Abstract A composite brazing material is described, composed of a layer (usually an ingot) of high manganese content aluminum alloy (3000 series alloy; the "core") and a layer of high silicon content aluminum alloy (4000 series alloy; the "cladding") with a layer of aluminum alloy having the following composition: ______________________________________ silicon 6.8-8.2 wgt. %
iron up to 0.8 wgt. %
copper up to 0.25 wgt. %
manganese up to 0.10 wgt. %
zinc up to 0.20 wgt. %
other elements up to 0.15 wgt. %
aluminum balance
______________________________________ disposed between the cladding and core layers and in contact with both. Subsequent hot rolling of the multi-layer composite produces a good bond between the core and the cladding through the intermediate layer. The resulting brazing material has the external properties of a simple two-layer composite of core and cladding without the intermediate layer. The three layer composite of the present invention, however, has a much stronger interlayer bond and is not subject to the serious delamination or bond failures of the prior art two-layer materials. Additional composite layers can also be used, with a layer of the intermediate alloy as described herein placed between each successive pair of the 3000 and 4000 series alloy layers. One typical configuration is composed of a 3003 core, clad each side with 4104 alloy sheets and with a 4343 intermediate alloy sheet on either side of the core between the core and each cladding sheet.
A composite brazing material comprising a first layer composed of a 3000 series aluminum alloy, a second layer composed of a 4000 series aluminum alloy and, disposed therebetween and bonded respectively to said first and second layers, an intermediate layer composed of an aluminum alloy having the following composition: ______________________________________
silicon 6.8-8.2 wgt. %
iron up to 0.8 wgt. %
copper up to 0.25 wgt. %
manganese up to 0.10 wgt. %
zinc up to 0.20 wgt. %
other elements up to 0.15 wgt. %
aluminum balance
______________________________________
Claim 2
Dependent Claim
88 words
A composite brazing material comprising a first layer composed of a 3000 series aluminum alloy, a second layer composed of a 4000 series aluminum alloy and, disposed therebetween and bonded respectively to said first and second layers, an intermediate layer composed of an aluminum alloy having the following composition: ______________________________________
silicon 6.8-8.2 wgt. %
iron up to 0.8 wgt. %
copper up to 0.25 wgt. %
manganese up to 0.10 wgt. %
zinc up to 0.20 wgt. %
other elements up to 0.15 wgt. %
aluminum balance
______________________________________
Claim 3
Dependent Claim
26 words
An article as in claim 1 wherein said first layer comprises the core of the composite and said second layer comprises the cladding of the composite.
Claim 4
Dependent Claim
25 words
An article as in claim 2 wherein there are two layers of said cladding with the cladding layers adjacent to opposite surfaces of the core.
Claim 5
Dependent Claim
25 words
An article as in claim 3 wherein said 4000 series alloy cladding material is 4104 alloy and said 3000 series core material is 3003 alloy.
Claim 6
Dependent Claim
18 words
An article as in claims 1, 2, 3 or 4 wherein said intermediate layer material is 4343 alloy.