Assignee: International Business Machines Corp
•
Filing: 1984-01-24
•
Granted: 1984-12-25
•
Expires: 2004-01-24
Abstract
Abstract Disclosed is a method of etching a metallized substrate by laser radiation. The substrate is exposed to a selected gas which spontaneously reacts with the metal forming a solid reaction product with the metal by a partial consumption of the metal. A beam of radiation of a wavelength suitable for absorption by the reaction product and/or by the metal thereunder is applied in a desired pattern to vaporize the reaction product and thereby selectively etch the metal.
Inventors
- 👤 Lee Chen
- 👤 Tung J. Chuang
- 👤 Gangadhara S. Mathad
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:28
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/02; H05K3/027; C; C23; C23F; C23F4/00; C23F4/02
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
77 words
A method of radiation induced dry etching of a metallized substrate comprising the steps of: (a) mounting the substrate in a reaction chamber, (b) establishing a predetermined low pressure in the chamber; (c) controllably introducing a selected gas into the chamber to form a solid reaction product with the metal by a partial consumption of said metal; and (d) selectively removing the reaction product by applying a beam of laser radiation and thereby selectively etching the metal.
Claim 2
Independent Claim
77 words
A method of radiation induced dry etching of a metallized substrate comprising the steps of: (a) mounting the substrate in a reaction chamber, (b) establishing a predetermined low pressure in the chamber; (c) controllably introducing a selected gas into the chamber to form a solid reaction product with the metal by a partial consumption of said metal; and (d) selectively removing the reaction product by applying a beam of laser radiation and thereby selectively etching the metal.
Claim 3
Dependent Claim
24 words
The method as in claim 1 wherein said radiation is of a wavelength suitable for absorption by said reaction product or by said metal.
Claim 4
Dependent Claim
23 words
The method as in claim 2 wherein said reaction product is removed by said radiation by thermal and electronic excitation and eventual vaporization.
Claim 5
Dependent Claim
12 words
The method as in claim 2 wherein gas is a halogen gas.
Claim 6
Dependent Claim
14 words
The method as in claim 2 wherein said gas is a halogen based gas.
Claim 7
Dependent Claim
11 words
The method as in claim 4 wherein said gas is chlorine.
Claim 8
Dependent Claim
18 words
The method as in claim 6 wherein said metal is copper and said reaction product is copper chloride.
Claim 9
Dependent Claim
18 words
The method as in claim 6 wherein said metal is Chromium and said reaction product is chromium chloride.
Claim 10
Dependent Claim
17 words
The method as in claim 7 or 8 wherein said radiation is generated by a Nd:YAG laser.
Claim 11
Dependent Claim
17 words
The method as in claim 7 or 8 wherein said radiation is generated by an argon laser.
Claim 12
Dependent Claim
30 words
The method as in claim 9 wherein the wavelength of said Nd:YAG laser is selected from the group of component wavelengths consisting of 1060 nm, 532 nm and 355 nm.
Claim 13
Dependent Claim
22 words
The method as in claim 10 wherein said argon laser is a continuous wave laser operating at a wavelength of 515 nm.
Claim 14
Dependent Claim
30 words
The method as in claim 5 wherein radiation is of a wavelength suitable also for dissociating the halogen based gas into reactant radicals to enhance formation of said reaction product.
Claim 15
Dependent Claim
43 words
The method as in claim 13 wherein said laser is selected from the group consisting of a continuous wave argon laser operating at the wavelength of 515 nm and pulsed Nd:YAG lasers operating at the wavelengths of 532 nm and 355 nm, respectively.
Claim 16
Dependent Claim
28 words
The method as in claim 14 wherein said gas is thermally dissociated into reactant radicals and said reaction product is removed by thermal excitation by said laser radiation.
Claim 17
Dependent Claim
51 words
The method as in claim 5 wherein said radiation comprises ultraviolet component and non-ultraviolet component wavelengths, said ultraviolet component being suitable for dissociating said halogen based gas into reactant radicals to enhance formation of said reaction product and said non-ultraviolet component being suitable for excitation and removal of said reaction product.
Claim 18
Dependent Claim
32 words
The method as in claim 16 wherein said radiation is generated by a Nd:YAG laser, said ultraviolet component is of 355 nm wavelength and said non-ultraviolet component is of 1060 nm wavelength.
Claim 19
Dependent Claim
48 words
The method as in claim 5 wherein the wavelength of said laser radiation is in the non-ultraviolet region, said method further comprising applying ultraviolet radiation in simultaneous relationship with said laser beam to dissociate said halogen based gas into reactant radicals to enhance formation of said reaction product.
Claim 20
Dependent Claim
17 words
The method as in claim 18 wherein said ultraviolet radiation is generated by a UV flood lamp.
Claim 21
Dependent Claim
19 words
The method as in claim 18 wherein said laser is Nd:YAG laser operating at a wavelength of 1060 nm.
Claim 22
Independent Claim
95 words
A method of radiation induced dry etching of a metal layer formed on a substrate, said method comprising: reacting said metal layer with a halogen gas forming a solid metal halide reaction product layer thereon by a partial consumption of the metal layer; and selectively removing said reaction product by applying, in a predetermined pattern, laser radiation of a wavelength suitable for absorption by said reaction product and causing thermal and electronic excitation and eventual vaporization of the reaction product in a region in correspondence with said pattern and thereby selectively etching the metal layer.
Claim 23
Independent Claim
95 words
A method of radiation induced dry etching of a metal layer formed on a substrate, said method comprising: reacting said metal layer with a halogen gas forming a solid metal halide reaction product layer thereon by a partial consumption of the metal layer; and selectively removing said reaction product by applying, in a predetermined pattern, laser radiation of a wavelength suitable for absorption by said reaction product and causing thermal and electronic excitation and eventual vaporization of the reaction product in a region in correspondence with said pattern and thereby selectively etching the metal layer.
Claim 24
Dependent Claim
20 words
The method as in claim 21 wherein said radiation is suitable for absorption by the metal underlying said reaction product.
Claim 25
Dependent Claim
20 words
The method as in claim 21 or 22 wherein said radiation is of a wavelength in the range 200-1060 nm.
References Cited (Backward Citations)
US3364087A
Cited
US4221047A
Cited
US4260649A
Cited
US4245273A
Cited
US4332999A
Cited
US4331504A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-25 | 1988-06-25 | 1988-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-25 | 1992-06-25 | 1992-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-25 | 1996-06-25 | 1996-12-25 | $7700.00 | Window Closed / Lapsed |