Process for forming microcrystalline silicon material and product
Assignee: Atlantic Richfield Co
•
Filing: 1983-09-29
•
Granted: 1985-01-08
•
Expires: 2003-09-29
Abstract
Abstract A process for forming microcrystalline silicon material includes the steps of introducing a silicon-containing gas, hydrogen gas and a relatively inert gas into a work environment to form a preselected gas atmosphere, and establishing a glow discharge through the gas atmosphere. A microcrystalline thin film of silicon is formed on a substrate exposed to the discharge. In a preferred embodiment, the power level of the discharge is less than 0.08 watts per square centimeter and the film is deposited at a rate of no more than approximately two angstroms per second. Under these circumstances, the material deposited on the substrate is bombarded by ions of the relatively inert gas, causing the material to form a microcrystalline thin film.
Inventors
- 👤 David P. Tanner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 06:59
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/24; H; H10; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2922; H10P14/32; H10P14/3202; H10P14/3204; H10P14/3211; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3438; H10P14/3441; H10P14/3442
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
115 words
A process for forming microcrystalline silicon comprising the steps of: introducing a silicon-containing gas, hydrogen gas and a relatively inert gas into a work environment to form a preselected gas atmosphere; the relative concentration of the inert gas being no less than approximately 10 volumetric percent and no more than approximately 50 volumetric percent, and the gas atmosphere being maintained at a flow rate of no more than approximately 5×10 -3 SCCM per cubic centimeter within the work environment; establishing a glow discharge through the gas atmosphere; at a power level less than 0.3 watts per square centimeter; and exposing a substrate to the glow discharge to form a microcrystalline thin film of silicon thereon.
Claim 2
Dependent Claim
115 words
A process for forming microcrystalline silicon comprising the steps of: introducing a silicon-containing gas, hydrogen gas and a relatively inert gas into a work environment to form a preselected gas atmosphere; the relative concentration of the inert gas being no less than approximately 10 volumetric percent and no more than approximately 50 volumetric percent, and the gas atmosphere being maintained at a flow rate of no more than approximately 5×10 -3 SCCM per cubic centimeter within the work environment; establishing a glow discharge through the gas atmosphere; at a power level less than 0.3 watts per square centimeter; and exposing a substrate to the glow discharge to form a microcrystalline thin film of silicon thereon.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein: the power level of the discharge is less than 0.08 watts per square centimeter.
Claim 4
Dependent Claim
23 words
The process of claim 2 wherein: the relatively inert gas is chosen from the group consisting of helium, neon, argon, krypton and xenon.
Claim 5
Dependent Claim
27 words
The process of claim 3 wherein: the gas atmosphere includes the silicon-containing gas, hydrogen gas and the inert gas in a relative volumetric abundance of approximately 1:5:5.
Claim 6
Dependent Claim
19 words
The process of claim 3 wherein: a dopant-containing gas is introduced into the work environment to dope the film.
Claim 7
Dependent Claim
13 words
The process of claim 5 wherein: the dopant-containing gas comprises PH 3 .
Claim 8
Dependent Claim
20 words
The process of claim 3 wherein: the glow discharge is an rf discharge between a pair of capacitively-coupled electrode means.
Claim 9
Dependent Claim
32 words
The product by the process of claim 2 which has a dark conductivity of at least approximately 0.1 inverse ohm-centimeters and an activation energy of no more than approximately 0.03 electron volts.
Claim 10
Dependent Claim
14 words
The product of claim 8 which has a conductivity greater than 1.0 inverse ohm-centimeter.
Claim 11
Dependent Claim
22 words
The process of claim 2 wherein: the film is deposited at a rate of no more than approximately 2 angstroms per second.
Claim 12
Dependent Claim
19 words
The process of claim 10 wherein: the substrate is exposed to the discharge for at least approximately ten minutes.
Claim 13
Dependent Claim
25 words
The process of claim 11 wherein: the microcrystalline film is formed by bombarding material deposited on the substrate with ions of the relatively inert material.
Claim 14
Dependent Claim
20 words
The process of claim 11 wherein: the gas atmosphere is maintained at a pressure of at least approximately 1 torr.
Claim 15
Dependent Claim
32 words
The product by the process of claim 13 which has a dark conductivity of at least approximately 0.1 inverse ohm-centimeters and an activation energy of no more than approximately 0.03 electron volts.
Claim 16
Dependent Claim
128 words
A process for forming microcrystalline silicon comprising the steps of: introducing silane, hydrogen gas and argon into a work environment to form a preselected gas atmosphere at a pressure of at least 1 torr, the relative volumetric abundance of silane, hydrogen gas and argon in the atmosphere being approximately 1:5:5 and the atmosphere being maintained at a flow rate of no more than approximately 5×10 -3 SCCM per cubic centimeter within the work environment; establishing a glow discharge through the gas atmosphere at a power level less than 0.08 watts per square centimeter; and exposing a substrate to the glow discharge for at least approximately 10 minutes to form a microcrystalline thin film of silicon thereon at a rate of between approximately 1 and 2 angstroms per second.
Claim 17
Dependent Claim
128 words
A process for forming microcrystalline silicon comprising the steps of: introducing silane, hydrogen gas and argon into a work environment to form a preselected gas atmosphere at a pressure of at least 1 torr, the relative volumetric abundance of silane, hydrogen gas and argon in the atmosphere being approximately 1:5:5 and the atmosphere being maintained at a flow rate of no more than approximately 5×10 -3 SCCM per cubic centimeter within the work environment; establishing a glow discharge through the gas atmosphere at a power level less than 0.08 watts per square centimeter; and exposing a substrate to the glow discharge for at least approximately 10 minutes to form a microcrystalline thin film of silicon thereon at a rate of between approximately 1 and 2 angstroms per second.
Claim 18
Dependent Claim
17 words
The product by the process of claim 15 which has a conductivity greater than 1.0 inverse ohm-centimeter.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-08 | 1988-07-09 | 1989-01-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-08 | 1992-07-09 | 1993-01-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-08 | 1996-07-09 | 1997-01-08 | $7700.00 | Window Closed / Lapsed |