Alloy resistant to high temperature oxidation
Assignee: Imphy SA
•
Filing: 1978-12-14
•
Granted: 1981-04-14
•
Expires: 1998-12-14
Abstract
Abstract An alloy which is resistant to high temperature oxidation includes by weight 15 to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4 to 6% of aluminum and at least 0.001% of at least one metal belonging to the group formed by the rare earths and metals in the same category, such as yttrium and scandium.
Inventors
- 👤 James H. Davidson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:52
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/18; C22C38/40
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
139 words
An alloy having good forgeability and resistance to high temperature oxidation, consisting essentially of, by weight, 15% to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4% to 6% of aluminum capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austenitic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal capable of increasing resistance to oxidation at a value greater than the value of the resistance to oxidation of the corresponding matrix iron, chromium, nickel, aluminum and selected from the group consisting of rare earths and metals of the same category capable for increasing the resistance to oxidation in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 2
Dependent Claim
139 words
An alloy having good forgeability and resistance to high temperature oxidation, consisting essentially of, by weight, 15% to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4% to 6% of aluminum capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austenitic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal capable of increasing resistance to oxidation at a value greater than the value of the resistance to oxidation of the corresponding matrix iron, chromium, nickel, aluminum and selected from the group consisting of rare earths and metals of the same category capable for increasing the resistance to oxidation in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 3
Dependent Claim
100 words
An alloy having good forgeability and resistance to high temperature oxidation, consisting essentially of, by weight, 15% to 30% of chromium, at least 10% nickel, at least 20% of iron, 4% to 6% of aluminum, capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austenitic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal selected from the group consisting of yttrium, cerium and lanthanum in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 4
Dependent Claim
100 words
An alloy having good forgeability and resistance to high temperature oxidation, consisting essentially of, by weight, 15% to 30% of chromium, at least 10% nickel, at least 20% of iron, 4% to 6% of aluminum, capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austenitic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal selected from the group consisting of yttrium, cerium and lanthanum in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 5
Dependent Claim
101 words
An alloy having good forgeability and resistance to high temperature oxidation consisting essentially of, by weight, 15% to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4% to 6% of aluminum capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austeno-ferritic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal selected from the group consisting of cerium, lanthanum, and yttrium in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 6
Dependent Claim
101 words
An alloy having good forgeability and resistance to high temperature oxidation consisting essentially of, by weight, 15% to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4% to 6% of aluminum capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austeno-ferritic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal selected from the group consisting of cerium, lanthanum, and yttrium in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 7
Dependent Claim
106 words
An alloy having good forgeability and resistance to high temperature oxidation consisting essentially of, by weight, 15% to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4% to 6% of aluminum capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austeno-ferritic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal selected from the group consisting of the rare earths and metals in the same category in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
Claim 8
Dependent Claim
106 words
An alloy having good forgeability and resistance to high temperature oxidation consisting essentially of, by weight, 15% to 30% of chromium, at least 10% of nickel, at least 20% of iron, 4% to 6% of aluminum capable of forming a protective layer of alumina, the iron, nickel and chromium contents being approximately defined in the austeno-ferritic field of FIG. 1, up to 0.15% of silicon, up to 0.4% of carbon, at least one metal selected from the group consisting of the rare earths and metals in the same category in an amount from 0.001% to 0.03% in solid solution and not combined with sulfur or oxygen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-13 | 1984-10-13 | 1985-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-13 | 1988-10-13 | 1989-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-13 | 1992-10-13 | 1993-04-14 | $7700.00 | Window Closed / Lapsed |