Vinylidene chloride-containing copolymer latices
Assignee: DeSoto Inc
•
Filing: 1983-10-06
•
Granted: 1984-12-25
•
Expires: 2003-10-06
Abstract
Abstract An aqueous latex is disclosed which possesses improved water resistance for use in exterior paints. This latex comprises an aqueous emulsion copolymer of monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of at least about 20% of vinyl acetate and monoethylenic ester, preferably acrylic or methacrylic esters, which provide the copolymer with a glass transition temperature in the range of -10° C. to +10° C., these monomers including from about 0.1% to 10.0% of a monomer promoting adhesion. The copolymerization is carried out in aqueous emulsion at a pH of 3-6 and the vinylidene chloride is preferably introduced at or near the bottom of a reactor maintained at atmospheric pressure. It is also preferred to introduce the vinylidene chloride after polymerization has been initiated with the other monomers.
Inventors
- 👤 James E. Devona
- 👤 Martin L. Essigmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:04
CPC Classifications
C; C08; C08F; C08F214/00; C08F214/02; C08F214/04; C08F214/08; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C08F220/16; C08F220/18; C08F220/1804
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
95 words
An aqueous latex comprising an aqueous emulsion copolymer of monoethylenically unsaturated monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of at least about 20% of vinyl acetate and monoethylenic acrylate or methacrylate ester with an alkanol containing from 2-8 carbon atoms providing the copolymer with a glass transition temperature in the range of -10° C. to +10° C., said monomers including from about 0.1% to 10.0% of an adhesion promoting monomer which contains a ureido hydrogen atom, said proportions being based on the total weight of monomers copolymerized.
Claim 2
Dependent Claim
95 words
An aqueous latex comprising an aqueous emulsion copolymer of monoethylenically unsaturated monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of at least about 20% of vinyl acetate and monoethylenic acrylate or methacrylate ester with an alkanol containing from 2-8 carbon atoms providing the copolymer with a glass transition temperature in the range of -10° C. to +10° C., said monomers including from about 0.1% to 10.0% of an adhesion promoting monomer which contains a ureido hydrogen atom, said proportions being based on the total weight of monomers copolymerized.
Claim 3
Dependent Claim
24 words
A latex as recited in claim 1 in which said monomers are provided in aqueous emulsion having a pH in the range of 3-6.
Claim 4
Dependent Claim
29 words
A latex as recited in claim 1 in which said adhesion promoting monomer is a monoethylenically unsaturated derivative of an ethylene urea present in amount of 0.5% to 3%.
Claim 5
Dependent Claim
22 words
A latex as recited in claim 1 in which said vinyl acetate is present in an amount of from 20% to 50%.
Claim 6
Dependent Claim
22 words
A latex as recited in claim 3 in which said vinyl acetate is present in an amount of from 30% to 40%.
Claim 7
Dependent Claim
33 words
A latex as recited in claim 1 in which said ester is n-butyl acrylate used in a proportion which provides a glass transition temperature in the range of -5° C. to +5° C.
Claim 8
Dependent Claim
94 words
An aqueous latex comprising an aqueous emulsion copolymer of monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of 30% to 40% of vinyl acetate with acrylic or methacrylic esters with an alkanol containing from 2-8 carbon atoms which provides the copolymer with a glass transition temperature in the range of -5° C. to +5° C., said monomers including from about 0.5% to 3.0% of a monoethylenically unsaturated derivative of ethylene urea providing a ureido hydrogen atom, said proportions being based on the total weight of monomers copolymerized.
Claim 9
Dependent Claim
94 words
An aqueous latex comprising an aqueous emulsion copolymer of monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of 30% to 40% of vinyl acetate with acrylic or methacrylic esters with an alkanol containing from 2-8 carbon atoms which provides the copolymer with a glass transition temperature in the range of -5° C. to +5° C., said monomers including from about 0.5% to 3.0% of a monoethylenically unsaturated derivative of ethylene urea providing a ureido hydrogen atom, said proportions being based on the total weight of monomers copolymerized.
Claim 10
Dependent Claim
10 words
an aqueous latex paint comprising the latex of claim 1.
Claim 11
Dependent Claim
20 words
An aqueous latex paint as recited in claim 9 in which said latex is neutralized to a pH of 6.5-8.0.
Claim 12
Independent Claim
119 words
A method of providing an aqueous latex characterized by superior resistance to water vapor transmission comprising, copolymerizing in aqueous emulsion monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of at least about 20% of vinyl acetate and acrylic or methacrylic esters with an alkanol containing from 2-8 carbon atoms which provide the copolymer with a glass transition temperature in the range of -10° C. to +10° C., said monomers including from about 0.1% to 10.0% of an adhesion promoting monomer which contains a ureido hydrogen atom, said proportions being based on the total weight of monomers copolymerized, and said copolymerization being carried out at a pH in the range of pH 3-6.
Claim 13
Independent Claim
119 words
A method of providing an aqueous latex characterized by superior resistance to water vapor transmission comprising, copolymerizing in aqueous emulsion monomers consisting essentially of from 15% to 40% of vinylidene chloride together with a mixture of at least about 20% of vinyl acetate and acrylic or methacrylic esters with an alkanol containing from 2-8 carbon atoms which provide the copolymer with a glass transition temperature in the range of -10° C. to +10° C., said monomers including from about 0.1% to 10.0% of an adhesion promoting monomer which contains a ureido hydrogen atom, said proportions being based on the total weight of monomers copolymerized, and said copolymerization being carried out at a pH in the range of pH 3-6.
Claim 14
Dependent Claim
47 words
A method as recited in claim 10 in which said polymerization is carried out at atmospheric pressure in an open reactor at a temperature above the boiling point of vinylidene chloride, and said vinylidene chloride is introduced into the polymerization reactor at or near the bottom thereof.
Claim 15
Dependent Claim
27 words
A method as recited in claim 10 in which the addition of vinylidene chloride is delayed until after the polymerization has been initiated with the other monomers.
References Cited (Backward Citations)
CA682007A
Cited
US3483154A
Cited
US3832317A
Cited
US3922451A
Cited
US4104220A
Cited
US4111877A
Cited
US4429095A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-25 | 1988-06-25 | 1988-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-25 | 1992-06-25 | 1992-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-25 | 1996-06-25 | 1996-12-25 | $7700.00 | Window Closed / Lapsed |