1-10 percent by weight.

Claim 5

Nacreous pigments of claim 3 wherein, in the metal oxide layer, the amount of Al 2 O 3 is about 0.2 to about 20 percent by weight.

Claim 6

Nacreous pigments of claim 4 of a particle diameter of 5-200 μm.

Claim 7

Nacreous pigments of claim 2 wherein, in the metal oxide layer, the amount of Al 2 O 3 is about 0.2 to about 20 percent of weight.

Claim 8

Nacreous pigments of claim 2 wherein, in the metal oxide layer, the total amount of SiO 2 and Al 2 O 3 is 0.2-30 percent by weight.

Claim 9

Nacreous pigments of claim 2 wherein, in the metal oxide layer, the total amount of SiO 2 and Al 2 O 3 is 2-20 percent by weight.

Claim 10

A process for preparing nacreous pigments having improved transparency and tinctorial strength and comprising mica flakes whose surfaces are coated with a metal oxide layer wherein the metal oxide layer comprises a homogeneous mixture of titanium dioxide, silicon dioxide and aluminum oxide; comprising coating mica flakes in an aqueous suspension of a pH of about 0.5-5 and a temperature of about 50°-100° C. by including in the suspension an amount of aluminum ions corresponding to the amount to be incorporated into the metal oxide layer and adding to the suspension two solutions at the same time, one a solution of a titanium salt providing an amount of titanium ions corresponding to the amount to be incorporated into the metal oxide layer and the other a basic solution effective to maintain said pH at an essentially constant value and containing an amount of solubilized SiO 2 corresponding to the amount to be incorporated into the metal oxide layer, uniformly co-precipitating onto the mica flakes titanium dioxide hydrate, silicon dioxide and aluminum hydroxide to form a uniform layer homogeneously containing said precipitated components, and then washing, drying and calcining the coated mica flakes.

Claim 11

A process for preparing nacreous pigments having improved transparency and tinctorial strength and comprising mica flakes whose surfaces are coated with a metal oxide layer wherein the metal oxide layer comprises a homogeneous mixture of titanium dioxide, silicon dioxide and aluminum oxide; comprising coating mica flakes in an aqueous suspension of a pH of about 0.5-5 and a temperature of about 50°-100° C. by including in the suspension an amount of aluminum ions corresponding to the amount to be incorporated into the metal oxide layer and adding to the suspension two solutions at the same time, one a solution of a titanium salt providing an amount of titanium ions corresponding to the amount to be incorporated into the metal oxide layer and the other a basic solution effective to maintain said pH at an essentially constant value and containing an amount of solubilized SiO 2 corresponding to the amount to be incorporated into the metal oxide layer, uniformly co-precipitating onto the mica flakes titanium dioxide hydrate, silicon dioxide and aluminum hydroxide to form a uniform layer homogeneously containing said precipitated components, and then washing, drying and calcining the coated mica flakes.

Claim 12

A process of claim 9, wherein the total amount of silicon and aluminum components co-precipitated onto the mica flakes correspond to an amount of about 0.2 to about 30 percent by weight in total of SiO 2 and Al 2 O 3 in the final calcined metal oxide layer.

Claim 13

A process of claim 9 wherein the aluminum is precipitated from a solution of aluminum chloride or aluminum sulfate, the titanium is precipitated from a solution of titanium chloride or titanium sulfate and the silicon is precipitated from a solution of an alkali metal silicate.

Claim 14

A process of claim 9 wherein the precipitation is effected by simultaneously adding to the acidic suspension of the mica platelets an acidic solution of titanium and aluminum.

Claim 15

A process of claim 12 wherein the solution of titanium and aluminum comprises TiCl 4 and AlCl 3 . 6 H 2 O in a ratio of TiCl 4 :AlCl 3 . 6 H 2 O of about 50:1a to about 2:1 and the solution of silicon comprises an alkali metal silicate and NaOH in amounts such that the ratio of silicon as SiO 2 to NaOH is about 5:1 to about 400:1.

Claim 16

In a composition comprising a base ingredient and a pearlescent pigment based on TiO 2 coated mica flakes, the improvement wherein the mica flakes are nacreous pigments having improved transparency and tinctorial strength, comprising mica flakes whose surfaces are coated with a metal oxide layer wherein said metal oxide layer consists essentially of a homogeneous mixture of titanium dioxide, silicon dioxide and aluminum oxide.

Claim 17

In a composition comprising a base ingredient and a pearlescent pigment based on TiO 2 coated mica flakes, the improvement wherein the mica flakes are nacreous pigments having improved transparency and tinctorial strength, comprising mica flakes whose surfaces are coated with a metal oxide layer wherein said metal oxide layer consists essentially of a homogeneous mixture of titanium dioxide, silicon dioxide and aluminum oxide.

Claim 18

A composition of claim 14 wherein the base ingredient is one useful for a plastic, lacquer, paint or cosmetic formulation.