Precipitation hardening austenitic superalloys
Assignee: United States Department of Energy
•
Filing: 1982-04-21
•
Granted: 1985-01-22
•
Expires: 2002-04-21
Abstract
Abstract Precipitation hardening, austenitic type superalloys are described. These alloys contain 0.5 to 1.5 weight percent silicon in combination with about 0.05 to 0.5 weight percent of a post irradiation ductility enhancing agent selected from the group of hafnium, yttrium, lanthanum and scandium, alone or in combination with each other. In addition, when hafnium or yttrium are selected, reductions in irradiation induced swelling have been noted.
Inventors
- 👤 Michael K. Korenko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:57
CPC Classifications
G; G21; G21C; G21C3/00; G21C3/02; G21C3/04; G21C3/06; G21C3/07; C; C22; C22C; C22C38/00; C22C38/18; C22C38/40; C22C38/50; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
97 words
An iron base, gamma prime precipitation hardening austenitic superalloy having improved ductility characteristics after neutron irradiation in a fast breeder nuclear reactor, comprising an iron-nickel-chromium alloy including about 0.05-0.5 weight percent of a ductility enhancing agent selected from the group consisting of yttrium, hafnium and scandium, alone or in combination with each other, titanium and aluminum in amounts effective to produce gamma prime hardening during thermal aging outside of said fast breeder nuclear reactor and silicon in an amount effective through interaction with said ductility enhancing agent to enhance the post neutron irradiation ductility of said alloy.
Claim 2
Dependent Claim
97 words
An iron base, gamma prime precipitation hardening austenitic superalloy having improved ductility characteristics after neutron irradiation in a fast breeder nuclear reactor, comprising an iron-nickel-chromium alloy including about 0.05-0.5 weight percent of a ductility enhancing agent selected from the group consisting of yttrium, hafnium and scandium, alone or in combination with each other, titanium and aluminum in amounts effective to produce gamma prime hardening during thermal aging outside of said fast breeder nuclear reactor and silicon in an amount effective through interaction with said ductility enhancing agent to enhance the post neutron irradiation ductility of said alloy.
Claim 3
Dependent Claim
19 words
The superalloy according to claim 1 wherein silicon comprises about 0.5 to about 1.5 weight percent of said alloy.
Claim 4
Dependent Claim
15 words
The superalloy according to claim 1 or 2 wherein said ductility enhancing agent is yttrium.
Claim 5
Dependent Claim
15 words
The superalloy according to claim 1 wherein said alloy contains said gamma prime phase alloy.
Claim 6
Dependent Claim
14 words
The superalloy according to claim 2 wherein said alloy contains said gamma prime phase.
Claim 7
Dependent Claim
80 words
A gamma prime strengthened austenitic superalloy comprising: about 7-17 weight percent chromium; about 24-45 weight percent nickel; about 2-3.8 weight percent titanium; about 0.5-2.2 weight percent aluminum; about 0.8-3.5 weight percent molybdenum; about 0.5-1.5 weight percent silicon; about 0.03-0.06 weight percent carbon; about 0.05-0.5 weight percent of an element selected from the group consisting of yttrium, hafnium and scandium, alone or in combination with each other; and wherein iron is essentially the balance of said gamma prime strengthened austenitic superalloy.
Claim 8
Dependent Claim
80 words
A gamma prime strengthened austenitic superalloy comprising: about 7-17 weight percent chromium; about 24-45 weight percent nickel; about 2-3.8 weight percent titanium; about 0.5-2.2 weight percent aluminum; about 0.8-3.5 weight percent molybdenum; about 0.5-1.5 weight percent silicon; about 0.03-0.06 weight percent carbon; about 0.05-0.5 weight percent of an element selected from the group consisting of yttrium, hafnium and scandium, alone or in combination with each other; and wherein iron is essentially the balance of said gamma prime strengthened austenitic superalloy.
Claim 9
Dependent Claim
15 words
The superalloy according to claim 6 further comprising up to about 2 weight percent manganese.
Claim 10
Dependent Claim
37 words
The superalloy according to claim 6 wherein said superalloy has improved fast neutron irradiation swelling properties and wherein said element is selected from the group consisting of hafnium and yttrium, alone or in combination with each other.
Claim 11
Dependent Claim
20 words
A duct for fuel pins, wherein said duct is comprised of the superalloy according to claim 1, 2 or 6.
Claim 12
Dependent Claim
15 words
A fuel pin cladding comprised of the superalloy according to claim 1, 2 or 6.
Claim 13
Dependent Claim
39 words
The superalloy according to claim 4, 5 or 6 fabricated by the process comprising the steps of: solution treating said superalloy; later aging said superalloy; and subsequently placing said superalloy in said fast breeder reactor in an aged condition.
Claim 14
Dependent Claim
32 words
The superalloy according to claim 1 or 2 fabricated by the process comprising the step of: cold working said superalloy; and later placing said superalloy in pile in a cold worked condition.
Claim 15
Dependent Claim
34 words
The superalloy fabricated by the process according to claim 12 further comprising the step of: aging said superalloy after said cold working and prior to placing said superalloy in said fast breeder nuclear reactor.
Claim 16
Dependent Claim
111 words
A gamma prime precipitation hardening austenitic superalloy having the following nominal composition: about 25 weight percent Ni; about 7.5 weight percent Cr; about 1.0 weight percent Si; about 1.0 weight percent Mo; about 0.2 weight percent Mn; about 0.05 weight percent Zr; about 3.3 weight percent Ti; about 1.7 weight percent Al; about 0.05 weight percent C; about 0.005 weight percent B; about 0.2 weight percent of an agent for enhancing the post neutron irradiation ductility of said superalloy after neutron irradiation in a fast breeder reactor selected from the group consisting of Sc, Y, La, and Hf, alone or in combination with each other; and the balance being essentially Fe.
Claim 17
Dependent Claim
111 words
A gamma prime precipitation hardening austenitic superalloy having the following nominal composition: about 25 weight percent Ni; about 7.5 weight percent Cr; about 1.0 weight percent Si; about 1.0 weight percent Mo; about 0.2 weight percent Mn; about 0.05 weight percent Zr; about 3.3 weight percent Ti; about 1.7 weight percent Al; about 0.05 weight percent C; about 0.005 weight percent B; about 0.2 weight percent of an agent for enhancing the post neutron irradiation ductility of said superalloy after neutron irradiation in a fast breeder reactor selected from the group consisting of Sc, Y, La, and Hf, alone or in combination with each other; and the balance being essentially Fe.
Claim 18
Dependent Claim
25 words
The alloy according to claim 14 wherein said agent for enhancing post neutron irradiation ductility is selected from the group consisting of Y and Hf.
Claim 19
Dependent Claim
13 words
The superalloy according to claim 2 wherein said ductility enhancing agent is scandium.
Claim 20
Dependent Claim
13 words
The superalloy according to claim 2 wherein said ductility enhancing agent is hafnium.
Claim 21
Dependent Claim
11 words
The superalloy according to claim 6 wherein said element is yttrium.
Claim 22
Dependent Claim
17 words
The alloy according to claim 14 wherein said agent for enhancing post neutron irradiation ductility is Y.
Claim 23
Dependent Claim
21 words
The alloy according to claim 6 wherein said element is limited to a concentration of about 0.2 to 0.5 weight percent.
Claim 24
Dependent Claim
23 words
The alloy according to claim 1 wherein said ductility enhancing agent is limited to a concentration of about 0.2 to 0.5 weight percent.
Claim 25
Dependent Claim
23 words
The alloy according to claim 2 wherein said ductility enhancing agent is limited to a concentration of about 0.2 to 0.5 weight percent.
References Cited (Backward Citations)
US2581420A
Cited
US2687954A
Cited
US3170847A
Cited
US3563728A
Cited
US3746536A
Cited
JPS49109116A
Cited
US4144380A
Cited
US4261767A
Cited
US4158606A
Cited
US4234385A
Cited
US4236943A
Cited
US4359350A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-22 | 1988-07-23 | 1989-01-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-22 | 1992-07-23 | 1993-01-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-22 | 1996-07-23 | 1997-01-22 | $7700.00 | Window Closed / Lapsed |