Implosive consolidation of a particle mass including amorphous material
Assignee: Oregon Health & Science University
•
Filing: 1983-09-08
•
Granted: 1984-12-25
•
Expires: 2003-09-08
Abstract
Abstract A method for the implosive consolidation into a solid body of a mass of free particles, which mass consists, selectively, entirely of amorphous particles, or a mixture of amorphous and nonamorphous particles. During the consolidation act, pressure and temperature are controlled in a manner which assures that the consolidated amorphous particles in the solid body exhibit substantially the same amorphous characteristics as those displayed by the unconsolidated, free amorphous particles.
Inventors
- 👤 Alan W. Hare
- 👤 Lawrence E. Murr
- 👤 F. Paul Carlson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 04:25
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/006; B22F3/02; B22F3/08; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/94; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/4902; Y10T29/49075; Y10T29/49076
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
108 words
A method for the implosive consolidation, into a solid body, of a particulate mass comprising free amorphous particles, said method including the steps of assembling such a mass to define, in the assembled but unconsolidated state, a chosen configuration for such a body, imploding the assembled mass by an external, substantially surrounding explosive force in a manner bonding the particles in the mass as a unit to form a solid body having such chosen configuration, and controlling said imploding in such a fashion that the contribution made to such body by such amorphous particles retains substantially the same amorphous characteristics as those exhibited by the unconsolidated amorphous particles.
Claim 2
Independent Claim
108 words
A method for the implosive consolidation, into a solid body, of a particulate mass comprising free amorphous particles, said method including the steps of assembling such a mass to define, in the assembled but unconsolidated state, a chosen configuration for such a body, imploding the assembled mass by an external, substantially surrounding explosive force in a manner bonding the particles in the mass as a unit to form a solid body having such chosen configuration, and controlling said imploding in such a fashion that the contribution made to such body by such amorphous particles retains substantially the same amorphous characteristics as those exhibited by the unconsolidated amorphous particles.
Claim 3
Dependent Claim
20 words
The method of claim 1 which is performed with a particulate mass including a mixture of amorphous and nonamorphous particles.
Claim 4
Independent Claim
145 words
A method for the implosive consolidation, into a solid body, of a particulate mass comprising free amorphous particles, where such amorphous particles are characterized by a known co-consolidation interface pressure and a known antiamorphic temperature limit, said method including the steps of assembling such a mass to define, in the assembled but unconsolidated state, a chosen configuration for such a body, producing an explosion in a region at least partially surrounding the assembled mass to create an imploding force thereon which generates a pressure on the totality of the assembled mass that is at least equal to such co-consolidation interface pressure, and which creates, in the space occupied by the mass, a temperature throughout the duration of the explosion which is less than such antiamorphic temperature limit, and by said producing, imploding the assembled mass to form such a body having such a chosen configuration.
Claim 5
Independent Claim
145 words
A method for the implosive consolidation, into a solid body, of a particulate mass comprising free amorphous particles, where such amorphous particles are characterized by a known co-consolidation interface pressure and a known antiamorphic temperature limit, said method including the steps of assembling such a mass to define, in the assembled but unconsolidated state, a chosen configuration for such a body, producing an explosion in a region at least partially surrounding the assembled mass to create an imploding force thereon which generates a pressure on the totality of the assembled mass that is at least equal to such co-consolidation interface pressure, and which creates, in the space occupied by the mass, a temperature throughout the duration of the explosion which is less than such antiamorphic temperature limit, and by said producing, imploding the assembled mass to form such a body having such a chosen configuration.
Claim 6
Dependent Claim
20 words
The method of claim 3 which is performed with a particulate mass including a mixture of amorphous and nonamorphous particles.
Claim 7
Independent Claim
83 words
A method for the implosive consolidation of free amorphous particles into a solid amorphous body comprising assembling such particles to define, in the assembled but unconsolidated state, a chosen configuration for such a body, and imploding the assembled particles by an external, substantially surrounding explosive force in a manner bonding the particles as a unit to form such a solid body having such a chosen configuration, with the body of bonded particles exhibiting substantially the same amorphic characteristics as did the prebonded particles.
Claim 8
Independent Claim
83 words
A method for the implosive consolidation of free amorphous particles into a solid amorphous body comprising assembling such particles to define, in the assembled but unconsolidated state, a chosen configuration for such a body, and imploding the assembled particles by an external, substantially surrounding explosive force in a manner bonding the particles as a unit to form such a solid body having such a chosen configuration, with the body of bonded particles exhibiting substantially the same amorphic characteristics as did the prebonded particles.
Claim 9
Independent Claim
137 words
A method for the implosive consolidation of free amorphous particles into a solid amorphous body, where such particles are characterized by a known co-consolidation interface pressure and a known antiamorphic temperature limit, said method comprising assembling such particles to define, in the assembled but unconsolidated state, a chosen configuration for such a body, producing an explosion in a region at least partially surrounding the assembled particles to create an imploding force thereon which generates a pressure on the totality of the assembled particles that is at least equal to such co-consolidation interface pressure, and which creates, in the space occupied by the particles, a temperature throughout the duration of the explosion which is less than such antiamorphic temperature limit, and by said producing, imploding the particles to form such a consolidated body having such a chosen configuration.
Claim 10
Independent Claim
137 words
A method for the implosive consolidation of free amorphous particles into a solid amorphous body, where such particles are characterized by a known co-consolidation interface pressure and a known antiamorphic temperature limit, said method comprising assembling such particles to define, in the assembled but unconsolidated state, a chosen configuration for such a body, producing an explosion in a region at least partially surrounding the assembled particles to create an imploding force thereon which generates a pressure on the totality of the assembled particles that is at least equal to such co-consolidation interface pressure, and which creates, in the space occupied by the particles, a temperature throughout the duration of the explosion which is less than such antiamorphic temperature limit, and by said producing, imploding the particles to form such a consolidated body having such a chosen configuration.
References Cited (Backward Citations)
US3081498A
Cited
SU784989A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-25 | 1988-06-25 | 1988-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-25 | 1992-06-25 | 1992-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-25 | 1996-06-25 | 1996-12-25 | $7700.00 | Window Closed / Lapsed |